Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, MD | 45.0 MPa | 6530 psi | ISO 527-3 |
Polimeri Europa Clearflex® FG 306 Hexene Copolymer Linear Low Density Polyethylene Clearflex FG 306 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidant, antiblocking and processing aid, suitable for blown film extrusion.Films manufactured with Clearf.. |
|||
Film Tensile Strength at Break, MD | 45.0 MPa | 6530 psi | ISO 527-3 |
Polimeri Europa Clearflex® FG 308 Octene Copolymer Linear Low Density Polyethylene Clearflex FG 308 is an octene copolymer linear low density polyethylene (C8-LLDPE), with antioxidant and processing aid, suitable for blown film extrusion.Films manufactured with Clearflex FG 308 ar.. |
|||
Film Tensile Strength at Break, MD | 45.0 MPa | 6530 psi | ISO 527-3 |
Polimeri Europa Clearflex® FG 368 Octene Comonomer Linear Low Density Polyethylene Clearflex FG 368 is an octene copolymer linear low density polyethylene (C8-LLDPE), with antioxidant and processing aid, suitable for blown film extrusion.Films manufactured with Clearflex FG 368 ar.. |
|||
Film Tensile Strength at Break, MD | 45.0 MPa | 6530 psi | ASTM D882 |
SABIC 518N Linear Low Density Polyethylene for Blown Film Product Description: 548N is a fractional melt index Linear Low Density Polyethylene grade suitable for high strength packaging applications. Films produced using this resin yield outstanding toug.. |
|||
Film Tensile Strength at Break, MD | 45.0 MPa | 6530 psi | ISO 527-3 |
Polimeri Europa Flexirene® FF 25 Butene Copolymer Linear Low Density Polyethylene Flexirene FF 25 is a butene copolymer linear low density polyethylene (C4-LLDPE), with antioxidants, suitable for blown film extrusion.Flexirene FF 25 is characterized by a high elongational viscosi.. |
|||
Film Tensile Strength at Break, MD | 45.0 MPa | 6530 psi | ISO 527-3 |
Polimeri Europa Flexirene® FG 20 F Butene Copolymer Linear Low Density Polyethylene Flexirene FG 20 F is a butene copolymer linear low density polyethylene (C4-LLDPE), with antioxidants, suitable for blown film extrusion.Main Applications: Flexirene FG 20 F is recommended for the .. |
|||
Film Tensile Strength at Break, MD | 45.0 MPa | 6530 psi | ISO 527-3 |
Polimeri Europa Flexirene® FG 23 I Butene Copolymer Linear Low Density Polyethylene Flexirene FG 23 I is a butene copolymer linear low density polyethylene (C4-LLDPE), with antioxidants, suitable for blown film extrusion.Flexirene FG 23 I represents the version of Flexirene FG 20 I.. |
|||
Film Tensile Strength at Break, MD | 45.0 MPa | 6530 psi | ISO 527-3 |
Polimeri Europa Flexirene® FG 30 Butene Copolymer Linear Low Density Polyethylene Flexirene FG 30 is a butene copolymer linear low density polyethylene (C4-LLDPE), with antioxidants, suitable for blown film extrusion.Films manufactured with Flexirene FG 30 are characterized by an.. |
|||
Film Tensile Strength at Break, MD | 45.0 MPa | 6530 psi | ISO 527-3 |
Polimeri Europa Flexirene® FG 30 U Butene Copolymer Linear Low Density Polyethylene Flexirene FG 30 U is a butene copolymer linear low density polyethylene (C4-LLDPE), with antioxidants, suitable for blown film extrusion.Films manufactured with Flexirene FG 30 U are characterized b.. |
|||
Film Tensile Strength at Break, MD | 45.0 MPa | 6530 psi | ASTM D 882 |
NOVA Chemicals Sclair® 17A Butene HDPE Film Resin 17A complies with the U.S. FDA specifications for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food, without te.. |
|||
