Crucible Steel 416 Plus Chromium Steel
| Category | Metal , Ferrous Metal , Stainless Steel , T 400 Series Stainless Steel |
| Manufacturer | Crucible Steel |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Crucible Steel 416 Plus Chromium Steel.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Crucible 416 Plus is a hardenable chromium steel to which elements have been added to improve machinability and non-galling characteristics. Better machinability than that of standard AISI Type 416 stainless is obtained by the use of special manufacturing methods and balanced chemistry. This grade is magnetic in all conditions. Typical applications are screw machine products and all machined parts requiring good corrosion resistanceInformation provided by Crucible Specialty Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 7.75 g/cc | 7.75 g/cc |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 155 | 155 | |
| Tensile Strength, Ultimate | 517 MPa | 75000 psi | |
| 62.1 MPa @Temperature 760 °C |
9000 psi @Temperature 1400 °F |
||
| 310 MPa @Temperature 538 °C |
45000 psi @Temperature 1000 °F |
||
| Tensile Strength, Yield | 276 MPa @Strain 0.200 % |
40000 psi @Strain 0.200 % |
|
| Elongation at Break | 30 % | 30 % | in 2" |
| Reduction of Area | 60 % | 60 % | |
| Creep Strength | 6.8947 MPa @Temperature 704 °C |
999.99 psi @Temperature 1300 °F |
|
| 64.43 MPa @Temperature 538 °C |
9345 psi @Temperature 1000 °F |
||
| Modulus of Elasticity | 200 GPa | 29000 ksi | Tension |
| Shear Modulus | 72.4 GPa | 10500 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 9.90 µm/m-°C @Temperature 0.000 - 100 °C |
5.50 µin/in-°F @Temperature 32.0 - 212 °F |
|
| 10.1 µm/m-°C @Temperature 0.000 - 316 °C |
5.60 µin/in-°F @Temperature 32.0 - 600 °F |
||
| 11.7 µm/m-°C @Temperature 0.000 - 649 °C |
6.50 µin/in-°F @Temperature 32.0 - 1200 °F |
||
| Specific Heat Capacity | 0.460 J/g-°C @Temperature 0.000 - 100 °C |
0.110 BTU/lb-°F @Temperature 32.0 - 212 °F |
|
| Thermal Conductivity | 24.90 W/m-K @Temperature 93.3 °C |
172.8 BTU-in/hr-ft²-°F @Temperature 200 °F |
|
| 28.5 W/m-K @Temperature 538 °C |
198 BTU-in/hr-ft²-°F @Temperature 1000 °F |
||
| Melting Point | 1480 - 1530 °C | 2700 - 2790 °F | |
| Solidus | 1480 °C | 2700 °F | |
| Liquidus | 1530 °C | 2790 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.15 % | <= 0.15 % | |
| Chromium, Cr | 12 - 14 % | 12 - 14 % | |
| Iron, Fe | >= 82.79 % | >= 82.79 % | As Remainder |
| Manganese, Mn | <= 1.25 % | <= 1.25 % | |
| Molybdenum, Mo | <= 0.60 % | <= 0.60 % | |
| Phosphorous, P | <= 0.060 % | <= 0.060 % | |
| Silicon, Si | <= 1.0 % | <= 1.0 % | |
| Sulfur, S | >= 0.15 % | >= 0.15 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000568 ohm-cm @Temperature 23.0 °C |
0.0000568 ohm-cm @Temperature 73.4 °F |