Polymer Property : Tensile Strength at Break = 80000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	552 - 586 MPa	80000 - 85000 psi	304 Stainless Steel butt joint
Lucas-Milhaupt BRAZE 380 Characteristics:Braze 380 is a free-flowing, low temperature filler metal with excellent wetting of most ferrous and non-ferrous base metals, and is a good substitute for cadmium-bearing filler meta..
Tensile Strength at Break	552 - 586 MPa	80000 - 85000 psi	304 Stainless Steel butt joint
Lucas-Milhaupt BRAZE 452 Characteristics:Braze 452 is a free-flowing, low temperature filler metal commonly used to replace cadmium-bearing filler metals of similar silver content. This alloy is best suited for narrow gap ..
Tensile Strength at Break	552 MPa	80000 psi
Shakespeare WP-104 diameter 0.2 mm Weft Polyester Monofilament Paper Machine Clothing MonofilamentStandard molecular weightPolyesterLow modulusWeft yarnLow shrinkage Information provided by Shakespeare Company.
Tensile Strength at Break	552 MPa	80000 psi
Shakespeare WP-104 diameter 0.4 mm Weft Polyester Monofilament Paper Machine Clothing MonofilamentStandard molecular weightPolyesterLow modulusWeft yarnLow shrinkage Information provided by Shakespeare Company.
Tensile Strength at Break	552 MPa	80000 psi
Shakespeare WP-120 diameter 0.2 mm Weft Polyester Monofilament Paper Machine Clothing MonofilamentHigh molecular weightPolyesterLow modulusWeft yarnLow shrinkage Information provided by Shakespeare Company.
Tensile Strength at Break	552 MPa	80000 psi
Shakespeare WP-120 diameter 0.5 mm Weft Polyester Monofilament Paper Machine Clothing MonofilamentHigh molecular weightPolyesterLow modulusWeft yarnLow shrinkage Information provided by Shakespeare Company.
Tensile Strength at Break	552 MPa	80000 psi
Shakespeare WP-120 diameter 0.7 mm Weft Polyester Monofilament Paper Machine Clothing MonofilamentHigh molecular weightPolyesterLow modulusWeft yarnLow shrinkage Information provided by Shakespeare Company.
Tensile Strength at Break	552 MPa	80000 psi
Shakespeare WP-550 diameter 0.5 mm Hydrolytically Stabilized Polyester Yarn Paper Machine Clothing MonofilamentHigh molecular weightPolyesterHydrolytically stableWarp and weft yarnLow shrinkageLow modulus Information provided by Shakespeare Company.
Tensile Strength at Break	>= 552 MPa	>= 80000 psi
Master Bond EP17HT-3 One component, snap-curing epoxy system Product Description: Master Bond Polymer System EP17HT-3 is a one part epoxy that fully cures in 2-3 minutes at 250-300°F. It is capable of service up to +400°F with excellent strength retention p..
Tensile Strength at Break	552 MPa	80000 psi	Stress relieved
California Fine Wire Copper Clad 1006 Steel (40% Conductivity) All values may vary dependent on specific design and usage1006 steel core, 99.99% copper cladCapabilities: WireRibbonSquareInsulatedPlatedInformation provided by California Fine Wire.
Tensile Strength at Break	552 MPa	80000 psi	Annealed
California Fine Wire Dumet Nickel Iron Core Copper Clad Alloy All values may vary dependent on specific design and usage99.9% copper cladding over iron-nickel coreCapabilities: WireRibbonSquareInsulatedPlatedInformation provided by California Fine Wire.
Tensile Strength at Break	552 MPa	80000 psi	Stress relieved
California Fine Wire Nickel 220 Super Alloy All values may vary dependent on specific design and usageCapabilities: WireRibbonSquareInsulatedPlatedInformation provided by California Fine Wire.
Tensile Strength at Break	552 MPa	80000 psi	Stress relieved
California Fine Wire Nickel 5900 Nickel Alloy All values may vary dependent on specific design and usageCapabilities: WireRibbonSquareInsulatedPlatedInformation provided by California Fine Wire.
Tensile Strength at Break	>= 552 MPa	>= 80000 psi
Carlson 20 Plus Alloy Carlson C20 Plus is a super-austenitic alloy, developed to provide maximum resistance to corrosion by sulfuric acid. Nickel chromium, molybdenum and copper contribute to the excellent overall resist..
Tensile Strength at Break	>= 552 MPa	>= 80000 psi
Carlson 317L 4N Austenitic Stainless Steel General DescriptionCarlson’s 317L, 317L 4, and 317L 4N are austenitic chromium-nickel-molybdenum stainless steels with alloy contents greater than the 316 grades. The additional chromium, nickel a..
Tensile Strength at Break	>= 552 MPa	>= 80000 psi
Carlson C 600 Nickel-Chromium-Iron Alloy Carlson Alloy C 600 is nickel-chromium alloy, developed for use in severely corrosive environments at elevated temperatures. The high nickel content of this alloy provides excellent resistance to c..
Tensile Strength at Break	>= 552 MPa	>= 80000 psi
Carlson C 600ESR Nickel-Chromium-Iron Alloy General DescriptionCarlson Alloy C 600 is nickel-chromium alloy, developed for use in severely corrosive environments at elevated temperatures. The high nickel content of this alloy provides excell..
Tensile Strength at Break	>= 552 MPa	>= 80000 psi
Carlson C 601 Nickel-Chromium-Iron Alloy General DescriptionCarlson Alloy C 6021 is a nickel-chromium alloy, developed specifically for high –temperature service. This alloy exhibits outstanding resistance to both cyclic and static oxida..
Tensile Strength at Break	552 - 586 MPa	80000 - 85000 psi	304 Stainless Steel butt joint
Lucas-Milhaupt BRAZE 402 Silver Based Cadmium Free Filler Metal Characteristics: Braze 402 is a free-flowing, intermediate temperature filler metal and as such is a good substitute for cadmium-bearing filler metals with similar silver contents. The material is ..