Film Tensile Strength at Break, MD | 45.0 MPa | 6530 psi | ISO 527-3 |
Polimeri Europa Flexirene® FG 20 I Butene Copolymer Linear Low Density Polyethylene Flexirene FG 20 I is a butene copolymer linear low density polyethylene (C4-LLDPE), with antioxidants, suitable for blown film extrusion.Main Applications: Flexirene FG 20 I is recommended for the .. |
|||
Film Tensile Strength at Break, MD | 45.0 MPa | 6530 psi | ISO 527-3 |
Polimeri Europa Flexirene® FG 23 F Butene Copolymer Linear Low Density Polyethylene Flexirene FG 23 F is a butene copolymer linear low density polyethylene (C4-LLDPE), with antioxidants, suitable for blown film extrusion.Flexirene FG 23 F represents the version of Flexirene FG 20 F.. |
|||
Film Tensile Strength at Break, MD | 45.0 MPa | 6530 psi | Blown Film at 1 mil; ASTM D-882 |
Chevron Phillips MarFlex® 7105DL Polyethylene; LLDPE
(discontinued **) Hexene linear low density polyethylene. This LLDPE is tailored for blown film applications that require: High strengthGood drawdownGood processabilityUse alone or in blends with LDPE or HDPEHigh a.. |
|||
Film Tensile Strength at Break, MD | 45.0 MPa | 6530 psi | 2 in per min; ASTM D882 |
Chevron Phillips Marlex® D252/257 Linear Low Density Polyethylene Film Resin
(discontinued **) Low Density, Linear Polyethylene Film ResinCustomer Benefits: This unique broad molecular weight distribution resin has a wide processing window and produces film with an excellent combination of to.. |
|||
Film Tensile Strength at Break, MD | 45.0 MPa | 6530 psi | ISO 527 |
Total Finathene® LL 6010 FH 18P LLDPE film
(discontinued **) Linear low density polyethylene made by gas phase process for blown film applications. Advised temperature profile: 190 to 220°C.Information provided provided by Total Petrochemicals.Total Petroche.. |
|||
Film Tensile Strength at Break, MD | 45.0 MPa | 6530 psi | ISO 527 |
Total Finathene® LL 6010 FE 18P LLDPE film
(discontinued **) Linear low density polyethylene made by gas phase process for blown film applications. Advised temperature profile: 190 to 220°C.Information provided provided by Total Petrochemicals.Total Petroche.. |
|||
Film Tensile Strength at Break, MD | 45.0 MPa | 6530 psi | ASTM D882 |
Chevron Phillips HiD® 9640 HDPE Blown Film Resin
(discontinued **) Copolymerization Enhances Film Toughness, Unique Combination of Density and Melt Index, Excellent Strength Properties as well as Good Heat Seal, Lower Density Imparts a Softer Feel and Lesser Tenden.. |
|||
Film Tensile Strength at Break, MD | 45.0 MPa | 6530 psi | ASTM D882 |
Reliance Industries Reclair O21010 Polyethylene Octene comonomer based Linear Low Density Polyethylene. Blow film grade. Contains an optimum level of antioxidants and polymer processing aids. Designed for lamination film applications. Character.. |
|||
Film Tensile Strength at Break, MD | <= 45.0 MPa | <= 6530 psi | ISO 527 |
Iran Petrochemical (PCC) EX 4 HM9455 F High Density Polyethylene EX4 is a high density polyethylene with 1-Butene as co monomer. It is high rigidity, low gel level, high drowdown, somewhat stiffer than EX 5.Applications: film extrusion, blending partner, refuse .. |
|||
Film Tensile Strength at Break, MD | <= 45.0 MPa | <= 6530 psi | ISO 527 |
Iran Petrochemical (PCC) EX 5 HM 9450 F High Density Polyethylene EX5 is a high density polyethylene with 1-Butene as co monomer.Applications: film extrusion, counter bag, carrier bag, wrapping filmsInformation provided by Iran Petrochemical Commercial Co. |
