Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 13.5 MPa | 1960 psi | ASTM D638-95 |
Multibase Multi-Pro® 5012 C Natural 50% Filler Content Polypropylene This product is well suited to fabricate non-glossy appliance parts, such as a vacuum cleaner canister. It replaces ABS at favorable cost performance characteristics.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 13.5 MPa | 1960 psi | TPE-0153 (ASTM D 412) |
Advanced Elastomer Systems VistaFlex® 641N Thermoplastic Rubber
(discontinued **) A translucent thermoplastic elastomer with snappiness. It can be processed using injection molding or extrusion processing techniques.Key Features: Flex modulus (1% Secant) 7.2 MPa (1050 psi); Vica.. |
|||
Tensile Strength, Ultimate | 13.5 MPa | 1960 psi | |
Freudenberg Simrit Simriz® 489 Ultra Pure FFKT Perfluoroelastomer Compound Perfluoro elastomers – or FFKM for short – have an ideal combination of characteristics, with their excellent chemical resistance, high level of temperature resistance, and high levels of .. |
|||
Tensile Strength, Ultimate | 13.5 MPa | 1960 psi | Press-cured 5 minutes at 190°C |
DuPont Vamac® DP Sartomer 350 Coagent Test Compound Vamac® DP is an ethylene acrylic dipolymer elastomer. Its general performance characteristics are similar to those of the Vamac® terpolymers, including:Good oil and chemical resistanceHigh temper.. |
|||
Tensile Strength, Ultimate | 13.5 MPa | 1960 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
Dow Nordel® IP 4520 Molded Golf Grip FormulationNordel® IP 4520 |