Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 32.0 - 115 MPa | 4640 - 16700 psi | Average value: 81.7 MPa Grade Count:5 |
Overview of materials for Thermoset Polyurethane, Liquid This property data is a summary of similar materials in the MatWeb database for the category "Thermoset Polyurethane, Liquid". Each property range of values reported is minimum and maximum values of.. |
|||
Flexural Yield Strength | 32.0 MPa | 4640 psi | at 3.5% strain; 4% strain at break; ISO 178 |
FKuR Kunststoff Fibrolon® P 7550 Wood-Plastic Compound, Fiber Reinforced FIBROLON® are fiber reinforced compounds. Fibrolon® P 7550 has a polypropylene base. With the brand name of FIBROLON® FKuR has developed natural fiber reinforced compounds (Wood-Plastics-C.. |
|||
Flexural Yield Strength | 32.0 MPa | 4640 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Thermocomp FX05032 PE (Europe-Africa-Middle East) LNP* THERMOCOMP* FX05032 is a compound based on Polyethylene resin containing Proprietary Filler(s). Added features include : Foaming Agent for Polyolefins.This data was supplied by SABIC-IP for t.. |
|||
Flexural Yield Strength | 32.0 MPa | 4640 psi | ASTM D790 |
Tipco Tipcolene® FX 995 - 10% Talc/Mineral Reinforced, Impact Modified Polypropylene Copolymer Compound with High Flow 10% Mineral Reinforced, High Flow, Impact Modified PP CopolymerApplications: Automotive Pillars & TrimsProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
.. |
|||
Flexural Yield Strength | 32.0 MPa | 4640 psi | 2 mm/min; ISO 178 |
Eurostar Starglas FX05032 PE Starglas FX05032 is Polyethylene Resin with a Proprietary Additive (foaming agent for polyolefins)Information provided by Eurostar. |
|||
Flexural Yield Strength | 32.0 - 170 MPa | 4640 - 24700 psi | Average value: 86.9 MPa Grade Count:184 |
Overview of materials for Polypropylene with 20% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 20% Glass Fiber Filler". Specific grades with glass content between 15% and 24% are i.. |
|||
Flexural Yield Strength | 32.0 - 210 MPa | 4640 - 30500 psi | Average value: 117 MPa Grade Count:217 |
Overview of materials for Polypropylene with 30% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Glass Fiber Filler". Specific grades with glass content between 25% and 34% are i.. |