Polymer Property : Tensile Strength at Break = 245 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	245 MPa	35500 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RCL36S PA 66 LNP LUBRICOMP* RCL36S is a compound based on Nylon 66 resin containing 30% Carbon Fiber, 15% PTFE. Added features of this material include: Electrically Conductive, Wear Resistant, Heat Stabilized...
Tensile Strength at Break	245 MPa	35500 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RCL36S PA 66 (Asia Pacific) LNP LUBRICOMP* RCL36S is a compound based on Nylon 66 resin containing Carbon Fiber, PTFE. Added features of this material include: Electrically Conductive.
Tensile Strength at Break	245 MPa	35500 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RCL36 PA 66 LNP* LUBRICOMP* RCL36 is a compound based on Nylon 66 resin containing 15% PTFE, 30% Carbon Fiber. Added features of this material include: Wesr Resistant, Electrically Conductive.
Tensile Strength at Break	245 MPa	35500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP RX98372H PA 66 LNP* Thermocomp* RX98372H is a compound based on Nylon 66 resin containing Proprietary Fillers. Characteristics of this grade are: Healthcare.
Tensile Strength at Break	245 MPa	35500 psi	ISO 527
SABIC Innovative Plastics LNP Verton UV00A PPA LNP VERTON* UV00A is a compound based on Polyphthalamide resin containing Long Glass.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break	245 MPa	35500 psi	ISO 527
SABIC Innovative Plastics LNP Verton UV00A PPA (Asia Pacific) LNP VERTON* UV00A is a compound based on Polyphthalamide resin containing Long Glass.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength at Break	245 MPa	35500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP Verton UV00ASXS PPA (Europe-Africa-Middle East) LNP* VERTON* UV00ASXS is a compound based on Polyphthalamide resin containing Long Glass Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Tensile Strength at Break	245 MPa	35500 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® BG-60 FC PA6-GF60 Product description: Grilon BG-60 FC is a heat stabilized PA6 injection molding grade with 60% glass fibers. Grilon BG-60 FC has the following important properties: Short cycle timesExcellent surfac..
Tensile Strength at Break	245 MPa	35500 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® BG-50 H PA6-GF50 Product description: Grilon BG-50 H is a high heat stabilized PA6 injection molding grade with 50% glass fibers. Grilon BG-50 H has the following important properties: High stiffnessHigh heat resist..
Tensile Strength at Break	245 MPa	35500 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® BG-50 S PA6-GF50 Product description: Grilon BG-50 S is a heat stabilized PA6 injection molding grade with 50% glass fibers. Grilon BG-50 S has the following important properties: High stiffnessExcellent surface fin..
Tensile Strength at Break	245 MPa	35500 psi	5 [mm/min]; ISO 527-1/2
Akro-Plastic Akroloy® PA GF 60 (2844) PA 6.6 & PA6I/6T Conditioned, 60% Glass Filled One of the most characteristic properties of polyamide (PA 6.6) is the absorption of moisture. This essentially leads to increased toughness and elongation at break, to name the most important param..
Tensile Strength at Break	245 MPa	35500 psi	ISO 527-1, -2
LNP Verton™ UF-700-10 Polyphthalamide, Long Glass Fiber Reinforcement (discontinued **) Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names..