SABIC Innovative Plastics LNP THERMOCOMP DF004ER PC (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP DF004ER PC (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* DF004ER is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release.
Physical Properties Metric English Comments
Density 1.33 g/cc
0.0480 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0025 - 0.0045 cm/cm
0.0025 - 0.0045 in/in
on Tensile Bar; SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 120 MPa
17400 psi
5 mm/min; ISO 527
Tensile Strength, Yield 97.0 MPa
14100 psi
5 mm/min; ISO 527
Elongation at Break 3.6 %
3.6 %
5 mm/min; ISO 527
Elongation at Yield 2.6 %
2.6 %
5 mm/min; ISO 527
Tensile Modulus 6.10 GPa
885 ksi
1 mm/min; ISO 527
Flexural Yield Strength 178 MPa
25800 psi
2 mm/min; ISO 178
Flexural Modulus 5.50 GPa
798 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 13.0 kJ/m²
6.19 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 55.0 kJ/m²
26.2 ft-lb/in²
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 144 °C
291 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 140 °C
284 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
Flammability, UL94 V-2

@Thickness 1.50 mm
 V-2

@Thickness 0.0591 in
 UL 94
V-1

@Thickness 3.00 mm
 V-1

@Thickness 0.118 in
 UL 94