Polymer Property : Tensile Strength, Yield = 93.1 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	93.1 MPa @Thickness 1.57 mm	13500 psi @Thickness 0.0620 in	LW; ASTM D638
Industrial Laminates/Norplex NP325 Cotton Fabric Description: Linen phenolic laminate with graphite added as a solid lubricant. Linen substrate provides better machining and wear resistance than NP315.Thickness Tested: 0.062", 0.125" and 0.500".
Tensile Strength, Yield	93.1 MPa @Thickness 1.57 mm	13500 psi @Thickness 0.0620 in	CW; ASTM D638
Industrial Laminates/Norplex NP611 Paper Base Laminate Description: Hot punching general-purpose phenolic grade. Mechanical properties approach those of NP610 with improved electrical properties and moisture resistance.Thickness Tested: 0.062", 0 125" a..
Tensile Strength, Yield	93.1 MPa @Thickness 1.57 mm	13500 psi @Thickness 0.0620 in	LW; ASTM D638
Industrial Laminates/Norplex NP629 Paper Base Laminate Description: It is a paper-phenolic high-pressure laminate. It is intended primarily for mechanical applications and is suitable for electrical applications as well. Thickness Tested: 0.062", 0.125"..
Tensile Strength, Yield	93.1 MPa @Thickness 1.57 mm	13500 psi @Thickness 0.0620 in	CW; ASTM D638
Industrial Laminates/Norplex NP680 Paper Base Laminate Description: Hot punching grade with electrical properties between NP611 to NP631.Thickness Tested: 0.062", 0.125" & 0.500"
Tensile Strength, Yield	93.1 MPa @Temperature 649 °C	13500 psi @Temperature 1200 °F
Carlson C 800H Nickel-Iron-Chromium Alloy General DescriptionCarlson Alloy C 800 is a nickel-iron-chromium alloy, combining high strength with excellent resistance to oxidation and carburization at elevated temperatures. This alloy resists..