Polymer Property : Film Tensile Strength at Break, MD = 100 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, MD	100 MPa	14500 psi	ASTM D882
Honeywell Stretch-Vac® 2000 Heat-Stabilized Blown Film (discontinued **) Description: Stretch-Vac® 2000 is a pink tinted, high elongation, heat-stabilized blown film produced from modified polyamide resin. It is available in widths up to 80 inches as layflat tubing and..
Film Tensile Strength at Break, MD	100 MPa	14500 psi	ISO 527
Victrex® APTIV® 1102-050M Polyetheretherketone (PEEK) Polymer Film, Semi-Crystalline, 20% Mineral Filled APTIV PEEK 1100 series films are the mineral filled semi-crystalline films made from VICTREX® PEEK polymer. The film provides a material solution for engineers in ultra-high performance application..
Film Tensile Strength at Break, MD	100 MPa @Thickness 0.100 mm	14500 psi @Thickness 0.00394 in	ISO 527
Victrex® APTIV® 1102-050M Polyetheretherketone (PEEK) Polymer Film, Semi-Crystalline, 20% Mineral Filled APTIV PEEK 1100 series films are the mineral filled semi-crystalline films made from VICTREX® PEEK polymer. The film provides a material solution for engineers in ultra-high performance application..
Film Tensile Strength at Break, MD	100 - 134 MPa	14500 - 19500 psi	ASTM D882
Honeywell ETFE EX30 Mono-Axially Oriented, ETFE Film (discontinued **) Description: ETFE EX30 is a 1.2 mil (30 micron) mono-axially oriented, ethylene tetrafluoroethylene (ETFE) film. It offers superior weather ability, UV transmission, chemical and graffiti resistanc..
Film Tensile Strength at Break, MD	100 MPa	14500 psi	ASTM D882
Honeywell Aegisâ„¢ H135MP Nylon 6 Extrusion Grade Homopolymer Film Description: Aegis H135MP is a lubricated and nucleated high viscosity, nylon 6 extrusion grade homopolymer for cast or blown film. It conforms to Food and Drug Administration requirements of 21 CFR..
Film Tensile Strength at Break, MD	100 MPa	14500 psi	ISO 527-3
EMS-Grivory Grivory® FG 34 NL nat 6023 PA6 Product description: Grilon FG 34 NL natural 6023 is a modified, medium viscosity polyamide 6. Grilon FG 34 NL natural 6023 exhibits following improvements compared to a PA 6: Better gas barrier pro..
Film Tensile Strength at Break, MD	100 MPa	14500 psi	ISO 527-3
EMS-Grivory Grivory® FG 40 NL nat 6018 PA6 Information provided by EMS Grivory
Film Tensile Strength at Break, MD	100 MPa	14500 psi	ISO 527-3
EMS-Grivory Grivory® FG 40 NL nat 6021 PA6 Product description: Grilon FG 40 NL natural 6021 is a modified, high viscosity polyamide 6. As a result of the modification in comparison to conventional polyamide 6 Grilon FG40 NL natural 6021 off..
Film Tensile Strength at Break, MD	100 MPa	14500 psi	ISO 527-3
EMS-Grivory Grivory® FG 47 NL nat 6028 PA6 Product description: Grilon FG 47 NL natural 6028 is a modified, high viscosity Polyamide 6, which contains also slip and nucleating agents. Grilon FG 47 NL natural 6028 shows following improvements..
Film Tensile Strength at Break, MD	100 MPa	14500 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Label-Lyte™ 33LL247 OPP Film Product Description: A super white opaque, high gloss, caviated BOPP film designed for use in reel-fed warp-around labeling applications where superior graphics are desired.Availability: Africa & Mi..
Film Tensile Strength at Break, MD	100 MPa	14500 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Label-Lyte™ 38LL247 OPP Film Product Description: A super white opaque, high gloss, cavitated BOPP film designed for use in reel-fed wrap-around labeling applications where superior graphics are desired.Availability: Africa & M..
Film Tensile Strength at Break, MD	100 MPa	14500 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Label-Lyte™ 38LW280 OPP Film Product Description: A super white opaque slip controlled, biaxially oriented polypropylene film, metalized on one side. Designed for use in reel-fed wrap-around applications, where outstanding meta..
Film Tensile Strength at Break, MD	100 MPa	14500 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Label-Lyte™ 47LL247 OPP Film Product Description: A super white opaque, high gloss, cavitated BOPP film designed for use in reel-fed wrap-around labeling applications where superior graphics are desired.Availability: Africa & M..
Film Tensile Strength at Break, MD	100 MPa	14500 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Label-Lyte™ 47LTL247 OPP Film Product Description: A super white opaque, high gloss, cavitated BOPP film designed for use in reel-fed wrap-around labeling applications where superior graphics are desired. 47LTL247 with supplied ..
