Polymer Property : 300% Modulus = 2.28 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
300% Modulus	0.0157 GPa	2.28 ksi	aged 70 hours at 250ºF in ASTM Oil #903
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 20 PHR HAF Black (Typical) MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c..
300% Modulus	0.0157 GPa	2.28 ksi	Vulcanized
KKPC KOSYN 1500M Styrene Butadiene Rubber Styrene Butadiene RubberCharacteristics: KOSYN SBR, a useful synthetic rubber, is a copolymer made from butadiene and styrene by cold emulsion polymerization. It has superior abrasion resistance and..
300% Modulus	0.0157 GPa @Temperature 145 Â°C, Time 2100 sec	2.28 ksi @Temperature 293 Â°F, Time 0.583 hour	ASTM D412
LG Chemical SBR 1500 High Acrylonitrile Polymer Description: NSBR 1500 is a cold polymerized styrene-butadiene copolymer with staining stabilizer. The cold polymerized SBR exhibits better abrasion, higher tensile strength and higher modulus than ..
300% Modulus	0.0157 GPa @Temperature 145 Â°C, Time 2100 sec	2.28 ksi @Temperature 293 Â°F, Time 0.583 hour	ASTM D412
LG Chemical SBR 1500H High Acrylonitrile Polymer Description: SBR 1500H is a cold polymerized styrene-butadiene copolymer with non-staining stabilizer and especially well-suited for adhesive applications. It has high internal strength, and excelle..
300% Modulus	0.0157 GPa	2.28 ksi	150Â°C, 40 min., Pressure Vulcanization. 40% Change after 100Â°C, 70 hrs, Oil Immersion
KKPC KOSYN KNB 230 Acrylonitrile Butadiene Rubber (NBR) Acrylonitrile Butadiene Rubber (NBR)Characteristics: KOSYN KNB is copolymer of high oil resistance and chemical resistance made from acrylonitrile and butadiene by the cold emulsion polymerization. ..
300% Modulus	0.0157 GPa	2.28 ksi	150Â°C, 40 min., Pressure Vulcanization. 43% Change after 100Â°C, 70 hrs, Oil Immersion
KKPC KOSYN KNB 35H Acrylonitrile Butadiene Rubber (NBR) Acrylonitrile Butadiene Rubber (NBR)Characteristics: KOSYN KNB is copolymer of high oil resistance and chemical resistance made from acrylonitrile and butadiene by the cold emulsion polymerization. ..
300% Modulus	0.0157 GPa @Temperature 145 Â°C, Time 2990 sec	2.28 ksi @Temperature 293 Â°F, Time 0.830 hour	cured; ASTM D412
LG Chemical NBR 6280 High Acrylonitrile Polymer Description: NBR 6280 is a copolymer of butadiene and acrylonitrile manufactured by advanced emulsion polymerization technology of Goodyear and LG Chem. NBR 6280 is a non staining, high mooney, and ..
300% Modulus	0.0157 GPa	2.28 ksi
Taiwan PU Corporation TPUI-E95 General Grade, Injection Molding Polyester Base TPU Thermoplastic Polyurethane (TPU), General Grade, Polyester Base, Injection MoldingInformation provided by Taiwan PU Corporation.
300% Modulus	0.0157 GPa	2.28 ksi	ASTM D412
Lubrizol Estane® ALR CL87A Thermoplastic Polyurethane Type: Estane® ALR CL87A is an aliphatic, polycaprolactone-based TPU with a Shore A Durometer of 85-90.Features: Contains a UV package that enhances outdoor weatherability. This high performance re..
300% Modulus	0.0157 GPa	2.28 ksi	aged 70 hours at 250ºF in ASTM Oil #903
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 20 PHR HAF Black (Typical) MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c..
300% Modulus	0.0157 GPa	2.28 ksi
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 70A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c..
300% Modulus	0.0157 GPa	2.28 ksi
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 70A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c..