Polymer Property : Tensile Strength at Break = 68.3 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	68.3 MPa	9900 psi	ASTM D638
Parker Chomerics PREMIER™ A220-FR EMI Shielding Plastic Description: PREMIER™ is the world’s first and most versatile commercially available conductive thermoplastic for real world EMI shielding solutions. It is a blend of PC/ABS thermoplastic polymer ..
Tensile Strength at Break	68.3 MPa @Temperature 23.0 °C	9910 psi @Temperature 73.4 °F	ISO 527-2
Solvay Specialty Polymers Amodel® AT-1002 HS Polyphthalamide (PPA) (Unverified Data**) Amodel AT-1002 HS is a neat, toughened, heat stabilized polyphthalamide (PPA) resin that offers superior retention of properties after humid thermal aging; high impact at low temperature and better ..
Tensile Strength at Break	68.3 MPa	9910 psi	ISO 527-2
Solvay Specialty Polymers AmodelÂ® AT-1002 HS Polyphthalamide (PPA) AmodelÂ® AT-1002 HS is a neat, toughened, heat stabilized polyphthalamide (PPA) resin that offers superior retention of properties after humid thermal aging; high impact at low temperature and bet..
Tensile Strength at Break	68.3 MPa	9910 psi	50 mm/min; ASTM D638
Styron CALIBREâ„¢ 2061 HD 15 Polycarbonate Resin Overview: CALIBREâ„¢ 2061 HD 15 Polycarbonate Resins are designed for steam and ethylene oxide sterilization required by the health care industry. CALIBRE 2061 HD 15 Polycarbonate Resins offer a ..
Tensile Strength at Break	68.3 MPa	9910 psi	50 mm/min; ASTM D638
Styron CALIBREâ„¢ 2061-15 Polycarbonate Resin Overview: CALIBREâ„¢ 2061-15 resin is suitable for steam and ethylene oxide sterilization required by the health care industry. CALIBRE 2061-15 provides excellent heat resistance, impact strength..
Tensile Strength at Break	68.3 MPa	9910 psi	50 mm/min; ASTM D638
Styron CALIBREâ„¢ 2061-6 Polycarbonate Resin Overview: CALIBREâ„¢ 2061-6 resin is suitable for steam and ethylene oxide sterilization required by the health care industry. CALIBRE 2061-6 provides excellent heat resistance, impact strength, ..
Tensile Strength at Break	68.3 MPa	9910 psi	50 mm/min; ASTM D638
Styron CALIBREâ„¢ 2091-15 Polycarbonate Resin Overview: CALIBREâ„¢ MEGARADâ„¢ 2091 Polycarbonate Resins are designed for single use medical devices (SUDs) that require gamma and electron-beam irradiation and an accelerated schedule for de..
Tensile Strength at Break	68.3 MPa	9910 psi	50 mm/min; ASTM D638
Styron CALIBREâ„¢ MEGARAD 2081-15 Polycarbonate Resin Overview: CALIBREâ„¢ MEGARAD 2081-15 Polycarbonate resin provides end-users of radiation sterilized medical devices a color closer to the water-clear look of the natural resin. When exposed to hi..
Tensile Strength at Break	68.3 MPa	9910 psi	50 mm/min; ASTM D638
Styron CALIBREâ„¢ MEGARAD 2081-6LR Polycarbonate Resin Overview: CALIBREâ„¢ 2081-6LR Polycarbonate resin was developed for medical applications requiring improved resistance to lipids over standard polycarbonate resins. When exposed to a 20% intralip..
Tensile Strength at Break	68.3 MPa	9910 psi	50 mm/min; ASTM D638
Styron CALIBREâ„¢ MEGARAD 2081-HD-15 2 Polycarbonate Resin Overview: CALIBREâ„¢ MEGARAD 2081 HD-15 2 polycarbonate resin provides end-users of radiation sterilized medical devices a color closer to the water-clear look of the natural resin. When exposed ..
Tensile Strength at Break	68.3 MPa	9900 psi	ASTM D638
Chase Plastics CP Pryme® NN100MD2 (COND, 50% RH) Nylon 66 with 2% MoS2 Lubricated Information provided by Chase Plastics.
Tensile Strength at Break	68.3 MPa	9900 psi	ASTM D638
Chase Plastics CP Pryme® PC100RHF Polycarbonate Form: PelletsInformation provided by Chase Plastics.