ExxonMobil LD 117.08 Blown Overwrap Film Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil LD 117.08 Blown Overwrap Film Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LD 117 resins are homopolymer film resins with good clarity and excellent stiffness. Film from LD 117 resins can be used in overwrap applications and push-through type packaging equipment. Film made from LD 117 resins can be drawn down to 1.0 mil gauge.Information provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.929 g/cc | 0.0336 lb/in³ | ExxonMobil Method |
| Thickness | 38.1 microns | 1.50 mil | |
| Melt Flow | 1.6 g/10 min | 1.6 g/10 min | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 13.3 MPa | 1930 psi | at 2% offset; ASTM D882 |
| Film Tensile Strength at Yield, TD | 15.0 MPa | 2170 psi | at 2% offset; ASTM D882 |
| Film Elongation at Break, MD | 170 % | 170 % | ASTM D882 |
| Film Elongation at Break, TD | 550 % | 550 % | ASTM D882 |
| Film Elongation at Yield, MD | 5.6 % | 5.6 % | ASTM D882 |
| Film Elongation at Yield, TD | 5.0 % | 5.0 % | ASTM D882 |
| Elmendorf Tear Strength MD | 250 g | 250 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 200 g | 200 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 6.559 g/micron | 166.6 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 5.248 g/micron | 133.3 g/mil | ASTM D1922 |
| Dart Drop | 2.10 g/micron | 53.3 g/mil | ASTM D1709 |
| Dart Drop Test | 80.0 g | 0.176 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 20.3 MPa | 2940 psi | ASTM D882 |
| 1% Secant Modulus, MD | 304 MPa | 44100 psi | ASTM D882 |
| 1% Secant Modulus, TD | 359 MPa | 52000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 114 °C | 238 °F | Peak Melting Temperature; ExxonMobil Method |
| Crystallization Temperature | 103 °C | 217 °F | ExxonMobil Method |
| Vicat Softening Point | 105 °C | 221 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 6.5 % | 6.5 % | ASTM D1003 |
| Gloss | 70 % | 70 % | 45°; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Thermal Stabilizer |