Carpenter Gall-Tough® Stainless, Annealed and Cold Drawn Bar, 0% Cold Work

Category Metal , Ferrous Metal , Stainless Steel , T S20000 Series Stainless Steel
Manufacturer Carpenter Technology Corporation (Cartech)
Trade Name Gall-Tough®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Carpenter Gall-Tough® Stainless, Annealed and Cold Drawn Bar, 0% Cold Work.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by Carpenter Technology Corporation.Threshold Galling Stress 103 MPa (higher stress tests not performed). The avg. total volume loss on the wear test is 5 mm³ at 100 rpm.Gall-Tough® stainless is a high silicon, high manganese, nitrogen strengthened, austenitic stainless alloy which possesses superior self-mated galling resistance and metal-to-metal wear resistance. The alloy possesses higher strength and high temperature oxidation resistance than Type 304 stainless with comparable corrosion resistance, depending on the environment.Gall-Tough® is a registered trademark of Carpenter Technology Corporation.
Physical Properties Metric English Comments
Density 7.85 g/cc

@Temperature 23.0 °C
0.284 lb/in³

@Temperature 73.4 °F
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 979 MPa
142000 psi
1344 MPa

@Temperature -73.0 °C
194900 psi

@Temperature -99.4 °F
Tensile Strength, Yield 379 MPa

@Strain 0.200 %
55000 psi

@Strain 0.200 %
448 MPa

@Strain 0.200 %,
Temperature -73.0 °C
65000 psi

@Strain 0.200 %,
Temperature -99.4 °F
Elongation at Break 59 %
59 %
in 4D
47 %

@Temperature -73.0 °C
47 %

@Temperature -99.4 °F
in 4D
Reduction of Area 59 %
59 %
68 %

@Temperature -73.0 °C
68 %

@Temperature -99.4 °F
Modulus of Elasticity 171.1 GPa

@Temperature 23.0 °C
24820 ksi

@Temperature 73.4 °F
Charpy Impact 325 J
240 ft-lb
V-notch
Thermal Properties Metric English Comments
CTE, linear 17.3 µm/m-°C

@Temperature 25.0 - 100 °C
9.60 µin/in-°F

@Temperature 77.0 - 212 °F
17.73 µm/m-°C

@Temperature 25.0 - 250 °C
9.850 µin/in-°F

@Temperature 77.0 - 482 °F
18.5 µm/m-°C

@Temperature 25.0 - 500 °C
10.3 µin/in-°F

@Temperature 77.0 - 932 °F
Specific Heat Capacity 0.5145 J/g-°C

@Temperature 52.0 - 102 °C
0.1230 BTU/lb-°F

@Temperature 126 - 216 °F
Thermal Conductivity 12.22 W/m-K

@Temperature 23.0 °C
84.81 BTU-in/hr-ft²-°F

@Temperature 73.4 °F
Maximum Service Temperature, Air 982 °C
1800 °F
Scaling Temperature for Continuous Service
Component Elements Properties Metric English Comments
Carbon, C <= 0.15 %
<= 0.15 %
Chromium, Cr 15 - 18 %
15 - 18 %
Iron, Fe 68 %
68 %
as remainder
Manganese, Mn 4.0 - 6.0 %
4.0 - 6.0 %
Molybdenum, Mo 0.50 - 2.5 %
0.50 - 2.5 %
Nickel, Ni 4.0 - 6.0 %
4.0 - 6.0 %
Nitrogen, N 0.080 - 0.20 %
0.080 - 0.20 %
Phosphorous, P <= 0.040 %
<= 0.040 %
Silicon, Si 3.0 - 4.0 %
3.0 - 4.0 %
Sulfur, S <= 0.040 %
<= 0.040 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000716 ohm-cm

@Temperature 23.0 °C
0.0000716 ohm-cm

@Temperature 73.4 °F