Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 517 MPa | 75000 psi | |
Hogen Durakut H15W 68 Tungsten/32 Copper PM Metal Composite RWMA Class ECM-EDMDURAKUT Copper-Tungsten and Silver-Tungsten are manufactured as electrode materials for EDM (Electrical Discharge Machining), ECM (Electro Chemical Machining) and ECD (Electro Che.. |
|||
Tensile Strength, Ultimate | 517 MPa | 75000 psi | |
Hogen Duralloy H10TC 56 Tungsten Carbide/44 Copper PM Metal Composite Hogen Duralloy refractory alloys are manufactured by pressing, sintering, and infiltrating tungsten with copper or silver.Typical Resistance Welding Applications: Used for heavy-duty or projection w.. |
|||
Tensile Strength, Ultimate | 517 MPa | 75000 psi | |
Hogen Duralloy H3W 68 Tungsten/32 Copper PM Metal Composite RWMA Class 10.Hogen Duralloy refractory alloys are manufactured by pressing, sintering, and infiltrating tungsten with copper or silver.Typical Resistance Welding Applications: Class 10 material is .. |
|||
Tensile Strength, Ultimate | 517 MPa | 75000 psi | |
High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Bar, After Process Annealed at 1600°F (871°C) High Permeability "49" alloy is a 48% nickel-iron alloy which has a saturation flux density of approximately 15,000 Gauss after hydrogen annealing. Hysteresis loss is very low in either DC or AC cir.. |
|||
Tensile Strength, Ultimate | 517 - 586 MPa | 75000 - 85000 psi | |
Materion BrushCAST® 21C High Strength Casting Alloy (As Cast) Pouring Temperature: 1010-1120°CHeat treatment required for max strength (Annealing): 760-790°C/water quenchHeat treatment required for max strength (Hardening): 760-790°C/water quenchDescr.. |
|||
Tensile Strength, Ultimate | 517 MPa | 75000 psi | |
Mi-Tech Metals CW68 68 Tungsten/32 Copper PM Metal Composite RWMA Class 10.Mi-Tech refractory alloys are manufactured by pressing, sintering, and infiltrating tungsten with copper or silver.Typical Resistance Welding Applications: Class 10 material is recomme.. |
|||
Tensile Strength, Ultimate | 517 MPa | 75000 psi | |
Mi-Tech Metals CW70E 68 Tungsten/32 Copper PM Metal Composite RWMA Class ECM-EDMMi-Tech Copper-Tungsten and Silver-Tungsten are manufactured as electrode materials for EDM (Electrical Discharge Machining), ECM (Electro Chemical Machining) and ECD (Electro Che.. |
|||
Tensile Strength, Ultimate | 517 MPa | 75000 psi | |
Mi-Tech Metals TC56 56 Tungsten Carbide/44 Copper PM Metal Composite Mi-Tech refractory alloys are manufactured by pressing, sintering, and infiltrating tungsten with copper or silver.Typical Resistance Welding Applications: Used for heavy-duty or projection welding .. |
|||
Tensile Strength, Ultimate | 517 MPa | 75000 psi | |
Universal Wire Works 70S-6 Steel Welding Wire Universal 70S-6 is designed for welding mild steels with CO2 shielding gas. This alloy should be used where low silicon mild steel wires have not been satisfactory on slightly contaminated base meta.. |
|||
Tensile Strength, Ultimate | 517 - 593 MPa | 75000 - 86000 psi | |
Eagle Brass 19010 XP-150 Copper Nickel Silicon, Extra Hard 19010 is an extreme versatile high performance copper nickel silicon alloy. It has an excellent combination of strength, conductivity and formability. Typical uses include terminals, relays, connect.. |
|||
Tensile Strength, Ultimate | 517 - 607 MPa | 75000 - 88000 psi | |
Eagle Brass 715 Copper Nickel 30%, Hard 715 exhibits excellent corrosion resistance, especially in marine applications. It has moderately high strength and has good creep resistance at elevated temperatures. The cost is relatively high co.. |
|||
Tensile Strength, Ultimate | 517 MPa | 75000 psi | |
Crucible Steel 416 Plus Chromium Steel Crucible 416 Plus is a hardenable chromium steel to which elements have been added to improve machinability and non-galling characteristics. Better machinability than that of standard AISI Type 4.. |
|||
Tensile Strength, Ultimate | 517 MPa | 75000 psi | Strip (TH04) |
CMW® 3 Copper Alloy CMW® 3 material is a high strength, high conductivity copper base alloy. CMW® 3 material is heat treatable. Optimum mechanical and physical properties of CMW® 3 material are developed by heat tre.. |
|||
