- Polymer Property : Tensile Strength, Yield = 55000 psi
Polymer Property : Tensile Strength, Yield = 55000 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 379 MPa @Strain 0.200 %, Temperature 204 °C |
55000 psi @Strain 0.200 %, Temperature 399 °F |
|
| Haynes Ultimet® alloy, 6.3-38.1 mm plate Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Tensile Strength, Yield | 379 MPa @Strain 0.200 % |
55000 psi @Strain 0.200 % |
|
| Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GMAW spray weld 1.1 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Tensile Strength, Yield | 379 MPa @Strain 0.200 % |
55000 psi @Strain 0.200 % |
|
| Special Metals INCONEL® 690 Nickel Superalloy, Cold Drawn Tube, 0.75 inch (19.0 mm) o.d. and 0.065 inch (1.65 mm) Thickness Composition adjustments for nuclear applications: 28-31 Cr; 0.04 max C; 0.10 max Co.Tensile strength (ultimate and yield) and elongation values reported here are typical for Cold Drawn Tube, 0.75 in.. |
|||
| Tensile Strength, Yield | 379 MPa @Strain 0.200 % |
55000 psi @Strain 0.200 % |
|
| Universal Wire Works 310 Stainless Steel (AMS 5694) Filler Metal Universal 310 alloy is primarily used for welding type 310 stainless steels, dissimilar steels and such types as 405, 410 and 430 steels when preheat and postheat are not practical. This alloy exhib.. |
|||
| Tensile Strength, Yield | >= 379 MPa | >= 55000 psi | |
| Alcoa Excalibar® 6013-T8 Aluminum, 3.8-8.2 cm diameter Weldability = A; Stress Corrosion Cracking Resistance = A; General Corrosion Resistance = B (A = best; E = worst). General 6013 characteristics and uses: High strength and good corrosion resistance... |
|||
| Tensile Strength, Yield | 379 - 434 MPa | 55000 - 63000 psi | 0.2% offset |
| Eagle Brass 210 Gilding Metal, Extra Hard CDA 210 is known for its resistance to corrosion. The alloy also lends itself to deep drawing such as bullet jackets and electrical applications where formability and conductivity are required. Typi.. |
|||
| Tensile Strength, Yield | 379 - 476 MPa | 55000 - 69000 psi | 0.2% offset |
| Eagle Brass 260 Cartridge Brass, 3/4 Hard Alloy C260 is commonly used for electrical components, electronic parts, and mechanical fasteners. The alloy has good strength but poor stress relaxation characteristics and does not make a particul.. |
|||
| Tensile Strength, Yield | >= 379 MPa | >= 55000 psi | 0.2% Offset |
| Eagle Brass 301 Austenitic Stainless Steel, 1/8 Hardened Type 301 is a chromium-nickel stainless steel that provides high strength and good ductility with chromium and nickel contents lowered to increase the work hardening range. This permits higher tens.. |
|||
| Tensile Strength, Yield | >= 379 MPa | >= 55000 psi | 0.2% Offset |
| Eagle Brass 302 Austenitic Stainless Steel, 1/8 Hardened Types 302 is a widely used variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled.Information provided by Eagle Brass Compa.. |
|||
| Tensile Strength, Yield | >= 379 MPa | >= 55000 psi | 0.2% Offset |
| Eagle Brass 316L Austenitic Stainless Steel, 1/8 Hardened Type 316L is an extra-low carbon version of Type 316 that minimizes carbide precipitation. Typical uses include exhaust manifolds, furnace parts, heat exchangers, jet engine parts, pharmaceutical a.. |
|||
| Tensile Strength, Yield | 379 - 483 MPa | 55000 - 70000 psi | 0.2% offset |
| Eagle Brass 519 Phosphor Bronzes 6%, 1/2 Hard Alloy C519 has 6% nominal tin producing higher mechanical strengths with a slight decrease in electrical conductivity when compared to C510 phosphor bronze. Often functionally interchangeable with C.. |
|||
| Tensile Strength, Yield | 379 - 490 MPa | 55000 - 71000 psi | 0.2% offset |
| Eagle Brass 706 Copper Nickel 10%, 1/2 Hard 706 exhibits excellent corrosion resistance, especially in marine applications. It has a relatively high strength and has resistance at elevated temperatures. The cost is relatively high compared to.. |
|||
| Tensile Strength, Yield | 379 MPa | 55000 psi | |
| Chicago Extruded Metals BioBrass® UNS C62500 Aluminum Bronze Finished product available in rods.Chicago Extruded Metal temper code: M30This alloy is registered with the U.S. EPA as Antimicrobial.Information provided by Chicago Extruded Metals |
|||
| Tensile Strength, Yield | >= 379 MPa | >= 55000 psi | 0.2% Offset |
| Eagle Brass 304 Austenitic Stainless Steel, 1/8 Hardened Types 304 is a widely used variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled.Information provided by Eagle Brass Compa.. |
|||
| Tensile Strength, Yield | >= 379 MPa | >= 55000 psi | 0.2% Offset |
| Eagle Brass 304L Austenitic Stainless Steel, 1/8 Hardened Type 304L is a very common variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled. Lower carbon 304L minimizes chromium ca.. |
