Polymer Property : Flexural Yield Strength = 260 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	260 MPa	37700 psi	ISO 178, ASTM D790
Nilit Nilamid A3 H G6 General Purpose 30% Glass Reinforced PA66 Description: Nilamid A3 H G6 is a general purpose 30% glass fiber reinforced NYLON 66 that gives an excellent combination of tensile strength, stiffness and impact strength. It is one of the most wi..
Flexural Yield Strength	260 MPa	37700 psi	ISO 178, ASTM D790
Nilit Nilamid A3 H6 G6 30% Glass Reinforced PA66 Description: Nilamid A3 H6 G6 is a 30% glass fiber reinforced NYLON 66 with a special stabilization system against hot oil and grease. As a result of this stabilization, the material has a brown nat..
Flexural Yield Strength	260 MPa	37700 psi	ISO 178, ASTM D790
Nilit Nilamid A3 H7 G6 30% Glass Reinforced PA66 Description: Nilamid A3 H7 G6 is a 30% glass fiber reinforced NYLON 66 with a high heat stabilization. This product combines good overall mechanical performance and impact strength with ease of proc..
Flexural Yield Strength	260 MPa	37700 psi	DIN 53 452
Albis Plastics Tedur® L V 9113-2 PPS, 60% Glass Fiber (discontinued **) Glass Fiber Grade with Highest Mechanical Strength and Stiffness. Incandescent wire resistance (2 mm) is 960°C per VDE 0471 T1.2.Applications: Housings for Shock Absorbers and Spring ElementsProce..
Flexural Yield Strength	260 MPa	37700 psi	ISO 178
Solvay TechnylÂ® A 218 V30 Nylon 66, 30% Glass Fiber, EH0 Polyamide PA66, reinforced with 30% of glass fiber, heat stabilized, for injection molding.Technyl A 218 V30 is used in all sectors of industry, offering an excellent combination between thermal and..
Flexural Yield Strength	260 MPa	37700 psi	ASTM D790
Samyang TramidÂ® 210G35 Polyamide, Reinforced Strong with excellent thermal resistance. Abrasion resistance, chemical resistance and oil resistance are excellent.210G35 is a reinforced grade.Applications:Automotive gear level housingConnectors..
Flexural Yield Strength	260 MPa	37700 psi	ISO 178
Solvay TechnylÂ® A 216 V30 Nylon 66, 30% Glass Fiber, EH0 Polyamide PA66, reinforced with 30% of glass fiber, for injection molding.Technyl A 216 V30 is used in all sectors of industry, offering an excellent combination between thermal and mechanical prope..
Flexural Yield Strength	260 MPa	37700 psi	ISO 178
Wellman Wellamid® GF30-60 XE-N 30% Glass Fiber Reinforced Nylon 6, Lubricated & Heat Stabilized Typical Applications: Radio and TV components, dishwasher roller carriages, chain saw oil reservoirs, gears, housings, door & window latches, power hand tool housings, high temperature devices.Data ..
Flexural Yield Strength	260 MPa	37700 psi	Flexural elongation is 2.3%; ASTM D790
Toyobo TS401 HS PPS, 40% Glass Fiber Reinforced Key Feature: High toughness, high flow. Features high weld strength.High performance injection-molding resin created from crystalline polyphenylene sulfide, using a special formulation technology d..
Flexural Yield Strength	260 MPa	37700 psi	Flexural elongation is 1.6%; ASTM D790
Toyobo TS201 HS PPS, Glass Fiber/Mineral Reinforced Key Feature: High stiffness, high toughnessHigh performance injection-molding resin created from crystalline polyphenylene sulfide, using a special formulation technology developed by Toyobo. Excel..
Flexural Yield Strength	260 MPa	37700 psi	ASTM D790
Cheng Yu Plastic N6G25 Nylon 6, 25% Glass Filled
Flexural Yield Strength	260 MPa	37700 psi	ASTM D790
Cheng Yu Plastic N6GV30 Flame Retardant Nylon 6, 30% Glass Filled
Flexural Yield Strength	260 MPa	37700 psi	ASTM D790
Cheng Yu Plastic NG1500S Nylon 66, 50% Glass Fiber Reinforced
Flexural Yield Strength	260 MPa	37700 psi	ASTM Data
BASF Capron® 8334G Impact Modified, 40% Glass-Filled Nylon 6 (Dry) (discontinued **) Capron 8334G is a heat stabilized, 40% glass fiber reinforced polyamide 6 molding compound developed for applications requiring a high level of stiffness combined with excellent impact performance. ..
Flexural Yield Strength	260 MPa	37700 psi	DIN 53 452
Albis Plastics Tedur® L 9510-1 PPS, 40% Glass Fiber High Strength, High Rigidity Standard Grade. Incandescent wire resistance (2 mm) is 960°C per VDE 0471 T1.2.Applications: Pump Impellers, Valve Housings and BushingsProcessing: Injection Molding (..