DuPont Performance Polymers Hytrel® 3078FG Polyester Elastomer TPC-ET  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer DuPont Performance Polymers
Trade Name Hytrel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hytrel® 3078FG Polyester Elastomer TPC-ET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30 Shore D High Performance Polyester Elastomer Developed for Food Contact ApplicationsInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
ISO 1183
Water Absorption 0.80 %

@Thickness 2.00 mm
0.80 %

@Thickness 0.0787 in
Sim. to ISO 62
Moisture Absorption 0.200 %

@Thickness 2.00 mm
0.200 %

@Thickness 0.0787 in
Sim. to ISO 62
Linear Mold Shrinkage, Flow 0.0060 cm/cm
0.0060 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
ISO 294-4 2577
Melt Flow 5.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
5.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
5.3 g/10 min

@Load 2.16 kg,
Temperature 190 °C
5.3 g/10 min

@Load 4.76 lb,
Temperature 374 °F
cm³/10min; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 26
26
15s; ISO 868
<= 30
<= 30
ISO 868
Tensile Strength at Break 23.0 MPa
3340 psi
ISO 527-1/-2
Tensile Stress 1.10 MPa

@Strain 10.0 %
160 psi

@Strain 10.0 %
ISO 527-1/-2
4.10 MPa

@Strain 50.0 %
595 psi

@Strain 50.0 %
ISO 527-1/-2
0.620 MPa

@Strain 7.80 %,
Temperature 120 °C
89.9 psi

@Strain 7.80 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
0.890 MPa

@Strain 7.88 %,
Temperature 100 °C
129 psi

@Strain 7.88 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
0.960 MPa

@Strain 18.94 %,
Temperature 120 °C
139 psi

@Strain 18.94 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
1.04 MPa

@Strain 7.84 %,
Temperature 90.0 °C
151 psi

@Strain 7.84 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
1.13 MPa

@Strain 30.07 %,
Temperature 120 °C
164 psi

@Strain 30.07 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
1.24 MPa

@Strain 41.21 %,
Temperature 120 °C
180 psi

@Strain 41.21 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
1.27 MPa

@Strain 7.29 %,
Temperature 60.0 °C
184 psi

@Strain 7.29 %,
Temperature 140 °F
TPE; ISO 11403-1 -2
1.31 MPa

@Strain 52.35 %,
Temperature 120 °C
190 psi

@Strain 52.35 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
1.36 MPa

@Strain 6.64 %,
Temperature 40.0 °C
197 psi

@Strain 6.64 %,
Temperature 104 °F
TPE; ISO 11403-1 -2
1.37 MPa

@Strain 5.71 %,
Temperature 0.000 °C
199 psi

@Strain 5.71 %,
Temperature 32.0 °F
TPE; ISO 11403-1 -2
1.37 MPa

@Strain 67.2 %,
Temperature 120 °C
199 psi

@Strain 67.2 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
1.40 MPa

@Strain 82.8 %,
Temperature 120 °C
203 psi

@Strain 82.8 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
1.40 MPa

@Strain 168.19 %,
Temperature 120 °C
203 psi

@Strain 168.19 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
1.40 MPa

@Strain 149.63 %,
Temperature 120 °C
203 psi

@Strain 149.63 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
1.41 MPa

@Strain 19.13 %,
Temperature 100 °C
205 psi

@Strain 19.13 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
1.42 MPa

@Strain 134.78 %,
Temperature 120 °C
206 psi

@Strain 134.78 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
1.45 MPa

@Strain 97.65 %,
Temperature 120 °C
210 psi

@Strain 97.65 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
1.45 MPa

@Strain 112.5 %,
Temperature 120 °C
210 psi

@Strain 112.5 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
1.64 MPa

@Strain 18.07 %,
Temperature 90.0 °C
238 psi

@Strain 18.07 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
1.68 MPa

@Strain 30.38 %,
Temperature 100 °C
244 psi

@Strain 30.38 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
1.74 MPa

@Strain 8.52 %,
Temperature 23.0 °C
252 psi

@Strain 8.52 %,
Temperature 73.4 °F
TPE; ISO 11403-1 -2
