Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Aged 732°C (1350°F)/4hr/AC

Category Metal , Nonferrous Metal , Nickel Alloy , Superalloy
Manufacturer Carpenter Technology Corporation (Cartech)
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Aged 732°C (1350°F)/4hr/AC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by Carpenter Technology Corporation.Custom Age 625 PLUS® alloy is a precipitation hardenable, nickel-base alloy which, in many environments, displays corrosion resistance similar to that of Alloy 625 and superior to that of Alloy 718. A yield strength (0.2% offset) above 120 ksi (827 MPa) can be obtained by aging without prior warm or cold working. The precipitation hardening capability is particularly important in applications where large-section size or intricate shape precludes warm working. In the age hardened (high strength) condition, Custom Age 625 PLUS alloy offers exceptional resistance to stress corrosion cracking as well as general, pitting and crevice corrosion.Custom Age 625 PLUS alloy could be considered for applications where severely corrosive environments are a concern, such as those encountered in deep sour gas wells as well as in a variety of refinery and chemical process industry applications. In addition, Custom Age 625 PLUS alloy could be considered a candidate for use in marine environments, where Alloy 625 has been used successfully. The higher strength capability of Custom Age 625 PLUS alloy may be particularly useful for fasteners and shafts.Custom Age 625 PLUS® is a registered trademark of Carpenter Technology Corporation.
Physical Properties Metric English Comments
Density 8.40 g/cc
0.303 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 290
290
Estimated from Rockwell C for 3000 kg load, 10 mm ball Brinell measurement.
Hardness, Knoop 315
315
Estimated from Rockwell C
Hardness, Rockwell C 30
30
Hardness, Vickers 304
304
Estimated from Rockwell C
Tensile Strength, Ultimate 1117 MPa
162000 psi
Tensile Strength, Yield 710 MPa

@Strain 0.200 %
103000 psi

@Strain 0.200 %
Elongation at Break 48 %
48 %
In 4D
Reduction of Area 65 %
65 %
Modulus of Elasticity 207 GPa

@Temperature 23.0 °C
30000 ksi

@Temperature 73.4 °F
Fatigue Strength 690 MPa

@# of Cycles 5.00e+6
100000 psi

@# of Cycles 5.00e+6
smooth, axial
Thermal Properties Metric English Comments
CTE, linear 12.6 µm/m-°C

@Temperature 25.0 - 100 °C
7.00 µin/in-°F

@Temperature 77.0 - 212 °F
13.4 µm/m-°C

@Temperature 25.0 - 300 °C
7.44 µin/in-°F

@Temperature 77.0 - 572 °F
14.0 µm/m-°C

@Temperature 25.0 - 500 °C
7.78 µin/in-°F

@Temperature 77.0 - 932 °F
Specific Heat Capacity 0.418 J/g-°C
0.0999 BTU/lb-°F
Melting Point 1257 - 1356 °C
2295 - 2473 °F
Solidus 1257 °C
2295 °F
Liquidus 1356 °C
2473 °F
Component Elements Properties Metric English Comments
Aluminum, Al <= 0.35 %
<= 0.35 %
Carbon, C <= 0.030 %
<= 0.030 %
Chromium, Cr 19 - 22 %
19 - 22 %
Iron, Fe 5.0 %
5.0 %
as remainder
Manganese, Mn <= 0.20 %
<= 0.20 %
Molybdenum, Mo 7.0 - 9.5 %
7.0 - 9.5 %
Nickel, Ni 59 - 63 %
59 - 63 %
Niobium, Nb (Columbium, Cb) 2.75 - 4.0 %
2.75 - 4.0 %
Phosphorous, P <= 0.015 %
<= 0.015 %
Silicon, Si <= 0.20 %
<= 0.20 %
Sulfur, S <= 0.010 %
<= 0.010 %
Titanium, Ti 1.0 - 1.6 %
1.0 - 1.6 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0001299 ohm-cm
0.0001299 ohm-cm