- Polymer Property : Flexural Strength = 28900 psi
Polymer Property : Flexural Strength = 28900 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 199 MPa | 28900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics LNP Lubricomp OFG26XXP PPS - Linear LNP* Lubricomp* OFG26XXP is a compound based on Linear PPS containing Glass Fiber and Graphite Powder. Characteristics of this grade are Internally Lubricated.This data was supplied by SABIC-IP for.. |
|||
| Flexural Strength | 199 MPa | 28900 psi | ISO 178 |
| Solvay TECHNYL® eXten D238 V30 Nylon 6,10, 30% glass fiber, DRY Description: TECHNYL® eXten D 238 V30 is a PA6,10 30% glass fiber reinforced and impact modified suitable for injection molding. TECHNYL® eXten D 238 V30 is based on a partially bio-sourced po.. |
|||
| Flexural Strength | 199 MPa | 28900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| SABIC Innovative Plastics ULTEM 2100 PEI 10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. NSF 51 listing, WRAS certification in recognized colors. |
|||
| Flexural Strength | 199 MPa | 28900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| SABIC Innovative Plastics ULTEM 2100 PEI (Asia Pacific) 10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. NSF 51 listing, WRAS certification in recognized colors. |
|||
| Flexural Strength | 199 MPa | 28900 psi | 2.6 mm/min, 100 mm span; ASTM D 790 |
| SABIC Innovative Plastics Ultem 2100N PEI (Asia Pacific) 10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Flexural Strength | 199 MPa | 28900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| SABIC Innovative Plastics ULTEM 2100R PEI 10% Glass fiber filled, standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing. |
|||
| Flexural Strength | 199 MPa | 28900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| SABIC Innovative Plastics ULTEM 2100R PEI (Asia Pacific) 10% Glass fiber filled, standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing. |
|||
| Flexural Strength | 199 MPa | 28900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| SABIC Innovative Plastics ULTEM 2110 PEI (Asia Pacific) 10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. |
|||
| Flexural Strength | 199 MPa | 28900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP STAT-KON DE0069F PC (Asia Pacific) LNP* Stat-kon* DE0069F is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, , Flame Retardant. |
|||
| Flexural Strength | 199 MPa | 28900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP STAT-KON DEL13EXC PC (Asia Pacific) LNP* STAT-KON* DEL13EXC is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber. Added features of this material include: Easy Molding. |
|||
| Flexural Strength | 199 MPa | 28900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics Valox® 414 PBT (Asia Pacific) 40% GR, increased strength/stiffness vs unreinforced. Non-flame retardant. For appliance handles, spotlights, electric motors, pump housings etc.This data was supplied by SABIC-IP for the Asia Pacif.. |
|||
| Flexural Strength | 199 MPa | 28900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP DF006 PC (Asia Pacific) LNP* Thermocomp* DF006 is a compound based on Polycarbonate resin containing Glass Fiber. |
|||
| Flexural Strength | 199 MPa | 28900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP DF006HL PC LNP THERMOCOMP* DF006HL is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material include: Low Extractible, Healthcare. |
|||
| Flexural Strength | 199 MPa | 28900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP DF006HL PC (Asia Pacific) LNP* THERMOCOMP* DF006HL is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Low Extractible. |
|||
| Flexural Strength | 199 MPa | 28900 psi | ASTM D 790 |
| SABIC Innovative Plastics LNP Thermocomp LF003E PEEK (Asia Pacific) LNP* Thermocomp* LF003E is a compound based on Polyetheretherketone resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Flexural Strength | 199 MPa | 28900 psi | ASTM D 790 |
| SABIC Innovative Plastics LNP Thermocomp OFJ66 PPS - Linear LNP* Thermocomp* OFJ66 is a compound based on PPS - Linear resin containing Glass Fiber, Mineral. Added features of this material include: Low Warpage.This data was supplied by SABIC-IP for the Ame.. |
|||
| Flexural Strength | 199 MPa | 28900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP QF0069 PA6.10 LNP* THERMOCOMP* QF0069 is a compound based on Nylon 6/10 resin containing 30% Glass Fiber. Added features of this material include: Flame Retardant. |
|||
| Flexural Strength | 199 MPa | 28900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP RF00469S PA 66 LNP* THERMOCOMP* RF00469S is a compound based on Nylon 66 resin containing 20% Glass Fiber. Added features of this material include: Flame Retardant, Heat Stabilized. |
|||
| Flexural Strength | 199 MPa | 28900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP RF00469S PA 66 (Asia Pacific) LNP* Thermocomp* RF00469S is a compound based on Nylon 66 resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant, Heat Stabilized. |
|||
| Flexural Strength | 199 MPa | 28900 psi | ASTM D 790 |
| SABIC Innovative Plastics LNP Thermocomp RF0049S PA 66 LNP THERMOCOMP* RF0049S is a compound based on Nylon 66 resin containing Flame Retardant, Glass Fiber. Added features of this material include: Flame Retardant.This data was supplied by SABIC-IP fo.. |
|||
| Flexural Strength | 199 MPa | 28900 psi | ASTM D 790 |
| SABIC Innovative Plastics LNP Thermocomp RF0049S PA 66 (Asia Pacific) LNP THERMOCOMP* RF0049S is a compound based on Nylon 66 resin containing Flame Retardant, Glass Fiber. Added features of this material include: Flame Retardant.This data was supplied by SABIC-IP fo.. |
|||
| Flexural Strength | 199 MPa | 28900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP WF008 PBT (Asia Pacific) LNP* THERMOCOMP* WF008 is a compound based on Polybutylene Terephalate resin containing Glass Fiber. |
|||
| Flexural Strength | 199 MPa | 28900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP ZF406XXX PPO Blend (Asia Pacific) LNP THERMOCOMP* ZF406XXX is a compound based on PPO Blend resin containing Flame Retardant, Glass Fiber. Added features of this material include: Flame Retardant. |
|||
| Flexural Strength | 199 MPa | 28900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| SABIC Innovative Plastics ULTEM 2110R PEI 10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing. |
|||
| Flexural Strength | 199 MPa | 28900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| SABIC Innovative Plastics ULTEM 2110R PEI (Asia Pacific) 10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing. |
|||
| Flexural Strength | 199 MPa | 28900 psi | ASTM D 790 |
| SABIC Innovative Plastics LNP Thermocomp OFJ66 PPS - Linear (Asia Pacific) LNP* Thermocomp* OFJ66 is a compound based on PPS - Linear resin containing Glass Fiber, Mineral. Added features of this material include: Low Warpage.This data was supplied by SABIC-IP for the Asi.. |
|||
| Flexural Strength | 199 MPa | 28900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOTUF DF008EI PC LNP* Thermotuf* DF008EI is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release, High Impact. |
|||
| Flexural Strength | 199 MPa | 28900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOTUF DF008EI PC (Asia Pacific) LNP* Thermotuf* DF008EI is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release, High Impact. |
|||
| Flexural Strength | 199 MPa | 28900 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP Verton MV00ASUV_WH9D703 PP Preliminary data for 50% Long fiber single color pellet filled PPThis data was supplied by SABIC-IP for the Americas region. |
|||
| Flexural Strength | 199 MPa | 28900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| SABIC Innovative Plastics ULTEM 2110 PEI 10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. |
|||
Copyright © lookpolymers.com All Rights Reserved