Polymer Property : Tensile Strength, Yield = 103000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	708 MPa @Strain 0.200 %	103000 psi @Strain 0.200 %
Kennametal Stellite StelliteÂ® 6K 1.6 mm thick sheet 13.3 mm^3 volume loss--abrasive wear data. Applications include agitators, augers, ball mills, banbury mills, cams, crusher bearings, dryers, dry presses, dump cars, fans, filters, food machinery, g..
Tensile Strength, Yield	710 MPa @Strain 0.200 %, Temperature 650 Â°C	103000 psi @Strain 0.200 %, Temperature 1200 Â°F	Precipitation Hardened prior to test
Special Metals NIMONICÂ® Alloy 80A A nickel-chromium alloy similar to NIMONIC alloy 75 but made precipitation hardenable by additions of aluminum and titanium. The alloy has good corrosion and oxidation resistance and high tensile a..
Tensile Strength, Yield	710 MPa @Strain 0.200 %	103000 psi @Strain 0.200 %
Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Aged 732°C (1350°F)/4hr/AC Data provided by Carpenter Technology Corporation.Custom Age 625 PLUS® alloy is a precipitation hardenable, nickel-base alloy which, in many environments, displays corrosion resistance similar to t..
Tensile Strength, Yield	709 MPa @Strain 0.200 %	103000 psi @Strain 0.200 %
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 10% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i..
Tensile Strength, Yield	713 MPa @Strain 0.200 %	103000 psi @Strain 0.200 %
Carpenter Custom 455® Stainless Steel, Annealed, 25 mm Bar Data provided by Carpenter Technology Corporation.Recognizing the need for high-strength alloys with good corrosion resistance to atmospheric environments, the Carpenter Research Laboratory develope..
Tensile Strength, Yield	707 MPa @Treatment Temp. 760 °C, Time 1.44e+7 sec	103000 psi @Treatment Temp. 1400 °F, Time 4000 hour	0.2%. Room temp test after thermal exposure
Haynes 282® Nickel Alloy Plate, Solution Annealed and Age-Hardened, after long term high temperature exposure Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and land-b..
Tensile Strength, Yield	707 MPa	103000 psi
Kennametal Stellite Stellite® 4 Cobalt Chromium Alloy The higher tungsten content of Stellite alloy 4 gives improved high temperature properties and an increase in abrasive wear resistance over Stellite alloy 6, but not as good as Stellite alloy 12 or ..