Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 138 MPa | 20000 psi | ASTM D790 |
Chevron Phillips Ryton® R10 5002C PPS Polyphenylene Sulfide
(discontinued **) Ryton® PPS is used in many electronic and automotive applications because of its high strength, favorable electrical properties, and high temperature stability.Data provided by the manufacturer.Sol.. |
|||
Flexural Yield Strength | 138 - 186 MPa | 20000 - 27000 psi | Average value: 165 MPa Grade Count:8 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 30% Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), 30% Carbon Fiber Filled". Specific grades with carbon fiber conte.. |
|||
Flexural Yield Strength | 138 - 450 MPa @Temperature -40.0 - 121 °C |
20000 - 65300 psi @Temperature -40.0 - 250 °F |
Average value: 249 MPa Grade Count:5 |
Overview of materials for Nylon 6, 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 40% Glass Fiber Filled". Specific grades with glass content between 35% and 44% are included. E.. |
|||
Flexural Yield Strength | 138 - 348 MPa | 20000 - 50500 psi | Average value: 251 MPa Grade Count:34 |
Overview of materials for Nylon 612, Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Nylon 612, Carbon Fiber Filler". Each property range of values reported is minimum and maximum values of.. |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM CRS5011R PEI Enhanced flow Polyetherimide copolymer (Tg 225C) with internal mold release and enhanced chemical resistance to strong acids, bases, aromatics and ketones. ECO Conforming. |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM CRS5011R PEI (Europe-Africa-Middle East) Enhanced flow Polyetherimide copolymer (Tg 225C) with internal mold release and enhanced chemical resistance to strong acids, bases, aromatics and ketones. Resin is RoHS compliant. |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Ultem HFATX200 PEI+PCE (Europe-Africa-Middle East) High flow Polyetherimide blend with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP DF002H PC LNP THERMOCOMP* DF002H is a compound based on Polycarbonate resin containing 10% Glass Fiber. Added feature includes: Healthcare. |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | ASTM D790 |
Techmer ES Luriblend® PSU GF20 TL5 20% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 20% Filler by WeightAdditive: PTFE LubricantFeatures: LubricatedInformation provided by TP Composites, Inc. |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | ASTM D790 |
Techmer ES Plastiblend® PA6/6 HS L Nylon 66 Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer and LubricantFeatures: Heat Stabilized, Low Viscosity and LubricatedProcessing Method: Injection MoldingInformation provided by TP .. |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | ASTM D790 |
Techmer ES Plastiblend® PA6/6 M L Nylon 66 Availability: North AmericaForms: PelletsAdditive: LubricantFeatures: Fast Molding Cycle, Low Viscosity and LubricatedProcessing Method: Injection MoldingInformation provided by TP Composites, Inc. |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 9085 PEI Blend High flow Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke and flame evolution. |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON DFD03 PC LNP* STAT-KON* DFD03 is a compound based on Polycarbonate containing 15% Glass Fiber. Added feature of this grade is: Impact Modified. |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | ASTM D790 |
Techmer ES Luriblend® PEI GF30 TL15 BK 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightAdditive: PTFE LubricantFeatures: LubricatedInformation provided by TP Composites, Inc. |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | ASTM D790 |
Clariant Renol BR2029 Nylon 66, General Purpose, Black Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | ASTM D790 |
Clariant Renol PA101LRD-190 Nylon 66, General Purpose, Lubricated Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | ASTM D790 |
Clariant Renol PA113 Nylon 66, Heat Stabilized, Lubricated Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | ASTM D790 |
Clariant Renol PA11BK FDA Nylon 66, General Purpose, FDA, Black Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | |
Bulk Molding Compounds BMC 845 Vinyl Ester Molding Compounds, 30% Glass-Filled Description: BMC 845 is designed for use in PEM type fuel cell applications such as end plates and manifolds. It is a corrosion resistant product that shows outstanding creep resistance and compress.. |
|||
Flexural Yield Strength | 138 - 193 MPa | 20000 - 28000 psi | Average value: 175 MPa Grade Count:22 |
Overview of materials for Polyethersulfone (PES), 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 20% Glass Fiber Filled". Each property range of values reported is minimum and m.. |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | ASTM D790 |
Techmer ES HiFill FR® PA6/6 GF10 FR BK 10% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 10% Filler by WeightFeatures: Flame Retardant Appearance: BlackProcessing Method: Injection MoldingInformation provided by.. |