- Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
- Kingfa FW-650 Flame Retardant ABS
Kingfa FW-650 Flame Retardant ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant |
| Manufacturer | Kingfa Sci. & Tech. Co. |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kingfa FW-650 Flame Retardant ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features:Weather resistanceSuper high impact resistanceApplications:Injection moldingSwitchSocketInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc @Temperature 23.0 °C |
1.10 g/cc @Temperature 73.4 °F |
ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm @Temperature 23.0 °C |
0.0040 - 0.0060 in/in @Temperature 73.4 °F |
ASTM D955 |
| Melt Flow | 2.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| 25 g/10 min @Load 10.0 kg, Temperature 220 °C |
25 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 95 | 95 | ASTM D785 |
| Tensile Strength at Break | 37.0 MPa | 5370 psi | 50mm/min; ASTM D638 |
| Elongation at Break | 20 % | 20 % | 50mm/min; ASTM D638 |
| Flexural Strength | 56.0 MPa | 8120 psi | 2mm/min; ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | 2mm/min; ASTM D790 |
| Izod Impact, Notched | 2.87 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
5.38 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| 3.11 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
5.83 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 87.0 °C @Thickness 6.40 mm |
189 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C @Thickness 6.40 mm |
172 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 91.0 °C @Load 5.00 kg |
196 °F @Load 11.0 lb |
50°C/min; ASTM D1525 |
| 101 °C @Load 1.00 kg |
214 °F @Load 2.20 lb |
120°C/min; ASTM D1525 | |
| Flammability Test | <= 750 | <= 750 | [°C]; IEC60695 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 23.0 kV/mm | 584 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 245 °C | <= 473 °F | |
| Rear Barrel Temperature | 180 - 210 °C | 356 - 410 °F | Start Point: 190°C |
| Middle Barrel Temperature | 190 - 220 °C | 374 - 428 °F | Start Point: 205°C |
| Front Barrel Temperature | 200 - 230 °C | 392 - 446 °F | Start Point: 215°C |
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | Start Point: 220°C |
| Mold Temperature | 30.0 - 60.0 °C | 86.0 - 140 °F | Start Point: 50°C |
| Drying Temperature | 70.0 - 80.0 °C @Time 7200 - 14400 sec |
158 - 176 °F @Time 2.00 - 4.00 hour |
Pre-dry |
| Back Pressure | 0.000 - 1.00 MPa | 0.000 - 145 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed | Slow to Moderate | |
| Weather Resistance (delta E) | ASTM D4459; 300hr |