- Special Metals INCONEL® 690 Nickel Superalloy, Cold Drawn Tube, 0.75 inch (19.0 mm) o.d. and 0.065 inch (1.65 mm) Thickness
Special Metals INCONEL® 690 Nickel Superalloy, Cold Drawn Tube, 0.75 inch (19.0 mm) o.d. and 0.065 inch (1.65 mm) Thickness
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | INCONEL® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals INCONEL® 690 Nickel Superalloy, Cold Drawn Tube, 0.75 inch (19.0 mm) o.d. and 0.065 inch (1.65 mm) Thickness.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Composition adjustments for nuclear applications: 28-31 Cr; 0.04 max C; 0.10 max Co.Tensile strength (ultimate and yield) and elongation values reported here are typical for Cold Drawn Tube, 0.75 inch (19.0 mm) o.d. and 0.065 inch (1.65 mm) Thickness. Other property values are typical of INCONEL® alloy 690.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.19 g/cc | 0.296 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 699.8 MPa | 101500 psi | |
| Tensile Strength, Yield | 379 MPa @Strain 0.200 % |
55000 psi @Strain 0.200 % |
|
| Elongation at Break | 46 % | 46 % | |
| Modulus of Elasticity | 211 GPa | 30600 ksi | |
| Poissons Ratio | 0.289 | 0.289 | |
| Shear Modulus | 81.8 GPa | 11900 ksi | Calculated |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.06 µm/m-°C @Temperature 24.0 - 100 °C |
7.811 µin/in-°F @Temperature 75.2 - 212 °F |
Mean |
| 14.53 µm/m-°C @Temperature 24.0 - 300 °C |
8.072 µin/in-°F @Temperature 75.2 - 572 °F |
Mean | |
| 15.19 µm/m-°C @Temperature 24.0 - 500 °C |
8.439 µin/in-°F @Temperature 75.2 - 932 °F |
Mean | |
| 17.41 µm/m-°C @Temperature 20.0 - 1000 °C |
9.672 µin/in-°F @Temperature 68.0 - 1830 °F |
Mean, extrapolated | |
| Specific Heat Capacity | 0.450 J/g-°C | 0.108 BTU/lb-°F | |
| Thermal Conductivity | 13.5 W/m-K | 93.7 BTU-in/hr-ft²-°F | |
| Melting Point | 1343 - 1377 °C | 2449 - 2511 °F | |
| Solidus | 1343 °C | 2449 °F | |
| Liquidus | 1377 °C | 2511 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.050 % | <= 0.050 % | |
| Chromium, Cr | 27 - 31 % | 27 - 31 % | |
| Copper, Cu | 0.50 % | 0.50 % | |
| Iron, Fe | 7.0 - 11 % | 7.0 - 11 % | |
| Manganese, Mn | <= 0.50 % | <= 0.50 % | |
| Nickel, Ni | >= 58 % | >= 58 % | |
| Silicon, Si | <= 0.50 % | <= 0.50 % | |
| Sulfur, S | <= 0.15 % | <= 0.15 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0001148 ohm-cm | 0.0001148 ohm-cm | |
| Magnetic Permeability | 1.001 | 1.001 | at 200 Oersted (15.9 kA/m) |
Users viewing this material also viewed the following:
- PolyMirae Moplen EP540S Injection Molding Grade Polypropylene
- Matrixx Group 80S7451 45% Glass Reinforced PET (discontinued **)
- LATI Latamid 66 H2 G/25-V0HF1 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant
- SABIC Innovative Plastics Ultem DH1004F PEI
- A. Schulman POLYTROPE™ TPP 524 Injection Molding Grade Olefinic Thermoplastic Elastomer
- CPT C-Flex® R70-050 Clear Biocompatible TPE
- Cossa Polimeri ESTALENE EN 25 C Modified Polyolefin Blend
- Epoxy Technology EPO-TEK® OM125 Optical Epoxy
- Clariant Renol PPSP0006HW Polypropylene Homopolymer, Heavy Weight Compound
- Abatron AboCoat 8709-10 Silver-Filled Electrically Conductive Acrylic Compound
Copyright © lookpolymers.com All Rights Reserved