Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	945 MPa	137000 psi
Kennametal Stellite NucalloyÂ® 488 High-Silicon Nickel-Base Hardfacing Alloy NucalloyÂ® alloys are unique, patented, high-silicon, nickel-base hardfacing alloys that are designed to have optimum combinations of hardness and toughness, similar to the cobalt base alloys . B..
Tensile Strength, Ultimate	945 MPa	137000 psi
Kennametal Stellite NucalloyÂ® 488V High-Silicon Nickel-Base Hardfacing Alloy Applications include diesel engine valves, and injection mold screws.NucalloyÂ® alloys are unique, patented, high-silicon, nickel-base hardfacing alloys that are designed to have optimum combinati..
Tensile Strength, Ultimate	941 MPa	137000 psi	at Center, Transverse
International Mold Steel P20 Plastic Mold Steel P20 tool steel is 28 â€“ 32 HRC (Din # 1.2738). Features better hardenability than AISI P20 due to the addition of nickel. Information provided by International Mold Steel.
Tensile Strength, Ultimate	945 MPa	137000 psi
Haynes 188 alloy, 0% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095Â°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
Tensile Strength, Ultimate	945 MPa @Temperature 650 Â°C	137000 psi @Temperature 1200 Â°F
Haynes 25 alloy, cold worked sheet, 20 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Ultimate	945 MPa	137000 psi
Haynes 188 alloy, cold rolled and 1175Â°C solution annealed sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095Â°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
Tensile Strength, Ultimate	945 MPa	137000 psi
Haynes 625 alloy, 40% cold reduction, 1120Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Tensile Strength, Ultimate	945 MPa @Temperature 20.0 °C	137000 psi @Temperature 68.0 °F	Longitudinal Tests from 3" rolled plate at 293 HB
EDRO P1FM #31 Free Machining Holder Steel EDRO #31 P1-FM is a free machining low alloy steel supplied prehardened to 262-321 HB.P1-FM is characterized by excellent machinability, uniform and consistent hardness in all dimensions, good resis..
Tensile Strength, Ultimate	944 MPa	137000 psi	Transverse
AK Steel 15-5 PH® Precipitation Hardening Stainless Steel, Condition H 1150-M AK Steel 15-5 PH® provides high strength, good corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C), and good toughness in both base metal and welds. Short-time, ..
Tensile Strength, Ultimate	945 MPa @Temperature 650 °C	137000 psi @Temperature 1200 °F
Haynes 242® alloy, hot rolled plate, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good thermal..
Tensile Strength, Ultimate	945 MPa @Temperature 600 °C	137000 psi @Temperature 1110 °F
Kennametal Stellite Nucalloy® 430 High-Silicon Nickel-Base Hardfacing Alloy Applications include components of chemical processing.Nucalloy® alloys are unique, patented, high-silicon, nickel-base hardfacing alloys that are designed to have optimum combinations of hardness ..
Tensile Strength, Ultimate	945 MPa	137000 psi
HP Alloys Alloy X, 15% Cold Worked 15% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, and Haynes International.