Polymer Property : Film Tensile Strength at Break, MD = 7980 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, MD	35.0 - 55.0 MPa	5080 - 7980 psi	ISO 527-3
Borealis BD212CF Polypropylene Copolymer BD212CF is a heterophasic copolymer. This grade is suitable for the manufacturing of unoriented films on cast and tubular quench film lines. Applications: BD212CF is designed for food packaging, l..
Film Tensile Strength at Break, MD	45.0 - 55.0 MPa	6530 - 7980 psi	ISO 527-3
Borealis Borclear™ RD738CF Propylene Alpha Olefin Copolymer for Cast Film Borclear RD738CF is a slip and antiblock formulation propylene alpha olefin copolymer resin. It is suitable for the manufacturing of unoriented film on chill roll process.Borclear RD738CF is suitabl..
Film Tensile Strength at Break, MD	45.0 - 55.0 MPa	6530 - 7980 psi	ISO 527-3
Borealis Borclear™ RE718CF Propylene Alpha Olefin Copolymer for Metallizable Cast Film Borclear RE718CF is a propylene alpha olefin copolymer resin formulation with antiblocking agent and without Ca-stearate, especially developed for the manufacturing of unoriented cast films for meta..
Film Tensile Strength at Break, MD	45.0 - 55.0 MPa	6530 - 7980 psi	ISO 527-3
Borealis Bormed™ TD109CF Polypropylene Copolymer Bormed™ TD109CF is a propylene alpha olefin copolymer. This grade is suitable for the manufacturing of unoriented films on cast and tubular quench film lines. Applications: lamination films, food..
Film Tensile Strength at Break, MD	35.0 - 55.0 MPa	5080 - 7980 psi	ISO 527-3
Borealis Bormod™ HD905CF Polypropylene Homopolymer for Cast Film Bormod HD905CF is a high crystallinity homopolymer film resin, based on special Borstar nucleating technology, suitable for the manufacturing of unoriented film on chill roll process. It is recomme..
Film Tensile Strength at Break, MD	35.0 - 55.0 MPa	5080 - 7980 psi	ISO 527-3
Borealis Bormod™ HD915CF Polypropylene Homopolymer for Cast Film Bormod HD915CF is a high crystallinity homopolymer film resin, based on special Borstar nucleating technology, especially developed for the manufacturing of unoriented film for metallizing. It is s..
Film Tensile Strength at Break, MD	35.6 - 55.0 MPa	5160 - 7980 psi	Average value: 47.1 MPa Grade Count:5
Overview of materials for High Density Polyethylene (HDPE), Injection Molded This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Injection Molded". Each property range of values reported is minimum a..
Film Tensile Strength at Break, MD	45.0 - 55.0 MPa	6530 - 7980 psi	Average value: 47.8 MPa Grade Count:4
Overview of materials for High Density Polyethylene (HDPE), Extruded This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Extruded". Each property range of values reported is minimum and maxim..