Polymer Property : Flexural Yield Strength = 32.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	32.0 - 115 MPa	4640 - 16700 psi	Average value: 81.7 MPa Grade Count:5
Overview of materials for Thermoset Polyurethane, Liquid This property data is a summary of similar materials in the MatWeb database for the category "Thermoset Polyurethane, Liquid". Each property range of values reported is minimum and maximum values of..
Flexural Yield Strength	32.0 MPa	4640 psi	at 3.5% strain; 4% strain at break; ISO 178
FKuR Kunststoff FibrolonÂ® P 7550 Wood-Plastic Compound, Fiber Reinforced FIBROLONÂ® are fiber reinforced compounds. FibrolonÂ® P 7550 has a polypropylene base. With the brand name of FIBROLONÂ® FKuR has developed natural fiber reinforced compounds (Wood-Plastics-C..
Flexural Yield Strength	32.0 MPa	4640 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Thermocomp FX05032 PE (Europe-Africa-Middle East) LNP* THERMOCOMP* FX05032 is a compound based on Polyethylene resin containing Proprietary Filler(s). Added features include : Foaming Agent for Polyolefins.This data was supplied by SABIC-IP for t..
Flexural Yield Strength	32.0 MPa	4640 psi	ASTM D790
Tipco Tipcolene® FX 995 - 10% Talc/Mineral Reinforced, Impact Modified Polypropylene Copolymer Compound with High Flow 10% Mineral Reinforced, High Flow, Impact Modified PP CopolymerApplications: Automotive Pillars & TrimsProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd., ..
Flexural Yield Strength	32.0 MPa	4640 psi	2 mm/min; ISO 178
Eurostar Starglas FX05032 PE Starglas FX05032 is Polyethylene Resin with a Proprietary Additive (foaming agent for polyolefins)Information provided by Eurostar.
Flexural Yield Strength	32.0 - 170 MPa	4640 - 24700 psi	Average value: 86.9 MPa Grade Count:184
Overview of materials for Polypropylene with 20% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 20% Glass Fiber Filler". Specific grades with glass content between 15% and 24% are i..
Flexural Yield Strength	32.0 - 210 MPa	4640 - 30500 psi	Average value: 117 MPa Grade Count:217
Overview of materials for Polypropylene with 30% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Glass Fiber Filler". Specific grades with glass content between 25% and 34% are i..