|||
| Tensile Strength, Yield | >= 379 MPa @Strain 0.500 % |
>= 55000 psi @Strain 0.500 % |
Any thickness |
| Cadi 1815 Copper Alloy Zirconium addition to chromium copper improves creep resistance at high operating temperatures and reportedly reduces sticking of electrodes to the work during spot welding of galvanized materials. .. |
|||
| Tensile Strength, Yield | >= 379 MPa @Strain 0.500 % |
>= 55000 psi @Strain 0.500 % |
Any thickness |
| Cadi 182 Copper Alloy Chromium copper is the primary copper alloy used for resistance spot and seam welding. This alloy achieves good hardness and electrical conductivity through a combination of heat treatment and cold .. |
|||
| Tensile Strength, Yield | 379 MPa | 55000 psi | Stress relieved |
| California Fine Wire Copper Clad 1006 Steel (40% Conductivity) All values may vary dependent on specific design and usage1006 steel core, 99.99% copper cladCapabilities: WireRibbonSquareInsulatedPlatedInformation provided by California Fine Wire. |
|||
| Tensile Strength, Yield | >= 379 MPa @Strain 0.200 % |
>= 55000 psi @Strain 0.200 % |
|
| Carlson Nitronic® 50® Austenitic Stainless Steel General DescriptionNitronic 50 is a nitrogen-strengthened austenitic stainless steel that possesses corrosion resistance superior to 316, 316L, 317 and 317L plus approximately twice the yield streng.. |
|||
| Tensile Strength, Yield | 379 - 448 MPa @Strain 0.200 % |
55000 - 65000 psi @Strain 0.200 % |
|
| Ametek AM 388™ Alloy (UNS C72650) TD01 1/4 Hard Information supplied by Ametek Specialty Metal Products Division.Copper base Spinodal alloy with high conductivity and high strength. Outstanding performance for contacts in connectors, sockets and.. |
|||
| Tensile Strength, Yield | 379 MPa @Strain 0.200 % |
55000 psi @Strain 0.200 % |
Annealed |
| ATI Allegheny Ludlum 425 Mod Martensitic Stainless Steel Characteristics: superior wear resistance, hardenable, excellent corrosion resistance. Applications:cutlery, dental and surgical instruments, nozzles, valve parts, hardened steel ball and seats for.. |
|||
| Tensile Strength, Yield | 379 MPa @Strain 0.200 % |
55000 psi @Strain 0.200 % |
|
| ATI Allvac® Nickelvac® H-B-2 UNS N10665 Nickel Superalloy Vessels, pumps, valves, piping systems for the production of hydrochloric, sulfuric, acetic, and phosphoric acids.Property values are for samples in the metallurgical condition: 1600°F age.Informat.. |
|||
| Tensile Strength, Yield | 379 MPa @Strain 0.200 % |
55000 psi @Strain 0.200 % |
|
| ATI Allvac® Nickelvac® XM-19 UNS S20910 Specialty Steel Uses: Chemical processing equipment, high-strength pump shafts, surgical implants, intermedullary nails, plates, screws, wires.Property values are for samples in the metallurgical condition: 1900°F.. |
|||
| Tensile Strength, Yield | >= 379 MPa @Strain 0.200 % |
>= 55000 psi @Strain 0.200 % |
|
| Carlson Nitronic® 33® Austenitic Stainless Steel General DescriptionNitronic 33 is a nitrogen-strengthened austenitic stainless steel that combines high yield strength with excellent toughness and ductility. It’s magnetic permeability remains v.. |
|||
| Tensile Strength, Yield | 379 MPa | 55000 psi | Typical |
| ATI Allegheny Ludlum Ohmaloy® 30 Resistance Alloy Ohmaloy 30 alloy is a moderately magnetic, ductile stainless steel having extremely high electrical resistivity. In addition to imparting high electrical resistivity, the aluminum content in these .. |
|||
| Tensile Strength, Yield | 379 MPa @Strain 0.200 % |
55000 psi @Strain 0.200 % |
|
| ATI Allvac® 55, Titanium Alloy, Heat Treatment: 704°C (1300°F) Anneal Data provided by Allvac.Applications: Airframe skin, heat exchangers, cryogenic vessels, components for CPI equipment, condenser tubing, exhaust pipe shrouds. |
|||
| Tensile Strength, Yield | 379 MPa | 55000 psi | |
| ATI Allegheny Ludlum ALFA-I™ Stainless Steel Type 406 Characteristics:superior oxidation resistance for the temperature range 1600°F-over 2200°F, high electrical resistivity, high resistance to sulfidation, high resistance to carburization. Applicat.. |
|||
| Tensile Strength, Yield | 379 MPa @Strain 0.200 % |
55000 psi @Strain 0.200 % |
|
| Haynes Hastelloy® C-22® alloy, GMAW, aged 4000 hours at 450°C (800°F), unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Tensile Strength, Yield | 379 MPa @Strain 0.200 % |
55000 psi @Strain 0.200 % |
|
| Carpenter Gall-Tough® Stainless, Annealed and Cold Drawn Bar, 0% Cold Work Data provided by Carpenter Technology Corporation.Threshold Galling Stress 103 MPa (higher stress tests not performed). The avg. total volume loss on the wear test is 5 mm³ at 100 rpm.Gall-Tough®.. |
|||