Tensile Strength, Ultimate | 517 MPa @Diameter <=25.0 mm |
75000 psi @Diameter <=0.984 in |
Drawn Rod & Bar |
CMW® 3 Copper Alloy CMW® 3 material is a high strength, high conductivity copper base alloy. CMW® 3 material is heat treatable. Optimum mechanical and physical properties of CMW® 3 material are developed by heat tre.. |
|||
Tensile Strength, Ultimate | 517 MPa | 75000 psi | cold worked |
CMW® ELKONIUM 18 silver, copper, cadmium alloy The alloying of silver with cadmium produces materials with good arc extinction, good corrosion resistance and low contact resistance characteristics and provides them with good switching capability.. |
|||
Tensile Strength, Ultimate | 517 MPa | 75000 psi | annealed |
CMW® ELKONIUM 301 platinum based alloy Platinum has complete freedom from atmospheric corrosion and is preferred for devices that have low closed forces and where surety of making a circuit may be a problem. It has a high melting point (.. |
|||
Tensile Strength, Ultimate | 517 MPa | 75000 psi | annealed |
CMW® ELKONIUM 302 platinum based alloy Platinum has complete freedom from atmospheric corrosion and is preferred for devices that have low closed forces and where surety of making a circuit may be a problem. It has a high melting point (.. |
|||
Tensile Strength, Ultimate | 517 MPa @Temperature 316 °C |
75000 psi @Temperature 601 °F |
|
Carpenter 20-Mo6® Stainless Steel, Tensile Properties at 93°C Data provided by Carpenter Technology Corporation.This is an austenitic stainless steel which is resistant to corrosion in hot chloride environments with low pH. It has good resistance to pitting, .. |
|||
Tensile Strength, Ultimate | 517 MPa | 75000 psi | |
AK Steel 436 Ferritic Stainless steel Information provided by AK Steel |
|||
Tensile Strength, Ultimate | 517 MPa | 75000 psi | |
Carpenter Chrome Core® 18-FM Solenoid Quality Stainless Steel, Annealed Data provided by Carpenter Technology Corporation.This is a soft ferritic material designed for operation in more corrosive environments than tolerated by 18% Cr-Fe Type 430 stainless. This new mat.. |
|||
Tensile Strength, Ultimate | 517 MPa | 75000 psi | |
Carpenter Chrome Core® 18-FM Solenoid Quality Stainless Steel, Stress Relieved Data provided by Carpenter Technology Corporation.This is a soft ferritic material designed for operation in more corrosive environments than tolerated by 18% Cr-Fe Type 430 stainless. This new mat.. |
|||
Tensile Strength, Ultimate | 517 - 586 MPa | 75000 - 85000 psi | |
Ametek AM 388™ Alloy (UNS C72650) TD02 1/2 Hard Information supplied by Ametek Specialty Metal Products Division.Copper base Spinodal alloy with high conductivity and high strength. Outstanding performance for contacts in connectors, sockets and.. |
|||
Tensile Strength, Ultimate | 517 - 621 MPa | 75000 - 90100 psi | |
ATI Allegheny Ludlum Stainless Steel Free Machining Grade Type 303, Annealed (UNS S30300) Allegheny Ludlum's 303 is a free-machining stainless steel specifically designed to exhibit improved machinability. These modifications retain, in so far as possible, the good mechanical properties.. |
|||
Tensile Strength, Ultimate | 517 MPa | 75000 psi | |
AK Steel 410 Martensitic Stainless steel AK Steel 410 provides good corrosion resistance plus high strength and hardness. It is magnetic in both annealed and hardened conditions. A wide range of properties can be developed with different.. |
|||
Tensile Strength, Ultimate | 517 MPa | 75000 psi | |
AK Steel 435 Mod Ferritic Stainless steel Information provided by AK Steel |
|||
Tensile Strength, Ultimate | 517 MPa | 75000 psi | Typical |
PSM Industries PolyAlloys MIM-316L sintered Stainless Steel PolyAlloys Injected Metals, a division of PSM Industries, Inc., offers precision, High-Performance components for structural, magnetic and electronic applications that require a high degree of compl.. |
|||
Tensile Strength, Ultimate | 517 MPa | 75000 psi | |
High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Bar, After Process Annealed at 1600°F (871°C) High Permeability "49" alloy is a 48% nickel-iron alloy which has a saturation flux density of approximately 15,000 Gauss after hydrogen annealing. Hysteresis loss is very low in either DC or AC cir.. |