Polymer Property : Film Tensile Strength at Break, TD = 6500 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, TD	44.8 MPa	6500 psi	ASTM D882
Westlake Hifor Xtreme SC74844 Linear Low Density Polyethylene WESTLAKE HIFOR Xtreme SC74844 polymer is a high strength linear low density polyethylene designed for blown film extrusion that contains medium slip, high antiblock and processing aid. Films produce..
Film Tensile Strength at Break, TD	44.8 MPa	6500 psi	ASTM D882
Westlake Hifor Xtreme SC74853 Linear Low Density Polyethylene WESTLAKE HIFOR Xtreme SC74853 polymer is a high strength linear low density polyethylene designed for blown film extrusion that contains no slip, high antiblock and processing aid. Films produced wi..
Film Tensile Strength at Break, TD	44.8 MPa	6500 psi	ASTM D882
Westlake Hifor Xtreme SC74858 Linear Low Density Polyethylene WESTLAKE HIFOR Xtreme SC74858 polymer is a high strength, good clarity linear low density polyethylene designed for blown film extrusion that contains no slip or antiblock and processing aid. Films ..
Film Tensile Strength at Break, TD	44.8 MPa	6500 psi	ASTM D882
Westlake Mxsten CV77512 Polyethylene Plastomer Mxsten CV plastomer CV77512 is a polyethylene plastomer designed for blown film extrusion that contains high slip, high antiblock and high processing aid additives. Films produced with this resin ex..
Film Tensile Strength at Break, TD	44.8 MPa	6500 psi	ASTM D882
Westlake Mxsten CV77523 Polyethylene Plastomer Mxsten CV plastomer CV77523 is a polyethylene plastomer designed for blown film extrusion that contains high slip, very high antiblock and polymer processing aid additives. Films produced with this ..
Film Tensile Strength at Break, TD	44.8 MPa	6500 psi	Calculated from mfr's report of 182 N/cm per ASTM D828 and the typical thickness
DuPont™ Nomex® 414 Paper, 15 mil Nominal Thickness Nomex® Type 414 is designed for uses requiring a strong, yet flexible and conformable sheet. It is electrically and thermally similar to Type 410. Type 414 was designed as slot insulation in hand..
Film Tensile Strength at Break, TD	44.8 MPa	6500 psi	ASTM D882
Dow FLEXOMER™ ETS-9064 NT 7, 2mil Very Low Density Polyethylene (VLDPE) Resin FLEXOMER™ ETS-9064 NT 7 is intended for use in single of multi-layer blown-film constructions or thick sheets. Films extruded from ETS-9064 NT 7 have a high tear strength, high impact strength, an..
Film Tensile Strength at Break, TD	44.8 MPa	6500 psi
Dow Primacor® 1410 Ethylene Acrylic Acid (EAA) Film properties below based on a film thickness of 60 µm. Data provided by Dow Chemical.