Polymer Property : Film Tensile Strength at Break, TD = 20.3 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, TD	20.3 MPa	2940 psi	ASTM D882
ExxonMobil LD 117.03 Blown Overwrap Film Resin (discontinued **) LD 117 resins are homopolymer film resins with good clarity and excellent stiffness. Film from LD 117 resins can be used in overwrap applications and push-through type packaging equipment. Film ma..
Film Tensile Strength at Break, TD	20.3 MPa	2940 psi	ASTM D882
ExxonMobil LD 117.08 Blown Overwrap Film Resin (discontinued **) LD 117 resins are homopolymer film resins with good clarity and excellent stiffness. Film from LD 117 resins can be used in overwrap applications and push-through type packaging equipment. Film ma..
Film Tensile Strength at Break, TD	20.3 MPa	2940 psi	ASTM D882
Teknor Apex Terraloy™ BP 20001A Thermoplastic Starch + Copolyester Notes: Terraloy™ BP-20001A is a Thermoplastic Starch/Biodegradable Copolyester ready-to-process compound that contains up to 40% of TPS renewable content and is 100% biodegradable. This compound i..
Film Tensile Strength at Break, TD	20.3 MPa	2940 psi
Dow LDPE 493A Low Density Polyethylene, Film Grade DOW LDPE 493A resin, is a high strength, general purpose resin used for shipping sack, industrial liner and produce film applications. DOW LDPE 493A resin can be blended with most linear low density..
Film Tensile Strength at Break, TD	20.3 - 24.3 MPa	2940 - 3520 psi
3M 6147 Performance Reinforced Water Activated Tape 3M™ Performance Reinforced Water Activated Tape 6147 is used for box sealing and other packaging applications. This has a fiberglass reinforced paper backing and a high tack water activated adhesiv..