ExxonMobil LD 117.03 Blown Overwrap Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LD 117.03 Blown Overwrap Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LD 117 resins are homopolymer film resins with good clarity and excellent stiffness. Film from LD 117 resins can be used in overwrap applications and push-through type packaging equipment. Film made from LD 117 resins can be drawn down to 1.0 mil gauge.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.929 g/cc
0.0336 lb/in³
ExxonMobil Method
Thickness 38.1 microns
1.50 mil
Melt Flow 1.6 g/10 min
1.6 g/10 min
ExxonMobil Method
Antiblock Level 1000 ppm
1000 ppm
Slip Level 750 ppm
750 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 13.3 MPa
1930 psi
at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD 15.0 MPa
2170 psi
at 2% offset; ASTM D882
Film Elongation at Break, MD 170 %
170 %
ASTM D882
Film Elongation at Break, TD 550 %
550 %
ASTM D882
Film Elongation at Yield, MD 5.6 %
5.6 %
ASTM D882
Film Elongation at Yield, TD 5.0 %
5.0 %
ASTM D882
Elmendorf Tear Strength MD 250 g
250 g
ASTM D1922
Elmendorf Tear Strength TD 200 g
200 g
ASTM D1922
Elmendorf Tear Strength, MD 6.559 g/micron
166.6 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 5.248 g/micron
133.3 g/mil
ASTM D1922
Dart Drop 2.10 g/micron
53.3 g/mil
ASTM D1709
Dart Drop Test 80.0 g
0.176 lb
ASTM D1709
Film Tensile Strength at Break, MD 25.0 MPa
3630 psi
ASTM D882
Film Tensile Strength at Break, TD 20.3 MPa
2940 psi
ASTM D882
1% Secant Modulus, MD 304 MPa
44100 psi
ASTM D882
1% Secant Modulus, TD 359 MPa
52000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 114 °C
238 °F
Peak Melting Temperature; ExxonMobil Method
Crystallization Temperature 103 °C
217 °F
ExxonMobil Method
Vicat Softening Point 105 °C
221 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 6.5 %
6.5 %
ASTM D1003
Gloss 70 %
70 %
45°; ASTM D2457
Descriptive Properties Value Comments
Features Thermal Stabilizer