Dow FLEXOMER™ ETS-9064 NT 7, 2mil Very Low Density Polyethylene (VLDPE) Resin

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer	Dow Chemical
Trade Name	FLEXOMER™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Dow FLEXOMER™ ETS-9064 NT 7, 2mil Very Low Density Polyethylene (VLDPE) Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

FLEXOMER™ ETS-9064 NT 7 is intended for use in single of multi-layer blown-film constructions or thick sheets. Films extruded from ETS-9064 NT 7 have a high tear strength, high impact strength, and high puncture resistance and are readily heat sealable.Information provided by Dow

Physical Properties	Metric	English	Comments
Density	0.911 g/cc	0.0329 lb/in³	ASTM D792
Thickness	50.8 microns	2.00 mil
Melt Flow	1.0 g/10 min	1.0 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	9.65 MPa	1400 psi	ASTM D882
Film Tensile Strength at Yield, TD	10.3 MPa	1500 psi	ASTM D882
Film Elongation at Break, MD	800 %	800 %	ASTM D882
Film Elongation at Break, TD	900 %	900 %	ASTM D882
Secant Modulus, MD	0.1531 GPa	22.20 ksi	2% Secant; ASTM D882
Secant Modulus, TD	0.1703 GPa	24.70 ksi	2% Secant; ASTM D882
Impact	264	264	[ft-lbf/in<sup>3</sup>]; Puncture Resistance; Dow Method
	3800	3800	[ft-lbf/in<sup>3</sup>]; Toughness MD; ASTM D882
	3900	3900	[ft-lbf/in<sup>3</sup>]; Toughness TD; ASTM D882
Elmendorf Tear Strength MD	825 g	825 g	ASTM D1922
Elmendorf Tear Strength TD	1150 g	1150 g	ASTM D1922
Elmendorf Tear Strength, MD	16.24 g/micron	412.5 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	22.6 g/micron	575 g/mil	ASTM D1922
Dart Drop Test	330 g	0.728 lb	Method B; ASTM D1709
Film Tensile Strength at Break, MD	51.7 MPa	7500 psi	ASTM D882
Film Tensile Strength at Break, TD	44.8 MPa	6500 psi	ASTM D882
Heat Seal Strength Initiation Temperature	100 °C	212 °F	2 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method

Thermal Properties	Metric	English	Comments
Melting Point	122 °C	252 °F	Dow Method (DSC)
Vicat Softening Point	94.0 °C	201 °F	ASTM D1525

Optical Properties	Metric	English	Comments
Haze	11 %	11 %	ASTM D1003
Gloss	62 %	62 %	45°; ASTM D2457
Transmission, Visible	98 %	98 %	Clarity; ASTM D1746