Polymer Property : Flexural Yield Strength = 20000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	138 MPa	20000 psi	ASTM D790
Chevron Phillips Ryton® R10 5002C PPS Polyphenylene Sulfide (discontinued **) Ryton® PPS is used in many electronic and automotive applications because of its high strength, favorable electrical properties, and high temperature stability.Data provided by the manufacturer.Sol..
Flexural Yield Strength	138 MPa	20000 psi	ASTM D790
RTP Company RTP 2200 AR 10 Polyetheretherketone (PEEK) Aramid Fiber 10% (discontinued **)& Aramid Fiber 10%Comments:Aramid FiberUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Company.Data fo..
Flexural Yield Strength	138 MPa	20000 psi	ASTM D790
RTP Company RTP 1400 AR 5 Polyethersulfone (PES) Aramid Fiber 5% (discontinued **) Aramid Fiber 5%Comments:Aramid FiberUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Company.Data for..
Flexural Yield Strength	138 MPa	20000 psi	ASTM D790
RTP Company RTP 2100 AR 5 Polyetherimide (PEI) Aramid Fiber 5% (discontinued **) Aramid Fiber 5%Comments:Aramid FiberUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Company.Data for..
Flexural Yield Strength	138 MPa	20000 psi	ASTM D790
RTP Company RTP 205F TFE 15 Nylon 12 (PA 12) Glass Fiber 30% - PTFE 15% (discontinued **)& Glass Fiber 30% - PTFE 15%Comments:Glass FiberPTFE LubricatedUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provide..
Flexural Yield Strength	138 - 450 MPa @Temperature -40.0 - 121 °C	20000 - 65300 psi @Temperature -40.0 - 250 °F	Average value: 249 MPa Grade Count:5
Overview of materials for Nylon 6, 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 40% Glass Fiber Filled". Specific grades with glass content between 35% and 44% are included. E..
Flexural Yield Strength	138 - 348 MPa	20000 - 50500 psi	Average value: 251 MPa Grade Count:34
Overview of materials for Nylon 612, Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Nylon 612, Carbon Fiber Filler". Each property range of values reported is minimum and maximum values of..
Flexural Yield Strength	138 MPa	20000 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ULTEM CRS5011R PEI (Asia Pacific) Enhanced flow Polyetherimide copolymer (Tg 225C) with internal mold release and enhanced chemical resistance to strong acids, bases, aromatics and ketones. ECO Conforming.
Flexural Yield Strength	138 MPa	20000 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ULTEM CRS5011R PEI (Europe-Africa-Middle East) Enhanced flow Polyetherimide copolymer (Tg 225C) with internal mold release and enhanced chemical resistance to strong acids, bases, aromatics and ketones. Resin is RoHS compliant.
Flexural Yield Strength	138 MPa	20000 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ULTEM UF5011S PEI Enhanced flow, Specialty filtered Polyetherimide (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics and ketones. ECO Conforming.
Flexural Yield Strength	138 MPa	20000 psi	ASTM D790
Techmer ES LuriblendÂ® PC CF10 TL15 FR BK 10% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 10% Filler by WeightAdditive: PTFE LubricantFeatures: Lubricated and Flame RetardantAppearance: BlackInformation provided..
Flexural Yield Strength	138 MPa	20000 psi	ASTM D790
Techmer ES PlastiblendÂ® PA6/6 HS L Nylon 66 Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer and LubricantFeatures: Heat Stabilized, Low Viscosity and LubricatedProcessing Method: Injection MoldingInformation provided by TP ..
Flexural Yield Strength	138 MPa	20000 psi	ASTM D790
Techmer ES PlastiblendÂ® PA6/6 M L Nylon 66 Availability: North AmericaForms: PelletsAdditive: LubricantFeatures: Fast Molding Cycle, Low Viscosity and LubricatedProcessing Method: Injection MoldingInformation provided by TP Composites, Inc.
Flexural Yield Strength	138 MPa	20000 psi	ASTM D790
Techmer ES PlastiblendÂ® PA6/6 Nylon 66 Availability: North AmericaForms: PelletsFeatures: Low ViscosityProcessing Method: Injection MoldingInformation provided by TP Composites, Inc.
