Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 30% Carbon Fiber Filled

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 30% Carbon Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 30% Carbon Fiber Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), 30% Carbon Fiber Filled". Specific grades with carbon fiber content between 25% and 34% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.15 - 1.38 g/cc
0.0415 - 0.0499 lb/in³
Average value: 1.20 g/cc Grade Count:8
Filler Content 25.0 - 30.0 %
25.0 - 30.0 %
Average value: 28.8 % Grade Count:4
Water Absorption 0.140 - 0.200 %
0.140 - 0.200 %
Average value: 0.157 % Grade Count:7
Linear Mold Shrinkage 0.000500 - 0.00200 cm/cm
0.000500 - 0.00200 in/in
Average value: 0.00119 cm/cm Grade Count:8
Mechanical Properties Metric English Comments
Hardness, Rockwell R 108 - 110
108 - 110
Average value: 109 Grade Count:4
Tensile Strength, Ultimate 103 - 124 MPa
15000 - 18000 psi
Average value: 115 MPa Grade Count:5
Tensile Strength, Yield 110 - 131 MPa
16000 - 19000 psi
Average value: 122 MPa Grade Count:3
Elongation at Break 1.00 - 2.00 %
1.00 - 2.00 %
Average value: 1.38 % Grade Count:6
Modulus of Elasticity 17.2 - 19.3 GPa
2500 - 2800 ksi
Average value: 18.4 GPa Grade Count:4
Flexural Yield Strength 138 - 186 MPa
20000 - 27000 psi
Average value: 165 MPa Grade Count:8
Flexural Modulus 12.4 - 17.2 GPa
1800 - 2500 ksi
Average value: 14.6 GPa Grade Count:8
Izod Impact, Notched 0.427 - 0.641 J/cm
0.800 - 1.20 ft-lb/in
Average value: 0.547 J/cm Grade Count:8
Izod Impact, Unnotched 2.14 - 3.20 J/cm
4.00 - 6.00 ft-lb/in
Average value: 2.71 J/cm Grade Count:7
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 104 - 113 °C
220 - 235 °F
Average value: 111 °C Grade Count:6
Deflection Temperature at 1.8 MPa (264 psi) 102 - 110 °C
215 - 230 °F
Average value: 106 °C Grade Count:7
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:7
Electrical Properties Metric English Comments
Electrical Resistivity 10.0 ohm-cm - 1e+05
10.0 ohm-cm - 1e+05
Average value: 179 ohm-cm Grade Count:6
Surface Resistance 10.0 - 10000 ohm
10.0 - 10000 ohm
Average value: 3190 ohm Grade Count:3
Processing Properties Metric English Comments
Melt Temperature 204 - 238 °C
400 - 460 °F
Average value: 221 °C Grade Count:3
Mold Temperature 62.8 - 85.0 °C
145 - 185 °F
Average value: 73.9 °C Grade Count:4
Drying Temperature 82.2 °C
180 °F
Average value: 82.2 °C Grade Count:3
Moisture Content 0.100 %
0.100 %
Average value: 0.100 % Grade Count:3
Dew Point -17.8 °C
0.000 °F
Average value: -17.8 °C Grade Count:3
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi
Average value: 86.2 MPa Grade Count:4