Film Tensile Strength at Break, MD	100 MPa	14500 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Metallyte™ 38ICE M OPP Film Product Description: A coextruded super white opaque, low density, biaxially oriented polypropylene film, metalized on one side. This film is designed for HFFS applications, heat seal or cold seal.A..
Film Tensile Strength at Break, MD	100 MPa	14500 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Metallyte™ 38MW280 OPP Film Product Description: A super white opaque biaxially oriented polypropylene film, metalized on one side. Ideal for single web packaging applications on HFFS in combination with cold seal.Availability..
Film Tensile Strength at Break, MD	100 MPa	14500 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Metallyte™ 38MW480 OPP Film Product Description: A super white opaque biaxially oriented polypropylene film, metalized on one side.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features: Outstanding opacity an..
Film Tensile Strength at Break, MD	100 MPa	14500 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Oppalyte™ 35MW647 OPP Film Product Description: A super white opaque biaxially oriented polypropylene film acrylic coated two sides. Provides outstanding performances on all types of packaging machines.Availability: Africa & ..
Film Tensile Strength at Break, MD	100 MPa	14500 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Oppalyte™ 38ICE OPP Film Product Description: A coextruded white opaque, low density, biaxially oriented polypropylene film. This film is designed for the ice cream applications, and is suitable for heat seal and cold seal ..
Film Tensile Strength at Break, MD	100 MPa	14500 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Oppalyte™ 38MO447 OPP Film Product Description: A coextruded white opaque, low density, biaxially oriented polypropylene film, heat sealable on the inside. The treated layer must be printed and varnished to provide the necess..
Film Tensile Strength at Break, MD	100 MPa	14500 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Oppalyte™ 38MW247 OPP Film Product Description: A super white opaque biaxially oriented polypropylene film. It is designed for use in cold seal applications where superior optics and graphics are desired.Availability: Africa ..
Film Tensile Strength at Break, MD	100 MPa	14500 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Oppalyte™ 45MW647 OPP Film Product Description: A super white opaque biaxially oriented polypropylene film acrylic coated two sides. Acrylic provides excellent aroma barrier and excellent support for printing. The film provid..
Film Tensile Strength at Break, MD	100 MPa	14500 psi	ISO 527-3
EMS-Grivory Grivory® F 40 NL PA6 Product description: Grilon F 40 NL natural 6018 is a nucleated and lubricated high viscosity polyamide 6. This product exhibits the following features: Good gas barrierGood mechanical propertiesGoo..
Film Tensile Strength at Break, MD	100 MPa	14500 psi	ISO 527-3
EMS-Grivory Grivory® F 47 NL nat 6028 PA6 Product description: Grilon F 47 NL natural 6028 is a nucleated, high viscosity polyamide 6. This product exhibits the following features: Good gas barrierGood mechanical propertiesGood barrier agai..
Film Tensile Strength at Break, MD	100 MPa	14500 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Label-Lyte™ 60LH538 OPP Film Product Description: A super white opaque polypropylene film face stock with a proprietary caviated core providing high yield and excellent opacity. The coated print surface provides exceptional ink..
Film Tensile Strength at Break, MD	100 MPa	14500 psi	ASTM D882
Honeywell Stretch-Vac® Elastomax 1000 Heat-Stabilized Blown Film (discontinued **) Description: Capran® Elastomax 1000 is a pink tinted, heat-stabilized blown film produced from modified nylon resin. It is available in widths up to 80 inches as layflat tubing and 120 inches as s..
Film Tensile Strength at Break, MD	100 MPa	14500 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Oppalyte™ 30MW747 OPP Film Product Description: White opaque biaxially oriented polypropylene film coated on one side acrylic, one side PVdC. Provides excellent performances on all packaging machines. 30MW747 is a super white..
Film Tensile Strength at Break, MD	100 MPa	14500 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Oppalyte™ 33MW247 OPP Film Product Description: A super white opaque biaxially oriented polypropylene film. It is designed for use in cold seal applications where superior optics and graphics are desired.Availability: Africa ..
Film Tensile Strength at Break, MD	100 MPa	14500 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Oppalyte™ 40MW647 OPP Film Product Description: A super white opaque, biaxially oriented polypropylene film acrylic coated two sides. Provides outstanding performance on all types of packaging machines.Availability: Africa & ..
Film Tensile Strength at Break, MD	100 MPa	14500 psi	ISO 527-3
EMS-Grivory Grivory® F 50 nat 6368 PA6 Product description: Grilon F 50 natural 6368 is a modified, very high viscous Polyamide 6 for extrusion processes: Very high melt strengthGood chemical resistanceGood gas-barrierGood mechanical pro..