Ravago Manufacturing Americas Hylon® N1000STL Nylon 6/6 (DAM)  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ravago Manufacturing Americas Hylon® N1000STL Nylon 6/6 (DAM)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Entec.
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
ASTM D792
Water Absorption 0.80 %
0.80 %
24 hrs; ASTM D570
Linear Mold Shrinkage 0.019 cm/cm
0.019 in/in
0.125 in; ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 107
107
ASTM D785
Tensile Strength at Break 51.7 MPa
7500 psi
ASTM D638
Elongation at Break 55 %
55 %
ASTM D638
Flexural Strength 72.4 MPa
10500 psi
ASTM D790
Flexural Modulus 1.79 GPa
260 ksi
ASTM D790
Izod Impact, Notched 8.54 J/cm
16.0 ft-lb/in
73°F; ASTM D256
Thermal Properties Metric English Comments
CTE, linear 140 µm/m-°C

@Temperature 20.0 °C
78.0 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 218 °C
425 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 68.3 °C
155 °F
Unannealed; ASTM D648
Flammability, UL94 HB
HB
0.0590 in, NC
HB
HB
0.118 in, NC
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
ASTM D257
Dielectric Constant 3.2

@Frequency 100 Hz
3.2

@Frequency 100 Hz
ASTM D150
Processing Properties Metric English Comments
Melt Temperature 277 - 293 °C
530 - 560 °F
Mold Temperature 48.9 - 87.8 °C
120 - 190 °F
Drying Temperature 73.9 °C
165 °F
Dry Time 2 - 4 hour
2 - 4 hour
Moisture Content 0.18 %
0.18 %
Back Pressure 0.138 - 0.414 MPa
20.0 - 60.0 psi
Screw Speed 40 - 120 rpm
40 - 120 rpm
Descriptive Properties Value Comments
Holding Pressure 400 to 1400 psi
Injection Rate Fast