Industrial Laminates/Norplex NP680 Paper Base Laminate

Category Polymer , Thermoset
Manufacturer Industrial Laminates/Norplex
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Industrial Laminates/Norplex NP680 Paper Base Laminate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Hot punching grade with electrical properties between NP611 to NP631.Thickness Tested: 0.062", 0.125" & 0.500"
Physical Properties Metric English Comments
Specific Gravity 1.25 - 1.35 g/cc

@Thickness 1.57 mm
 1.25 - 1.35 g/cc

@Thickness 0.0620 in
 ASTM D792
Moisture Absorption at Equilibrium 1.5 %

@Thickness 1.57 mm
 1.5 %

@Thickness 0.0620 in
 ASTM D229
Mechanical Properties Metric English Comments
Hardness, Rockwell M 85 - 105

@Thickness 1.57 mm
 85 - 105

@Thickness 0.0620 in
 ASTM D785
Tensile Strength, Yield 93.1 MPa

@Thickness 1.57 mm
 13500 psi

@Thickness 0.0620 in
 CW; ASTM D638
117 MPa

@Thickness 1.57 mm
 17000 psi

@Thickness 0.0620 in
 LW; ASTM D638
Modulus of Elasticity 6.21 GPa

@Thickness 1.57 mm
 900 ksi

@Thickness 0.0620 in
 CW; ASTM D229
6.89 GPa

@Thickness 1.57 mm
 1000 ksi

@Thickness 0.0620 in
 LW; ASTM D229
Flexural Strength 149 MPa

@Thickness 1.57 mm
 21600 psi

@Thickness 0.0620 in
 CW; ASTM D790
182 MPa

@Thickness 1.57 mm
 26400 psi

@Thickness 0.0620 in
 LW; ASTM D790
Compressive Strength 262 MPa

@Thickness 12.7 mm
 38000 psi

@Thickness 0.500 in
 ASTM D695
Shear Strength 75.8 MPa

@Thickness 15.7 mm
 11000 psi

@Thickness 0.620 in
 ASTM D732
Izod Impact, Unnotched 0.262 J/cm

@Thickness 12.7 mm
 0.490 ft-lb/in

@Thickness 0.500 in
 CW, Cond E-48/50; ASTM D256
0.299 J/cm

@Thickness 12.7 mm
 0.560 ft-lb/in

@Thickness 0.500 in
 LW, Cond E-48/50; ASTM D256
Thermal Properties Metric English Comments
CTE, linear 20.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 11.1 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
CTE, linear, Transverse to Flow 16.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 8.89 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
Maximum Service Temperature, Air 130 °C
266 °F
Flammability, UL94 HB

@Thickness 1.57 mm
 HB

@Thickness 0.0620 in
Electrical Properties Metric English Comments
Dielectric Constant 5.0

@Thickness 1.57 mm
 5.0

@Thickness 0.0620 in
 Permittivity, Cond D-24/23; ASTM D150
Dielectric Strength 11.8 kV/mm

@Thickness 1.57 mm
 300 kV/in

@Thickness 0.0620 in
 Cond D-48/50; ASTM D229 S.T.
29.5 kV/mm

@Thickness 1.57 mm
 750 kV/in

@Thickness 0.0620 in
 Cond A; ASTM D229 S.T.
Dielectric Breakdown 10000 V

@Thickness 1.57 mm
 10000 V

@Thickness 0.0620 in
 Cond D-48/50; ASTM D229 S/S
55000 V

@Thickness 1.57 mm
 55000 V

@Thickness 0.0620 in
 Cond A; ASTM D229 S/S
Dissipation Factor 0.040

@Thickness 1.57 mm
 0.040

@Thickness 0.0620 in
 Cond D-24/23; ASTM D150
Arc Resistance 100 sec

@Thickness 3.17 mm
 100 sec

@Thickness 0.125 in
 ASTM D495
Comparative Tracking Index 180 V

@Thickness 3.17 mm
 180 V

@Thickness 0.125 in
 ASTM D3638
Descriptive Properties Value Comments
Bond Strength 1300 lb
0.5", ASTM D229
Color Natural, Black
Users viewing this material also viewed the following:
Copyright © lookpolymers.com All Rights Reserved