- Polymer Property : Tensile Strength at Break = 18.6 MPa
Polymer Property : Tensile Strength at Break = 18.6 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 18.6 MPa | 2700 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Wire & Cable JAC32A Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
| Tensile Strength at Break | 18.6 MPa | 2700 psi | 2 in/min; ASTM D638 |
| RheTech Products F4900-611UV Thermoplastic Polyolefin, UV Stabilized, XS9 Dark Neutral Metallic Applications: Exterior componentsBodyside moldingsStep padsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Tensile Strength at Break | 18.6 MPa | 2700 psi | 2 in/min; ASTM D638 |
| RheTech Products FT4900-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural Applications: Exterior componentsBodyside moldingsStep padsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Tensile Strength at Break | 18.6 MPa | 2700 psi | 2 in/min; ASTM D638 |
| RheTech Products FT4900-745UV Thermoplastic Polyolefin, UV Stabilized, CJM Medium Khaki Solid Applications: Exterior componentsBodyside moldingsStep padsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Tensile Strength at Break | 18.6 MPa | 2700 psi | 2 in/min; ASTM D638 |
| RheTech Products FT4900-74UV Thermoplastic Polyolefin, UV Stabilized, Exterior DX9 Black Applications: Exterior componentsBodyside moldingsStep padsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Tensile Strength at Break | 18.6 MPa | 2700 psi | 2 in/min; ASTM D638 |
| RheTech Products FT4900-772UV Thermoplastic Polyolefin, UV Stabilized, RXF Jet Black Applications: Exterior componentsBodyside moldingsStep padsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Tensile Strength at Break | 18.6 MPa | 2700 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ HC 2180 Polyvinyl Chloride, Flexible (PVC, Flexible) Geon HC 2180 is a 80 Shore A non-phthalate flexible vinyl compound made from FDA sanctioned ingredients. HC 2180 can be used for extrusion and injection molding healthcare applications.NOTE: All ing.. |
|||
| Tensile Strength at Break | 18.6 MPa | 2700 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ HC 2180G Polyvinyl Chloride, Flexible (PVC, Flexible) Geon HC 2180G is a 80 Shore A non-phthalate, gamma-stable flexible vinyl compound made from FDA sanctioned ingredients. HC 2180G can be used for extrusion and injection molding healthcare applicatio.. |
|||
| Tensile Strength at Break | 18.6 MPa | 2700 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ HC 3180G Polyvinyl Chloride, Flexible (PVC, Flexible) Geon HC 3180G is a non-phthalate, gamma-stable flexible vinyl compound made from FDA sanctioned ingredients. HC 3180G can be used for extrusion and injection molding healthcare applications. This pr.. |
|||
| Tensile Strength at Break | 18.6 MPa | 2700 psi | 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Flexible A9000 Polyvinyl Chloride, Flexible (PVC, Flexible) Recommended for interior applications.Information provided by PolyOne |
|||
| Tensile Strength at Break | 18.6 MPa | 2700 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Flexible R235AE Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
| Tensile Strength at Break | 18.6 MPa | 2700 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Flexible XV 3432 Trans 9000 Polyvinyl Chloride, Flexible (PVC, Flexible) This product has received full compliance certification for USP Biological Reactivity Tests under USP Plastic Class VI.NOTE: All ingredients used in the formulation of this compound are listed in th.. |
|||
| Tensile Strength at Break | 18.6 MPa | 2700 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Flexible XV3887 Polyvinyl Chloride, Flexible (PVC, Flexible) All ingredients used in the formulation of this compound are listed in the United States FDA Code of Federal Regulations, Title 21. The only restriction is that the plasticizer is For foods of high .. |
|||
| Tensile Strength at Break | 18.6 MPa | 2700 psi | 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Flexible C5D01 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
