- Polymer Property : Tensile Strength, Ultimate = 46400 psi
Polymer Property : Tensile Strength, Ultimate = 46400 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 320 MPa @Temperature 600 °C |
46400 psi @Temperature 1110 °F |
EN min.; EN 10002-5 |
| Outokumpu 4828 High Temperature Austenitic Stainless Steel Standardized high temperature steel for service at temperatures of up to 950-1000°C in dry air. Utilization in the temperature range of 600-900°C can lead to embrittlement.Applications: Heat and .. |
|||
| Tensile Strength, Ultimate | 320 MPa @Temperature 600 °C |
46400 psi @Temperature 1110 °F |
EN min.; EN 10002-5 |
| Outokumpu 4833 High Temperature Austenitic Stainless Steel Standardized high temperature steel for service at temperatures of up to 950-1000°C in dry air. Utilization in the temperature range of 600-900°C can lead to embrittlement.Applications: Heat and .. |
|||
| Tensile Strength, Ultimate | 320 MPa @Temperature 600 °C |
46400 psi @Temperature 1110 °F |
EN min.; EN 10002-5 |
| Outokumpu 4845 High Temperature Austenitic Stainless Steel Standardized high-temperature steel for use at temperatures up to 1100°C in dry air. Prone to embrittlement after exposure between 600-900°C. Applications: Heat and creep resistance. For use o.. |
|||
| Tensile Strength, Ultimate | >= 320 MPa | >= 46400 psi | |
| H.C. Starck MoCu 85/15 Molybdenum-Copper Composite Material Description of Product: Molybdenum-copper composite materials are produced by copper infiltration of porous sintered molybdenum. They are available with different copper contents (15 - 35 %). A t.. |
|||
| Tensile Strength, Ultimate | 320 MPa @Temperature 870 °C |
46400 psi @Temperature 1600 °F |
|
| Haynes Hastelloy® W alloy as a weld filler, base metal Alloy 188/ Multimet alloy 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| Tensile Strength, Ultimate | >= 320 MPa | >= 46400 psi | |
| SSAB Tunnplat Domex® 220YP Cold-forming Steel, HSLA Cold-forming Steel, HSLACharacteristics: Domex® is the brand name of hot rolled products from SSAB Tunnplat. Domex® cold-forming steels are modern structural steels. General use of Domex®.. |
|||
| Tensile Strength, Ultimate | 320 MPa | 46400 psi | |
| Wieland 1945 Wilaform Platinum Platinum alloy for universal use.Applications: chains, coin/shape, laminar decoration, pipes, tubingDental |
|||
| Tensile Strength, Ultimate | 320 MPa | 46400 psi | |
| Wieland 3011 Wilaform Silver Universally applicable silver alloyApplications: casting, chains, coin/shape, laminar decoration, pipes, tubingDental |
|||
| Tensile Strength, Ultimate | 320 - 400 MPa | 46400 - 58000 psi | |
| CLAL-MSX CUPROROR® TL1 1/4 hard, Copper Alloy Alloy especially suited to applications in electronics and electro technology. This doped copper, displays high electrical and thermal conductivity, good mechanical properties and excellent temperat.. |
|||
| Tensile Strength, Ultimate | 320 - 400 MPa | 46400 - 58000 psi | |
| CLAL-MSX SICLANIC S® TD3 Quenched Copper Alloy, 1/2 Hard SICLANIC S® is particularly recommended for the production of conductive contact blades. SICLANIC S® offers :electrical conductivity greatly superior to that of bronzes, brasses and nickel silver.. |
|||
| Tensile Strength, Ultimate | 320 MPa @Temperature 371 °C |
46400 psi @Temperature 700 °F |
|
| AK Steel 409 ULTRA FORM® Stainless Steel AK Steel 409 ULTRA FORM Stainless Steel provides an outstanding combination of improved forming and welding characteristics, while providing superior resistance to oxidation, corrosion, ridging and .. |
|||
| Tensile Strength, Ultimate | >= 320 MPa | >= 46400 psi | |
| AK Steel Cold Rolled Carbon Steel, Bake Hardenable (BH 210), SAE J2340 Type 210 B Information provided by AK Steel |
|||
| Tensile Strength, Ultimate | >= 320 MPa | >= 46400 psi | |
| AK Steel Cold Rolled Carbon Steel, Bake Hardenable (BH 250) Information provided by AK Steel |
|||
| Tensile Strength, Ultimate | >= 320 MPa | >= 46400 psi | Minimum |
| Aleris Weldural Aluminum Alloy, 400 mm Thickness Sample treatment not specified for property data.Applications include precise mechanical parts with high dimensional stability, machine components, molds, and refrigeration engineering. Good weldab.. |
|||
| Tensile Strength, Ultimate | 320 - 370 MPa | 46400 - 53700 psi | |
| ArcelorMittal 14 High formability steel for drawing, Hot rolled Available in the following: uncoated (DD14) Description: This range of non-alloyed mild steels is designed for deep and extra deep drawing applications. These products are used extensively in the au.. |
|||
| Tensile Strength, Ultimate | 320 MPa @Temperature 150 °C |
46400 psi @Temperature 302 °F |
Typical, after 10,000 hours |
| Aleris Weldural Aluminum Alloy, 100 mm Thickness Sample treatment not specified for property data.Applications include precise mechanical parts with high dimensional stability, machine components, molds, and refrigeration engineering. Good weldab.. |
|||