SABIC Innovative Plastics LNP THERMOCOMP DF006HL PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DF006HL PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* DF006HL is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material include: Low Extractible, Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D792 |
| Density | 1.43 g/cc | 0.0517 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.120 % | 0.120 % | 50% RH, 24 hrs; ASTM D570 |
| 0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0040 cm/cm @Time 86400 sec |
0.0010 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm @Time 86400 sec |
0.0050 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 110 MPa | 16000 psi | 5 mm/min; ISO 527 |
| 114 MPa | 16500 psi | Type I, 5 mm/min; ASTM D638 | |
| 126 MPa | 18300 psi | ASTM D638 | |
| Tensile Strength, Yield | 110 MPa | 16000 psi | 5 mm/min; ISO 527 |
| 115 MPa | 16700 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.7 % | 2.7 % | ASTM D638 |
| 3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
| 3.2 % | 3.2 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.8 % | 2.8 % | Type I, 5 mm/min; ASTM D638 |
| 2.8 % | 2.8 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 7.80 GPa | 1130 ksi | 1 mm/min; ISO 527 |
| 8.34 GPa | 1210 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 174 MPa | 25200 psi | ISO 178 |
| 180 MPa | 26100 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 199 MPa | 28900 psi | ASTM D790 | |
| Flexural Yield Strength | 183 MPa | 26500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 7.20 GPa | 1040 ksi | 2 mm/min; ISO 178 |
| 7.50 GPa | 1090 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 8.35 GPa | 1210 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.67 J/cm | 3.13 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.30 J/cm | 15.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 52.0 kJ/m² | 24.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 27.0 J @Temperature 23.0 °C |
19.9 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 8.00 J | 5.90 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 32.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 69.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C | 297 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 147 °C @Thickness 3.20 mm |
297 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 143 °C | 289 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 144 °C @Thickness 3.20 mm |
291 °F @Thickness 0.126 in |
unannealed; ASTM D648 |