Polymer Property : Film Tensile Strength at Break, MD = 3400 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, MD	23.4 MPa	3400 psi	ASTM D882
LyondellBasell PetrotheneÂ® M2520FN Low Density Polyethylene ApplicationsPETROTHENE M 2520 is a film grade resin that exhibits excellent optics, good gloss and good bubble stability. A typical application for this resin is high clarity packaging. Regulatory..
Film Tensile Strength at Break, MD	23.4 MPa	3400 psi	ASTM D882
LyondellBasell PetrotheneÂ® NA143063 Low Density Polyethylene ApplicationsPETROTHENE NA 143 is a series of homopolymer resins for blown film. Applications include stiff liners. Regulatory StatusNA 143 meets the requirements of the Food and Drug Administration..
Film Tensile Strength at Break, MD	23.4 MPa	3400 psi	ASTM D882
LyondellBasell PetrotheneÂ® NA963083 Low Density Polyethylene ApplicationsPETROTHENE NA 963 is a series of resins formulated with special antiblock additive and designed for a wide variety of industrial film applications where high impact strength and excellen..
Film Tensile Strength at Break, MD	23.4 MPa	3400 psi	ASTM D882
Westlake EP310 Low Density Polyethylene WESTLAKE polyethylene EP310 is a low-density polyethylene suggested for cast film bakery applications. This material has outstanding optical and processing properties.Application/UsesBakery bagsSoft..
Film Tensile Strength at Break, MD	23.4 MPa	3400 psi	ASTM D882
ExxonMobil LDPE LD 129.24 Low Density Polyethylene Resin Product Description: LD 129.24 is a medium density homopolymer film resin with good clarity and excellent stiffness. Film made from LD 129.24 can be used in overwrap applications and in push-through..
Film Tensile Strength at Break, MD	23.4 MPa	3400 psi	ASTM D882
ExxonMobil Optema® TC-110 Cast Ethylene Methyl Acrylate Product Description: Optema TC 110 is an ethylene methyl acrylate copolymer specifically formulated to offer extrusion and property performance for blown and cast film applications. It can produce f..
Film Tensile Strength at Break, MD	23.4 MPa	3400 psi	ASTM D882
Dow INTEGRAL™ 900 Deep Draw Multilayer Adhesive Film INTEGRAL 900 Adhesive Film is a heat-activated, moldable, thermally stable adhesive film capable of bonding to urethane foam-baked fabrics, polyester and nylon fabrics, fiberglass, and rigid urethan..
Film Tensile Strength at Break, MD	23.4 MPa	3400 psi	ASTM D882
Dow XU 66129.00 Developmental Monolayer Adhesive Film XU 66129.00 Developmental Monolayer Adhesive Film is a heat-activated, thermally stable adhesive film capable of bonding to urethane foam-backed fabrics, paper, fiberglass, non-wovens, and rigid ure..