Flexural Yield Strength	138 MPa	20000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP ZF006 PPE+PS (Europe-Africa-Middle East) LNP* THERMOCOMP* ZF006 is a compound based on PPE+PS Blend resin containing Glass Fiber
Flexural Yield Strength	138 MPa	20000 psi	ASTM D790
Sumitomo Bakelite North America 2004B Glass Reinforced Hardware Grade Epoxy Epoxy is the premier material for military firewall connectors.Information provided by Sumitomo Bakelite North America, Inc.
Flexural Yield Strength	138 MPa	20000 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ULTEM 9085 PEI Blend (Asia Pacific) High flow Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke and flame evolution.
Flexural Yield Strength	138 MPa	20000 psi	ASTM D790
Techmer ES LuriblendÂ® PEI GF30 TL15 BK 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightAdditive: PTFE LubricantFeatures: LubricatedInformation provided by TP Composites, Inc.
Flexural Yield Strength	138 MPa	20000 psi	ASTM D790
PlastxWorld CEVIAN® B6526 30% GF PBT/ABS Alloy Glass fiber and mineral filled, low warpage and flame retarded PBT/ABS.Information provided by PlastxWorld Inc.
Flexural Yield Strength	138 MPa	20000 psi	ASTM D790
Clariant Renol BR2029 Nylon 66, General Purpose, Black Data provided by Clariant Masterbatches
Flexural Yield Strength	138 MPa	20000 psi	ASTM D790
Clariant Renol PA101L Nylon 66, General Purpose, Lubricated Data provided by Clariant Masterbatches
Flexural Yield Strength	137.9 MPa	20000 psi
Abatron AboCast/AboCure 8109-1 High melting point.Processing: 100/30 pbw; mix at 130-140°C (270 °F); cures in 16 h/120°C (250°F), 10 h/140°C (285°F), 8 h/160°C (320°F), 2 h/ 200°C (390°F).Applications: Heavy duty castin..
Flexural Yield Strength	138 MPa	20000 psi
Bulk Molding Compounds BMC 845 Vinyl Ester Molding Compounds, 30% Glass-Filled Description: BMC 845 is designed for use in PEM type fuel cell applications such as end plates and manifolds. It is a corrosion resistant product that shows outstanding creep resistance and compress..
Flexural Yield Strength	138 - 216 MPa	20000 - 31300 psi	Average value: 190 MPa Grade Count:34
Overview of materials for Polycarbonate, 40% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 40% Glass Filled". Specific grades with glass content between 35% and 44% are included. E..
Flexural Yield Strength	138 MPa	20000 psi	ASTM D790
RTP Company RTP 4000A AR 15 TFE 15 SI 2 Polyphthalamide - Hot Water Mold (PPA) Aramid Fiber 15% - PTFE 15% - Silicone 2% Aramid Fiber 15% - PTFE 15% - Silicone 2%Comments:Aramid FiberPTFE LubricatedSilicone LubricatedUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can af..
Flexural Yield Strength	138 - 193 MPa	20000 - 28000 psi	Average value: 175 MPa Grade Count:22
Overview of materials for Polyethersulfone (PES), 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 20% Glass Fiber Filled". Each property range of values reported is minimum and m..
Flexural Yield Strength	138 MPa	20000 psi	ASTM D790
RTP Company RTP 1400 GB 20 Polyethersulfone (PES) Glass Bead 20% (discontinued **) Glass Bead 20%Comments:Glass BeadUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Company.Data for th..
Flexural Yield Strength	138 MPa	20000 psi	ASTM D790
RTP Company RTP 4402 High Temperature Nylon (HTN) Glass Fiber 15% (discontinued **) Glass Fiber 15%Comments:Glass FiberUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Company.Data for ..
Flexural Yield Strength	138 MPa	20000 psi	ASTM D790
RTP Company RTP 4000 AR 20 Polyphthalamide (PPA) Aramid Fiber 20% (discontinued **) Aramid Fiber 20%Comments:Aramid FiberUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Company.Data fo..
Flexural Yield Strength	138 - 179 MPa	20000 - 26000 psi	ASTM D790
Premix Premi-Glas® 1200-28 Polyester SMC (discontinued **) Premi-Glas® 1200-28 series is a low profile, 28 % glass reinforced polyester Sheet Molding Compound designed for recreational vehicle body panels applications that require excellent flexibility and..