|||
Film Tensile Strength at Break, MD | <= 45.0 MPa | <= 6530 psi | ISO 527 |
Iran Petrochemical (PCC) EX 6HT HM 9455 HT High Density Polyethylene EX 6HT is a high density polyethylene with 1-Butene as co monomer. It has good toughness, low gel level, good tear strength, high tenacity.Applications: film extrusion, blending partner, refuse ba.. |
|||
Film Tensile Strength at Break, MD | <= 45.0 MPa | <= 6530 psi | ISO 527 |
Iran Petrochemical (PCC) EX 4HS HM 9455 F1 High Density Polyethylene EX 4HS is a high density polyethylene with 1-Butene as co monomer. It has high rigidity, low gel level, high drawdown, very high stiffness and good tenacity.Applications: film extrusion, blending .. |
|||
Film Tensile Strength at Break, MD | 45.0 MPa | 6530 psi | ASTM D882 |
SCG Chemicals EL-Leneâ„¢ H5615F High Density Polyethylene Film Key Characteristics:High speed processingHigh tensile strengthHigh dart impactLow gel contentGood moisture barrierRecommended Applications: Ultra thin film ( |
|||
Film Tensile Strength at Break, MD | 45.0 - 55.0 MPa | 6530 - 7980 psi | ISO 527-3 |
Borealis Borclear™ RD738CF Propylene Alpha Olefin Copolymer for Cast Film Borclear RD738CF is a slip and antiblock formulation propylene alpha olefin copolymer resin. It is suitable for the manufacturing of unoriented film on chill roll process.Borclear RD738CF is suitabl.. |
|||
Film Tensile Strength at Break, MD | 45.0 - 55.0 MPa | 6530 - 7980 psi | ISO 527-3 |
Borealis Borclear™ RE718CF Propylene Alpha Olefin Copolymer for Metallizable Cast Film Borclear RE718CF is a propylene alpha olefin copolymer resin formulation with antiblocking agent and without Ca-stearate, especially developed for the manufacturing of unoriented cast films for meta.. |
|||
Film Tensile Strength at Break, MD | 45.0 - 55.0 MPa | 6530 - 7980 psi | ISO 527-3 |
Borealis Bormed™ TD109CF Polypropylene Copolymer Bormed™ TD109CF is a propylene alpha olefin copolymer. This grade is suitable for the manufacturing of unoriented films on cast and tubular quench film lines. Applications: lamination films, food.. |
|||
Film Tensile Strength at Break, MD | 45.0 - 65.0 MPa | 6530 - 9430 psi | ISO 527-3 |
Borealis Borsoft™ SA233CF High Impact Polypropylene Random Heterophasic Copolymer for Blown Film Borsoft SA233CF is a very soft random heterophasic copolymer, suitable for use on conventional blown film lines with air-coolingBorsoft SA233CF is especially suitable for soft packaging, hygienic fi.. |
|||
Film Tensile Strength at Break, MD | 45.0 MPa | 6530 psi | ASTM D882 |
Braskem LL 118/21 LLDPE Blown Film Extrusion Polyethylene 38µm film gauge, obtained in 40mm extruder, with blow up ratio 2, 2:1Applications: Automatic packaging (FFS); "liners"; general purpose; HDPE and LDPE blends. Information provided by Braskem |
|||
Film Tensile Strength at Break, MD | 45.0 - 55.0 MPa | 6530 - 7980 psi | Average value: 47.8 MPa Grade Count:4 |
Overview of materials for High Density Polyethylene (HDPE), Extruded This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Extruded". Each property range of values reported is minimum and maxim.. |
|||
Film Tensile Strength at Break, MD | 45.0 MPa | 6530 psi | ISO 527-3 |
Polimeri Europa Clearflex® H&T LGH 108 Octene Copolymer Linear Low Density Polyethylene Clearflex H&T LGH 108 is an octene copolymer linear low density polyethylene (C8-LLDPE), with antioxidants and processing aid, suitable for blown film extrusion.Films obtained from Clearflex H&T LGH.. |