Dow Primacor® 1410 Ethylene Acrylic Acid (EAA)
| Category | Polymer , Film , Thermoplastic , Ethylene Acrylic Acid |
| Manufacturer | Dow Chemical |
| Trade Name | Primacor® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow Primacor® 1410 Ethylene Acrylic Acid (EAA).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Film properties below based on a film thickness of 60 µm. Data provided by Dow Chemical.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.938 g/cc | 0.0339 lb/in³ | |
| Thickness | 60.0 microns | 2.36 mil | |
| Melt Flow | 1.5 g/10 min @Load 2.16 kg |
1.5 g/10 min @Load 4.76 lb |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 23.4 MPa | 3390 psi | Molded property |
| Film Tensile Strength at Yield, MD | 8.60 MPa | 1250 psi | |
| Film Tensile Strength at Yield, TD | 7.90 MPa | 1150 psi | |
| Tensile Strength, Yield | 8.30 MPa | 1200 psi | Molded property |
| Film Elongation at Break, MD | 470 % | 470 % | |
| Film Elongation at Break, TD | 510 % | 510 % | |
| Elongation at Break | 585 % | 585 % | Molded value |
| Tensile Modulus | 0.124 GPa | 18.0 ksi | |
| Elmendorf Tear Strength MD | 300 g | 300 g | |
| Elmendorf Tear Strength TD | 400 g | 400 g | |
| Elmendorf Tear Strength, MD | 5.00 g/micron | 127 g/mil | |
| Elmendorf Tear Strength, TD | 6.70 g/micron | 170 g/mil | |
| Dart Drop | 10.2 g/micron | 259 g/mil | |
| Film Tensile Strength at Break, MD | 42.7 MPa | 6190 psi | |
| Film Tensile Strength at Break, TD | 44.8 MPa | 6500 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 81.0 °C | 178 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 5.5 % | 5.5 % | |
| Gloss | 65 % | 65 % | 45° |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 191 °C | 376 °F | Film extrusion temperature |
Users viewing this material also viewed the following:
- Nye Lubricants 168 (SO) Synthetic Oil
- Premix Thermoplastics PRE-ELEC® PS 1331 Carbon Black Filled Conductive Thermoplastic Compound
- Inno-Comp INNOPOL® CS 2-9000 MA N Polypropylene Copolymer
- Borealis Borflow™ HL512FB Polypropylene Homopolymer
- Wellman Wellamid® XT1627-WBK2 High Impact, Weatherable Nylon 66
- AK Steel 420LC Martensitic Stainless steel
- ATI Allegheny Ludlum AL 610 Stainless Steel, UNS S30600
- Colorite Polymers 7012 Clear Injection Molding Vinyl Compound
- LNP Thermocomp® JF-1006 BK8-115 Polyethersulfone, Glass Fiber Reinforcement (discontinued **)
- Westlake Mxsten CV77526 Polyethylene Plastomer
Copyright © lookpolymers.com All Rights Reserved