Polymer Property : Tensile Strength, Ultimate = 945 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	945 MPa	137000 psi
Kennametal Stellite NucalloyÂ® 488 High-Silicon Nickel-Base Hardfacing Alloy NucalloyÂ® alloys are unique, patented, high-silicon, nickel-base hardfacing alloys that are designed to have optimum combinations of hardness and toughness, similar to the cobalt base alloys . B..
Tensile Strength, Ultimate	945 MPa	137000 psi
Kennametal Stellite NucalloyÂ® 488V High-Silicon Nickel-Base Hardfacing Alloy Applications include diesel engine valves, and injection mold screws.NucalloyÂ® alloys are unique, patented, high-silicon, nickel-base hardfacing alloys that are designed to have optimum combinati..
Tensile Strength, Ultimate	945 MPa	137000 psi
Haynes 188 alloy, 0% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095Â°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
Tensile Strength, Ultimate	945 MPa @Temperature 650 Â°C	137000 psi @Temperature 1200 Â°F
Haynes 25 alloy, cold worked sheet, 20 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Ultimate	945 MPa	137000 psi
Haynes 188 alloy, cold rolled and 1175Â°C solution annealed sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095Â°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
Tensile Strength, Ultimate	945 MPa	137000 psi
Haynes 625 alloy, 40% cold reduction, 1120Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Tensile Strength, Ultimate	945 MPa @Temperature 20.0 °C	137000 psi @Temperature 68.0 °F	Longitudinal Tests from 3" rolled plate at 293 HB
EDRO P1FM #31 Free Machining Holder Steel EDRO #31 P1-FM is a free machining low alloy steel supplied prehardened to 262-321 HB.P1-FM is characterized by excellent machinability, uniform and consistent hardness in all dimensions, good resis..
Tensile Strength, Ultimate	945 MPa @Temperature 650 °C	137000 psi @Temperature 1200 °F
Haynes 242® alloy, hot rolled plate, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good thermal..
Tensile Strength, Ultimate	945 MPa @Temperature 600 °C	137000 psi @Temperature 1110 °F
Kennametal Stellite Nucalloy® 430 High-Silicon Nickel-Base Hardfacing Alloy Applications include components of chemical processing.Nucalloy® alloys are unique, patented, high-silicon, nickel-base hardfacing alloys that are designed to have optimum combinations of hardness ..
Tensile Strength, Ultimate	945 MPa	137000 psi
HP Alloys Alloy X, 15% Cold Worked 15% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, and Haynes International.