1.83 MPa

@Strain 41.63 %,
Temperature 100 °C
265 psi

@Strain 41.63 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
1.94 MPa

@Strain 52.88 %,
Temperature 100 °C
281 psi

@Strain 52.88 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
1.98 MPa

@Strain 28.98 %,
Temperature 90.0 °C
287 psi

@Strain 28.98 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
2.03 MPa

@Strain 67.88 %,
Temperature 100 °C
294 psi

@Strain 67.88 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
2.08 MPa

@Strain 17.02 %,
Temperature 60.0 °C
302 psi

@Strain 17.02 %,
Temperature 140 °F
TPE; ISO 11403-1 -2
2.09 MPa

@Strain 82.14 %,
Temperature 100 °C
303 psi

@Strain 82.14 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
2.14 MPa

@Strain 97.14 %,
Temperature 100 °C
310 psi

@Strain 97.14 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
2.18 MPa

@Strain 112.14 %,
Temperature 100 °C
316 psi

@Strain 112.14 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
2.18 MPa

@Strain 39.89 %,
Temperature 90.0 °C
316 psi

@Strain 39.89 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
2.25 MPa

@Strain 134.64 %,
Temperature 100 °C
326 psi

@Strain 134.64 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
2.28 MPa

@Strain 149.65 %,
Temperature 100 °C
331 psi

@Strain 149.65 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
2.32 MPa

@Strain 168.4 %,
Temperature 100 °C
336 psi

@Strain 168.4 %,
Temperature 212 °F
TPE; ISO 11403-1 -2
2.33 MPa

@Strain 50.8 %,
Temperature 90.0 °C
338 psi

@Strain 50.8 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
2.34 MPa

@Strain 16.44 %,
Temperature 40.0 °C
339 psi

@Strain 16.44 %,
Temperature 104 °F
TPE; ISO 11403-1 -2
2.41 MPa

@Strain 65.12 %,
Temperature 90.0 °C
350 psi

@Strain 65.12 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
2.43 MPa

@Strain 13.11 %,
Temperature 0.000 °C
352 psi

@Strain 13.11 %,
Temperature 32.0 °F
TPE; ISO 11403-1 -2
2.49 MPa

@Strain 79.43 %,
Temperature 90.0 °C
361 psi

@Strain 79.43 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
2.55 MPa

@Strain 93.75 %,
Temperature 90.0 °C
370 psi

@Strain 93.75 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
2.55 MPa

@Strain 26.74 %,
Temperature 60.0 °C
370 psi

@Strain 26.74 %,
Temperature 140 °F
TPE; ISO 11403-1 -2
2.59 MPa

@Strain 5.25 %,
Temperature -20.0 °C
376 psi

@Strain 5.25 %,
Temperature -4.00 °F
TPE; ISO 11403-1 -2
2.60 MPa

@Strain 108.07 %,
Temperature 90.0 °C
377 psi

@Strain 108.07 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
2.66 MPa

@Strain 129.89 %,
Temperature 90.0 °C
386 psi

@Strain 129.89 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
2.72 MPa

@Strain 144.21 %,
Temperature 90.0 °C
395 psi

@Strain 144.21 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
2.78 MPa

@Strain 162.62 %,
Temperature 90.0 °C
403 psi

@Strain 162.62 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
2.87 MPa

@Strain 37.16 %,
Temperature 60.0 °C
416 psi

@Strain 37.16 %,
Temperature 140 °F
TPE; ISO 11403-1 -2
2.87 MPa

@Strain 187.85 %,
Temperature 90.0 °C
416 psi

@Strain 187.85 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
2.89 MPa

@Strain 20.12 %,
Temperature 23.0 °C
419 psi

@Strain 20.12 %,
Temperature 73.4 °F
TPE; ISO 11403-1 -2
2.91 MPa

@Strain 26.23 %,
Temperature 40.0 °C
422 psi

@Strain 26.23 %,
Temperature 104 °F
TPE; ISO 11403-1 -2
3.08 MPa

@Strain 46.89 %,
Temperature 60.0 °C
447 psi

@Strain 46.89 %,
Temperature 140 °F
TPE; ISO 11403-1 -2
3.13 MPa

@Strain 20.5 %,
Temperature 0.000 °C
454 psi

@Strain 20.5 %,
Temperature 32.0 °F
TPE; ISO 11403-1 -2
3.27 MPa

@Strain 36.02 %,
Temperature 40.0 °C
474 psi

@Strain 36.02 %,
Temperature 104 °F
TPE; ISO 11403-1 -2
3.28 MPa

@Strain 60.08 %,
Temperature 60.0 °C
476 psi

@Strain 60.08 %,
Temperature 140 °F
TPE; ISO 11403-1 -2