- Polymer Property : Tensile Strength at Break = 9000 psi
Polymer Property : Tensile Strength at Break = 9000 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 62.1 MPa | 9000 psi | 2 in/min; ASTM D638 |
| RheTech Products GC30P200-01BG 30% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, General Purpose Black, Blow Molding Grade Applications: Load floorSeat backFunctional supportsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | 2 in/min; ASTM D638 |
| RheTech Products GC35P200-01UV 35% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, UV Stabilized, General Purpose Black Applications: BracketsStructural componentsHeadlamp housingsWindow frameInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Polymer Resources PC-FR-UV-10-0002-16A Polycarbonate, Flame Retardant, Medium Flow Polycarbonate, Flame Retardant, Medium FlowFeatures: • Ultra High Impact Resistance • Self ExtinguishingProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on.. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Polymer Resources PC-GP3-D-[color]-6 Polycarbonate, FDA-compliant Feedstocks, High Flow with Mold Release Polycarbonate, FDA-compliant Feedstocks, High Flow with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samp.. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Ravago Manufacturing Americas Hylon® N1040MHL Nylon 6/6 (Cond) Information provided by Ravago. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D 638 |
| RTP Company RTP 301 TFE 15 FR L Polycarbonate (PC), Glass Fiber - PTFE Lubricated - Flame Retardant - Non-PBBO/E - UL94 V-0 The RTP 301 TFE FR L series of compounds incorporate various percentages of PTFE into a glass fiber reinforced polycarbonate base which also includes external lubricants for enhanced processing. Th.. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D 638 |
| RTP Company RTP 800 AR 15 TFE 10 Acetal (POM), Aramid Fiber Reinforced - PTFE Lubricated |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Polymer Resources NY6-IM1 Nylon 6, Impact Modified Nylon 6, Impact ModifiedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (.. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Polymer Resources NY6-IM1-[color]H Nylon, Impact Modified, Heat Stabilized (DAM) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provide.. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Polymer Resources PC-GP3-D-[color]-1 Polycarbonate, General Purpose, High Flow with Mold Release Polycarbonate, General Purpose, High Flow with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Infor.. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| M. Holland Company SA400 Styrene Acrylonitrile High clarityGood processabilityHigh stiffnessApplications: AppliancesCosmeticsHousehold goods |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Techmer ES Plaslube® NY-1/TF/20 BK223 PA66 |
|||
| Tensile Strength at Break | >= 62.1 MPa @Temperature 23.9 °C |
>= 9000 psi @Temperature 75.0 °F |
|
| Master Bond EP21ARHT Two component epoxy adhesive, sealant, coating and encapsulating system Product Description: Master Bond EP21ARHT is a two component epoxy resin system for high performance bonding, sealing, coating and encapsulating. It has a convenient 100 to 50 mix ratio by weight an.. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| A. Schulman ComAlloy® 510-3010 10% Glass Fiber Reinforced Polycarbonate Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| A. Schulman ComAlloy® 510-3010 10% Glass Fiber Reinforced Polycarbonate Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D 638 |
| RTP Company RTP 200 D UV Nylon 6/12 (PA); UV Stabilized |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D 638 |
| RTP Company RTP 200 TC-C-21 FR Nylon 6/6 (PA); Thermally Conductive - Electrically Conductive - Flame Retardant |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D 638 |
| RTP Company RTP 300 HF L UV Polycarbonate (PC), High Flow - Lubricated - UV Stabilized |
|||
| Tensile Strength at Break | >= 62.1 MPa | >= 9000 psi | |
| Master Bond EP30ND Non-Drip, Dimensionally Stable Epoxy Adhesive Description: Master Bond Polymer System EP30ND is a high viscosity, two component epoxy adhesive/sealant with a paste consistency. It will cure at room temperature or more rapidly at elevated temper.. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D 638 |
| RTP Company RTP 1300 C TFE 20 Polyphenylene Sulfide (PPS), PTFE Lubricated |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D 638 |
| RTP Company RTP 200 TFE 18 SI 2 HB Nylon 6/6 (PA) Unreinforced - PTFE Lubricated - Silicone Lubricated - UL94 HB |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | Compared to 300 for concrete |
| Abatron AboCrete Cement/Grout Resurfacing and Patching Epoxy Cement/grout resurfacing and patching epoxy for industrial, marine, institutional, and residential uses. The ultimate restoration and resurfacing material structurally and chemically superior to co.. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | |
| Abatron AboCast 8103-20 High-Performance Dielectric Epoxy AboCast 8103-20 is a dielectric in/outdoor epoxy system with superior arc-track resistance, high voltage and heat resistance, low ash and ion content, and it is chlorine-free. This system is unique .. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Polymer Resources PPX-GP5 Modified PPO, General Purpose with HDT of 270 F
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| PlastxWorld CEVIAN® A2603 15% GF PA/ABS Alloy, Conditioned Property data is for samples equilibrium moisture (1.1%)These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld.. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D 638 |
| RTP Company RTP 200 TC-I-20 FR Nylon 6/6 (PA), Thermally Conductive - Electrically Insulative - Flame Retardant |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D 638 |
| RTP Company RTP 800.5 Acetal (POM), Glass Fiber |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | 2 in/min; ASTM D638 |
| RheTech Products G20P100-406 20% Glass Fiber Reinforced Polypropylene, UV Stabilized, (Ford ZUEA) Midnight Black Applications: Arm rest insertVacuum canisterStorage binConsolesBattery traysInjection molding conditions reported in table.Information provided by RheTech Products. |
|||