Solvay Specialty Polymers Amodel® AT-1002 HS Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® AT-1002 HS Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amodel AT-1002 HS is a neat, toughened, heat stabilized polyphthalamide (PPA) resin that offers superior retention of properties after humid thermal aging; high impact at low temperature and better mechanical properties than many unreinforced thermoplastic polyester and nylon resins. This material was specifically designed for automotive electrical/electronic applications such as connectors, sockets and sensors. - Black: AT-1002 HS BK 718 - Natural: AT-1002 HS NTInjection Notes: Injection Rate: 1 to 3 in/sec Holding Pressure: 50% of injection pressureData is presented for dry polymer unless noted as 'conditioned'.Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183/A
Water Absorption 0.50 %

@Time 86400 sec
0.50 %

@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.020 cm/cm
0.020 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.021 cm/cm
0.021 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 68.3 MPa

@Temperature 23.0 °C
9910 psi

@Temperature 73.4 °F
ISO 527-2
Tensile Strength 76.5 MPa
11100 psi
Conditioned; ASTM D638
83.4 MPa
12100 psi
ASTM D638
Tensile Strength, Yield 38.6 MPa

@Temperature 100 °C
5600 psi

@Temperature 212 °F
ISO 527-2
75.2 MPa

@Temperature 23.0 °C
10900 psi

@Temperature 73.4 °F
ISO 527-2
Elongation at Break 80 %
80 %
Type IV; ASTM D638
100 %
100 %
Type IV, Conditioned; ASTM D638
15 %

@Temperature 23.0 °C
15 %

@Temperature 73.4 °F
ISO 527-2
Elongation at Yield 3.7 %

@Temperature 100 °C
3.7 %

@Temperature 212 °F
ISO 527-2
5.0 %

@Temperature 23.0 °C
5.0 %

@Temperature 73.4 °F
ISO 527-2
Tensile Modulus 2.76 GPa
400 ksi
Conditioned; ASTM D638
2.76 GPa
400 ksi
ASTM D638
2.10 GPa

@Temperature 100 °C
305 ksi

@Temperature 212 °F
ISO 527-2
2.76 GPa

@Temperature 23.0 °C
400 ksi

@Temperature 73.4 °F
ISO 527-2
Flexural Strength 73.1 MPa
10600 psi
Conditioned; ASTM D790
103 MPa
14900 psi
ASTM D790
49.6 MPa

@Temperature 100 °C
7190 psi

@Temperature 212 °F
ISO 178
79.3 MPa

@Temperature 23.0 °C
11500 psi

@Temperature 73.4 °F
ISO 178
Flexural Modulus 2.21 GPa
321 ksi
ASTM D790
2.28 GPa
331 ksi
Conditioned; ASTM D790
1.72 GPa

@Temperature 100 °C
249 ksi

@Temperature 212 °F
ISO 178
2.28 GPa

@Temperature 23.0 °C
331 ksi

@Temperature 73.4 °F
ISO 178
Shear Strength 57.2 MPa
8300 psi
Conditioned; ASTM D732
64.1 MPa
9300 psi
ASTM D732
Izod Impact, Notched 1.40 J/cm
2.62 ft-lb/in
ASTM D256
1.50 J/cm
2.81 ft-lb/in
Conditioned; ASTM D256
Izod Impact, Notched (ISO) 13.0 kJ/m²
6.19 ft-lb/in²
ISO 180/1A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 180/1U
Charpy Impact Unnotched NB
NB
ISO 179/1eU
Charpy Impact, Notched 1.30 J/cm²
6.19 ft-lb/in²
ISO 179/1eA
Dart Drop, Total Energy 47.5 J
35.0 ft-lb
Conditioned; ASTM D3763
54.2 J
40.0 ft-lb
ASTM D3763
Penetration 4003
4003
N, Penetration Impact, Maximum Load, Conditioned; ASTM D3763
4448
4448
N, Penetration Impact, Maximum Load; ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 78.0 µm/m-°C

@Temperature 0.000 - 100 °C
43.3 µin/in-°F

@Temperature 32.0 - 212 °F
TMA; ASTM E831
130 µm/m-°C

@Temperature 100 - 200 °C
72.2 µin/in-°F

@Temperature 212 - 392 °F
TMA; ASTM E831
CTE, linear, Transverse to Flow 93.0 µm/m-°C

@Temperature 0.000 - 100 °C
51.7 µin/in-°F

@Temperature 32.0 - 212 °F
ASTM E831
140 µm/m-°C

@Temperature 100 - 200 °C
77.8 µin/in-°F

@Temperature 212 - 392 °F
ASTM E831
Melting Point 315 °C
599 °F
Peak; ASTM D3418
315 °C
599 °F
ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi) 163 °C
325 °F
Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 118 °C
244 °F
Unannealed; ISO 75-2/Af
121 °C
250 °F
Annealed; ASTM D648
Flammability, UL94 HB
HB
UL 94
Electrical Properties Metric English Comments
Volume Resistivity 7.00e+14 ohm-cm
7.00e+14 ohm-cm
Conditioned; ASTM D257
1.20e+16 ohm-cm
1.20e+16 ohm-cm
ASTM D257
Surface Resistance 2.50e+13 ohm
2.50e+13 ohm
Conditioned; ASTM D257
8.00e+13 ohm
8.00e+13 ohm
ASTM D257
Dielectric Constant 3.3

@Frequency 1.00e+6 Hz
3.3

@Frequency 1.00e+6 Hz
ASTM D150
3.3

@Frequency 60.0 Hz
3.3

@Frequency 60.0 Hz
ASTM D150
3.8

@Frequency 60.0 Hz
3.8

@Frequency 60.0 Hz
Conditioned; ASTM D150
3.8

@Frequency 1.00e+6 Hz
3.8

@Frequency 1.00e+6 Hz
Conditioned; ASTM D150
Dielectric Strength 17.0 kV/mm
432 kV/in
Conditioned; ASTM D149
17.0 kV/mm
432 kV/in
ASTM D149
Dissipation Factor 0.0040

@Frequency 60.0 Hz
0.0040

@Frequency 60.0 Hz
ASTM D150
0.016

@Frequency 1.00e+6 Hz
0.016

@Frequency 1.00e+6 Hz
ASTM D150
0.018

@Frequency 60.0 Hz
0.018

@Frequency 60.0 Hz
Conditioned; ASTM D150
0.035

@Frequency 1.00e+6 Hz
0.035

@Frequency 1.00e+6 Hz
Conditioned; ASTM D150
Comparative Tracking Index >= 600 V
>= 600 V
Conditioned; ASTM D3638
>= 600 V
>= 600 V
ASTM D3638
High Voltage Arc-Tracking Rate, HVTR 12.0 mm/min
0.472 in/min
Conditioned; UL 746
12.0 mm/min
0.472 in/min
UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 304 °C
579 °F
Front Barrel Temperature 324 °C
615 °F
Melt Temperature 321 - 329 °C
610 - 624 °F
Mold Temperature <= 90.0 °C
<= 194 °F
Drying Temperature 110 °C
230 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content 0.060 %
0.060 %