| Tensile Strength at Break | 18.6 MPa | 2700 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Flexible R235AE White 1875 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
| Tensile Strength at Break | 18.6 MPa | 2700 psi | ASTM D4894 |
| 3M Dyneon™ CCX6380 PTFE, 10% Polyimide Filler
(discontinued **) Type II, free flowing.Typical Applications: Finished or semi-finished parts: sheets, rods, tubes, billets for skiving of films or machining into complex shapes.Information provided by the Dyneon div.. |
|||
| Tensile Strength at Break | 18.6 MPa | 2700 psi | 2 in/min; ASTM D638 |
| Ineos R01A-00 Polypropylene Random Copolymer Random copolymer R01A-00 is an antistatic polypropylene produced by a unique catalyst technology. It is designed for blow molding and extrusion applications and exhibits good stiffness and improved .. |
|||
| Tensile Strength at Break | 18.6 - 20.7 MPa | 2700 - 3000 psi | |
| ITW Plexus Plexusâ„¢ MA920 Methacrylate Adhesive Two-part adhesive designed for structural bonding of thermoplastic, metal, and composite assemblies.All purpose, low odor, short open time.Information provided by Illinois Tool Works. |
|||
| Tensile Strength at Break | 18.6 MPa | 2700 psi | 2 in/min; ASTM D638 |
| Ineos R05C-00 Polypropylene Random Copolymer Random copolymer R05C-00 is an antistatic, clarified polypropylene random copolymer produced by a unique catalyst technology. It is designed as a high gloss resin and exhibits good stiffness and imp.. |
|||
| Tensile Strength at Break | 18.6 MPa | 2700 psi | ASTM D638 |
| Teknor Apex APEX® 77-W280B-9 Polyvinyl Chloride, Flexible Notes: 60°C Jacket; RoHS Compliant Uses: Wire and Cable ApplicationsForms: PelletsInformation Provided by Teknor Apex |
|||
| Tensile Strength at Break | 18.6 MPa | 2700 psi | ASTM D412 |
| Teknor Apex MF 165 NT Polyvinyl Chloride, Flexible Film Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMUses-Film, Medical Applications Forms-PelletsAppearance-ClearInformation provided by Teknor Apex Company |
|||
| Tensile Strength at Break | 18.6 MPa | 2700 psi | ASTM D638 |
| Teknor Apex MF 165-J3 NT Polyvinyl Chloride, Flexible Film Uses: Medical/Healthcare Applications Forms: FilmInformation Provided by Teknor Apex |
|||
| Tensile Strength at Break | 18.6 MPa | 2700 psi | ASTM D412 |
| UBE UBEPOL VCR406 Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C) Description: UBEPOL-VCR is a new type of synthetic rubber system developed by UBE's original technology. UBEPOL-VCR consists of micro-dispersed syndiotactic 1,2-polybutadiene (SPB) with high mel.. |
|||
| Tensile Strength at Break | 18.6 MPa | 2700 psi | ASTM D638 |
| Borealis LE0595-07 Polyethylene Compound, Crosslinkable, Semiconductive LE0595-07 is a crosslinkable black polyethylene compound, specially designed for bonded semi conductive screen applications. LE0595-07 is a crosslinkable black polyethylene compound, specially desi.. |
|||
| Tensile Strength at Break | 18.6 MPa | 2700 psi | PVC (70)/CP80AS2(30) |
| Lubrizol Estane® CP80AS2 Thermoplastic Polyurethane Type: Estane® CP80AS2 is a soft, polyester based thermoplastic polyurethane resin.Features: Outstanding compatibility with flexible PVC allowing easy dispersion without pre-compounding.Uses: Tube/H.. |
|||
| Tensile Strength at Break | 18.6 MPa | 2690 psi | ASTM D3759 |
| 3M Scotch® 8959 Bi-Directional Filament Tape Scotch® Filament Tape 8959 is a bi-directional specialty packaging tape reinforced with continuous glass yarns in both the longitudinal and transverse direction along with a biaxially oriented poly.. |
|||
| Tensile Strength at Break | 18.6 MPa | 2700 psi | ASTM D3759 |
| 3M 5700 Safety Stripe Tape 3M™ Safety Stripe Tapes are durable vinyl tapes used to identify and mark traffic areas and physical hazards.Information provided by 3M |
|||
| Tensile Strength at Break | 18.6 MPa | 2700 psi | ASTM D3759 |
| 3M 5702 Safety Stripe Tape 3M™ Safety Stripe Tapes are durable vinyl tapes used to identify and mark traffic areas and physical hazards.Information provided by 3M |
|||
| Tensile Strength at Break | 18.6 MPa | 2700 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Flexible R350AE Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||