Styron CALIBREâ„¢ 2061-6 Polycarbonate Resin

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer Styron
Trade Name CALIBRE™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron CALIBREâ„¢ 2061-6 Polycarbonate Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Overview: CALIBREâ„¢ 2061-6 resin is suitable for steam and ethylene oxide sterilization required by the health care industry. CALIBRE 2061-6 provides excellent heat resistance, impact strength, and processability. CALIBRE 2061-6 resin is compliant with ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications. This product contains mold release and is currently available in black color. Main Characteristics:ISO 10993Applications:Medical applicationsInformation provided by Styron
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183/A
Water Absorption 0.32 %

@Temperature 23.0 °C
 0.32 %

@Temperature 73.4 °F
 Equilibrium, 50% RH; ISO 62
0.15 %

@Temperature 23.0 °C,
Time 86400 sec
 0.15 %

@Temperature 73.4 °F,
Time 24.0 hour
 ISO 62
Maximum Moisture Content 0.020
0.020
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ISO 294-4
Melt Flow 6.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 6.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 73
73
ASTM D785
Hardness, Rockwell R 118
118
ASTM D785
Tensile Strength at Break 68.3 MPa
9910 psi
50 mm/min; ASTM D638
Tensile Strength, Yield 62.1 MPa
9010 psi
50 mm/min; ASTM D638
Elongation at Break 150 %
150 %
50 mm/min; ASTM D638
Elongation at Yield 6.0 %
6.0 %
50 mm/min; ASTM D638
Tensile Modulus 2.41 GPa
350 ksi
50 mm/min; ASTM D638
Flexural Strength 96.5 MPa
14000 psi
2.0 mm/min; ASTM D470
Flexural Modulus 2.41 GPa
350 ksi
2.0 mm/min; ASTM D470
Izod Impact, Notched 8.50 J/cm

@Temperature 23.0 °C
 15.9 ft-lb/in

@Temperature 73.4 °F
 ASTM D256
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ASTM D256
Tensile Impact Strength 567 kJ/m²
270 ft-lb/in²
ASTM D1822
Dart Drop, Total Energy 89.3 J
65.9 ft-lb
ASTM D3763
Abrasion 45
45
[%] Taber; ASTM D1044
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 68.0 µm/m-°C

@Temperature -40.0 - 82.0 °C
 37.8 µin/in-°F

@Temperature -40.0 - 180 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 145 °C
293 °F
Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 129 °C
264 °F
Unannealed; ASTM D648
142 °C
288 °F
Annealed; ASTM D648
Vicat Softening Point 156 °C

@Load 5.10 kg
 313 °F

@Load 11.2 lb
 Rate A (50°C/h); ASTM D1525
Oxygen Index 26 %
26 %
ISO 4289-2
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+17 ohm-cm
2.00e+17 ohm-cm
ASTM D257
Dielectric Constant 3.0

@Frequency 60.0 Hz
 3.0

@Frequency 60.0 Hz
 ASTM D150
3.0

@Frequency 1.00e+6 Hz
 3.0

@Frequency 1.00e+6 Hz
 ASTM D150
Dielectric Strength 17.0 kV/mm
432 kV/in
ASTM D149
Dissipation Factor 0.0010

@Frequency 50.0 Hz
 0.0010

@Frequency 50.0 Hz
 ASTM D150
0.0020

@Frequency 1.00e+6 Hz
 0.0020

@Frequency 1.00e+6 Hz
 ASTM D150
Processing Properties Metric English Comments
Rear Barrel Temperature 271 - 288 °C
520 - 550 °F
Middle Barrel Temperature 277 - 299 °C
531 - 570 °F
Front Barrel Temperature 299 - 327 °C
570 - 621 °F
Nozzle Temperature 299 - 327 °C
570 - 621 °F
Melt Temperature 299 - 327 °C
570 - 621 °F
Mold Temperature 76.7 - 110 °C
170 - 230 °F
Drying Temperature 121 °C
250 °F
Dry Time 3.00 hour
3.00 hour
Screw Speed 40 - 70 rpm
40 - 70 rpm