Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 14.5 MPa | 2100 psi | ASTM D412 |
Multibase Multi-Flex® TPE A 9502 BLK , 7% Filler Content The moisture content is 0.02%. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 14.5 MPa | 2100 psi | ASTM D638 |
Multibase Multi-Flex® TPE D 4502 BLK Multi-Flex® D 4502 is based on Shell's Kraton G polymer and is suitable for applications for the automotive industry. It exhibits excellent paintability adhesion and is recommended as substrate fo.. |
|||
Tensile Strength, Ultimate | >= 14.5 MPa | >= 2100 psi | ASTM D412 |
Multibase Multi-Flex® TPE D 4701 GREY The burn rate is 0.9 in/min (23 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 14.5 MPa | 2100 psi | 20" / min.; ASTM D-683-95 |
Multibase Multi-Flex® TPO D 4508 D 4508 This product is suitable for airbag enclosures and is based on polyolefins/kraton rubber, exhibiting good paintability and low temperature performance.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 14.5 MPa | 2100 psi | TPE-0153 (ASTM D 412) |
Advanced Elastomer Systems Santoprene® 453-45 Thermoplastic Rubber
(discontinued **) A colorable thermoplastic flame retardant wire and cable elastomer with good fluid resistance, formulated to replace thermoset elastomers such as EPDM, polychloroprene, and chlorosulfonated polyethy.. |
|||
Tensile Strength, Ultimate | 14.5 MPa | 2100 psi | |
Freudenberg Simrit V75 Standard Fluoroelastomer Excellent resistance to petroleum products and solvents. Very good high-temperature performance. Fluorocarbon elastomers make up the most widely used seals in the semiconductor industry. Avoid polar.. |
|||
Tensile Strength, Ultimate | 14.5 MPa | 2100 psi | |
Sylvin Technologies 6146-80 PVC Wire/Cable Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 14.5 MPa | 2100 psi | |
Sylvin Technologies 8925-75 Natural PVC Extrusion Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 14.5 MPa | 2100 psi | |
Sylvin Technologies 8960-80 Natural PVC Extrusion Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 14.5 MPa | 2100 psi | |
Sylvin Technologies 8999-90 Natural PVC Extrusion Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 14.5 MPa | 2100 psi | |
Sylvin Technologies 9077-75C Natural PVC for Injection Molding Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 14.5 MPa | 2100 psi | |
Sylvin Technologies 9925-75 Natural PVC Molding Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 14.5 MPa | 2100 psi | |
Sylvin Technologies 9940-90 Natural PVC Molding Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 14.5 MPa | 2100 psi | |
Sylvin Technologies 9960-80 Natural PVC Molding Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 14.5 MPa | 2100 psi | |
Sylvin Technologies 503 PVC Wire/Cable Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 14.5 MPa | 2100 psi | |
Sylvin Technologies 5131-80 PVC Wire/Cable Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 14.5 MPa | 2100 psi | |
Sylvin Technologies 5134-70 PVC Wire/Cable Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 14.5 MPa | 2100 psi | Press-cured 5 minutes at 190°C |
DuPont Vamac® DP HVA-2 Coagent Test Compound Vamac® DP is an ethylene acrylic dipolymer elastomer. Its general performance characteristics are similar to those of the Vamac® terpolymers, including:Good oil and chemical resistanceHigh temper.. |
|||
Tensile Strength, Ultimate | 14.5 MPa | 2100 psi | |
Whitecast Polymer Engineering Epoxy Composite Casting Whitecast Polymer Engineering (WPE) low-density material is used for acoustic dampening requirements (Damping ratio = 0.158). There is an order of magnitude higher vibration dampening realized when.. |
|||
Tensile Strength, Ultimate | 14.5 MPa | 2100 psi | ASTM D412 |
Colorite Polymers CS8039UL Wire and Cable Insulation Vinyl Compound Description: Colorite specialty wire and cable compounds feature low smoke properties, excellent flame retardance, low temperature flexibility, and resistance to abrasion and chemicals. All are avai.. |
|||
Tensile Strength, Ultimate | 14.5 MPa | 2100 psi | ASTM D638 |
Colorite Polymers 91-477 General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r.. |
|||
Tensile Strength, Ultimate | 14.5 MPa | 2100 psi | ASTM D638 |
Colorite Polymers MULTICHEM™ 8014 Vinyl-Urethane Blend Description: MULTICHEM™ is characterized by:Greater ResiliencyImproved ElasticityLow Temperature PropertiesLower ExtractabilityMolding and ExtrusionInformation provided by Colorite Polymers. |
|||
Tensile Strength, Ultimate | 14.5 MPa | 2100 psi | ASTM D412; ISO 37; DIN 53504 |
Advanced Polymer Alloys DURACRYN 8070 NC Thermoplastic Rubber Information provided by Advanced Polymer Alloys |
|||
Tensile Strength, Ultimate | 14.5 MPa | 2100 psi | ASTM D412 |
Colorite Polymers Weatherflex™ CS1522WX (NTL70B) Wire and Cable Vinyl Compound Description: Colorite specialty wire and cable compounds feature low smoke properties, excellent flame retardance, low temperature flexibility, and resistance to abrasion and chemicals. All are avai.. |
|||
Tensile Strength, Ultimate | 14.5 - 1000 MPa | 2100 - 145000 psi | Average value: 144 MPa Grade Count:84 |
Overview of materials for Thermoplastic Polyurethane (TPUR), Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Thermoplastic Polyurethane (TPUR), Glass Fiber Reinforced". Each property range of values reported is mi.. |
|||
Tensile Strength, Ultimate | 14.5 MPa | 2100 psi | |
Sylvin Technologies 60509 PVC Wire/Cable Compound Information provided by Sylvin Technologies Inc. |