Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 68.3 MPa @Temperature 23.0 °C |
9910 psi @Temperature 73.4 °F |
ISO 527-2 |
Solvay Specialty Polymers Amodel® AT-1002 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel AT-1002 HS is a neat, toughened, heat stabilized polyphthalamide (PPA) resin that offers superior retention of properties after humid thermal aging; high impact at low temperature and better .. |
|||
Tensile Strength at Break | 68.3 MPa | 9910 psi | ISO 527-2 |
Solvay Specialty Polymers Amodel® AT-1002 HS Polyphthalamide (PPA) Amodel® AT-1002 HS is a neat, toughened, heat stabilized polyphthalamide (PPA) resin that offers superior retention of properties after humid thermal aging; high impact at low temperature and bet.. |
|||
Tensile Strength at Break | 68.3 MPa | 9910 psi | 50 mm/min; ASTM D638 |
Styron CALIBREâ„¢ 2061 HD 15 Polycarbonate Resin Overview: CALIBREâ„¢ 2061 HD 15 Polycarbonate Resins are designed for steam and ethylene oxide sterilization required by the health care industry. CALIBRE 2061 HD 15 Polycarbonate Resins offer a .. |
|||
Tensile Strength at Break | 68.3 MPa | 9910 psi | 50 mm/min; ASTM D638 |
Styron CALIBREâ„¢ 2061-15 Polycarbonate Resin Overview: CALIBREâ„¢ 2061-15 resin is suitable for steam and ethylene oxide sterilization required by the health care industry. CALIBRE 2061-15 provides excellent heat resistance, impact strength.. |
|||
Tensile Strength at Break | 68.3 MPa | 9910 psi | 50 mm/min; ASTM D638 |
Styron CALIBREâ„¢ 2061-6 Polycarbonate Resin Overview: CALIBREâ„¢ 2061-6 resin is suitable for steam and ethylene oxide sterilization required by the health care industry. CALIBRE 2061-6 provides excellent heat resistance, impact strength, .. |
|||
Tensile Strength at Break | 68.3 MPa | 9910 psi | 50 mm/min; ASTM D638 |
Styron CALIBREâ„¢ 2091-15 Polycarbonate Resin Overview: CALIBREâ„¢ MEGARADâ„¢ 2091 Polycarbonate Resins are designed for single use medical devices (SUDs) that require gamma and electron-beam irradiation and an accelerated schedule for de.. |
|||
Tensile Strength at Break | 68.3 MPa | 9910 psi | 50 mm/min; ASTM D638 |
Styron CALIBREâ„¢ MEGARAD 2081-15 Polycarbonate Resin Overview: CALIBREâ„¢ MEGARAD 2081-15 Polycarbonate resin provides end-users of radiation sterilized medical devices a color closer to the water-clear look of the natural resin. When exposed to hi.. |
|||
Tensile Strength at Break | 68.3 MPa | 9910 psi | 50 mm/min; ASTM D638 |
Styron CALIBREâ„¢ MEGARAD 2081-6LR Polycarbonate Resin Overview: CALIBREâ„¢ 2081-6LR Polycarbonate resin was developed for medical applications requiring improved resistance to lipids over standard polycarbonate resins. When exposed to a 20% intralip.. |
|||
Tensile Strength at Break | 68.3 MPa | 9910 psi | 50 mm/min; ASTM D638 |
Styron CALIBREâ„¢ MEGARAD 2081-HD-15 2 Polycarbonate Resin Overview: CALIBREâ„¢ MEGARAD 2081 HD-15 2 polycarbonate resin provides end-users of radiation sterilized medical devices a color closer to the water-clear look of the natural resin. When exposed .. |