ExxonMobil LDPE LD 129.24 Low Density Polyethylene Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Exxon Chemical
Trade Name LDPE
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LDPE LD 129.24 Low Density Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: LD 129.24 is a medium density homopolymer film resin with good clarity and excellent stiffness. Film made from LD 129.24 can be used in overwrap applications and in push-through type packaging equipment. LD 129.24 is suitable for processing in either blown or cast film equipment. Availability: Latin America, North America and South America Additive: Antiblock: 1000 ppmSlip: NoThermal Stabilizer: YesApplications: Bread BagsCast FilmCo-Extrusion FilmsDiaper BacksheetEmbossed FilmHygiene PackagingLabel FilmOverwrap FilmPaper Overwrap Information provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.929 g/cc
0.0336 lb/in³
ExxonMobil method
Melt Flow 2.3 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.3 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Antiblock Level 2000 ppm
2000 ppm
Slip Level 400 ppm
400 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 14.5 MPa
2100 psi
ASTM D882
Film Tensile Strength at Yield, TD 15.9 MPa
2300 psi
ASTM D882
Film Elongation at Break, MD 180 %
180 %
ASTM D882
Film Elongation at Break, TD 460 %
460 %
ASTM D882
Puncture Energy 0.316 J
0.233 ft-lb
ExxonMobil Method
Elmendorf Tear Strength MD 100 g
100 g
ASTM D1922
Elmendorf Tear Strength TD 270 g
270 g
ASTM D1922
Dart Drop Test 70.0 g
0.154 lb
ASTM D1709A
Film Tensile Strength at Break, MD 23.4 MPa
3400 psi
ASTM D882
Film Tensile Strength at Break, TD 17.2 MPa
2500 psi
ASTM D882
1% Secant Modulus, MD 324 MPa
47000 psi
ASTM D882
1% Secant Modulus, TD 386 MPa
56000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point <= 242 °C
<= 468 °F
Peak Melting Point; ExxonMobil method
Optical Properties Metric English Comments
Haze 8.1 %
8.1 %
ASTM D1003
Gloss 68 %
68 %
45°; ASTM D2457
Descriptive Properties Value Comments
Puncture Force 7 lbf
ExxonMobil Method