Polymer Property : Tensile Strength at Break = 10.5 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	10.5 MPa	1520 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Flexible 90250 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne
Tensile Strength at Break	10.5 MPa	1520 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Flexible 90461 Polyvinyl Chloride, Flexible (PVC, Flexible) Automotive OEM approval(s).Information provided by PolyOne
Tensile Strength at Break	10.5 MPa	1520 psi	Type IV specimen, compression molded, crosshead speed 2 in/min; ASTM D638
DuPont Nucrel® 2940 Ethylene-Methacrylic Acid Copolymer Resin (discontinued **) Nucrel® 2940is a tough, lightweight, easily processed ethylene copolymer resin. This resin is inherently flexible without the need for plasticizers. The resin can be pigmented, UV-stabilized for ..
Tensile Strength at Break	10.5 MPa	1520 psi	ASTM D638
LG Chemical LUTENE MB9500 LDPE Injection Molding Grade Description: The physical and structural characteristics of LUTENE MB9500 give it excellent flow properties and good productivity, clarity and surface gloss.Main Application: Powder coating, artific..
Tensile Strength at Break	<= 10.5 MPa	<= 1520 psi	after aging (6 weeks); IEC 60811-1-2
Borealis Visico™/Ambicat™ LE4427/LE4476 Polyethylene Compound, Crosslinkable Visico™ LE4427 / Ambicat™ LE4476 is a silane crosslinkable black compound designed for weather resistant covering/insulation of overhead and façade cables. The black base material Visico™ LE442..
Tensile Strength at Break	10.5 MPa	1520 psi	ISO 527-2
Carmel Olefins IPETHENE® 670 Low Density Polyethylene IPETHENE® 670 is a low density polyethylene extrusion coating and lamination grade. This grade can be processed at high coating temperatures and coating speeds. It exhibits low neck-in and stable w..
Tensile Strength at Break	10.5 MPa	1520 psi	ISO 527-2
Carmel Olefins IPETHENE® 810 Low Density Polyethylene IPETHENE® 810 is a low density polyethylene injection molding grade. It exhibits high melt flow rate, high gloss, and high stiffness. APPLICATIONS IPETHENE® 810 is used to produce lids, containe..
Tensile Strength at Break	10.5 MPa	1520 psi	ISO 527-2
Carmel Olefins IPETHENE® 470 Low Density Polyethylene IPETHENE® 470 is a low density polyethylene extrusion coating and lamination grade. This grade can be processed at high coating temperatures and coating speeds. It exhibits low neck-in and stable w..
Tensile Strength at Break	10.5 MPa	1520 psi	ISO 527-2
Carmel Olefins IPETHENE® 600 Low Density Polyethylene IPETHENE® 600 is a low density polyethylene injection molding grade. This grade is a good carrier for masterbatches production. It exhibits good stiffness and moderate melt flow rate. APPLICATIONS..
Tensile Strength at Break	<= 10.5 MPa	<= 1520 psi	after aging 168h, 150°C, 9% catalyst); IEC 60811-1-2
Borealis Visico™/Ambicat™ LE4421/LE4476 Polyethylene Compound, Crosslinkable Visico™ LE4421 / Ambicat™ LE4476 is a silane crosslinkable natural compound designed for low voltage power cables up to 6kV. The base material Visico™ LE4421 in combination with the catalyst mas..
Tensile Strength at Break	10.5 MPa	1530 psi	Air at 302°F, 168 hr; ASTM D573
ExxonMobil Santoprene® 101-80 Thermoplastic Elastomer A soft, black, versatile thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance for use in a wide range ..