UBE UBEPOL VCR617 Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C)

Category Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE)
Manufacturer UBE
Trade Name UBEPOL
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF UBE UBEPOL VCR617 Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: UBEPOL-VCR is a new type of synthetic rubber system developed by UBE's original technology. UBEPOL-VCR consists of micro-dispersed syndiotactic 1,2-polybutadiene (SPB) with high melting point and crystallinity, and high cis-1,4-polybutadiene rubber matrix. UBEPOL-VCR is improved on the processability and a lot of physical properties of the conventional polybutadiene rubber (BR).Information provided by UBE.
Mechanical Properties Metric English Comments
Hardness, Shore A 78
78
ASTM D412
Tensile Strength at Break 17.9 MPa
2600 psi
ASTM D412
Elongation at Break 290 %
290 %
ASTM D412
100% Modulus 0.00640 GPa
0.928 ksi
ASTM D412
200% Modulus 0.0133 GPa
1.93 ksi
ASTM D412
Rebound 46 %
46 %
BS.903,PART22
Tear Strength 62.0 kN/m
354 pli
ASTM D624
Abrasion 62
62
Lombourn Abrasion Index (Iwamoto Seisakusyo, Japan); UBE Method
330
330
Pico Abrasion Index; ASTM D2228
Compression Set 18 %
18 %
Method B, 70°C, 72hrs; ASTM D395
Descriptive Properties Value Comments
Cut Generation De Mattia Flexing Machine Min 300,000 times
ASTM D430
Cut Growth (2mm-->15mm)  De Mattia Flexing Machine Min 105 times
ASTM D313
Goodrich Flex,  0.175" Stroke, 55lb, 100°C, P.S. 19%
ASTM D623 (44°C change in temperature)
Wet Skid Resistance on Safety-Walk 23
UBE Method (British Portable Skid Resistance Tester)