Mechanical Properties | Metric | English | Comments |
---|---|---|---|
300% Modulus | 0.0157 GPa | 2.28 ksi | aged 70 hours at 250ºF in ASTM Oil #903 |
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 20 PHR HAF Black (Typical) MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
300% Modulus | 0.0157 GPa | 2.28 ksi | Vulcanized |
KKPC KOSYN 1500M Styrene Butadiene Rubber Styrene Butadiene RubberCharacteristics: KOSYN SBR, a useful synthetic rubber, is a copolymer made from butadiene and styrene by cold emulsion polymerization. It has superior abrasion resistance and.. |
|||
300% Modulus | 0.0157 GPa @Temperature 145 °C, Time 2100 sec |
2.28 ksi @Temperature 293 °F, Time 0.583 hour |
ASTM D412 |
LG Chemical SBR 1500 High Acrylonitrile Polymer Description: NSBR 1500 is a cold polymerized styrene-butadiene copolymer with staining stabilizer. The cold polymerized SBR exhibits better abrasion, higher tensile strength and higher modulus than .. |
|||
300% Modulus | 0.0157 GPa @Temperature 145 °C, Time 2100 sec |
2.28 ksi @Temperature 293 °F, Time 0.583 hour |
ASTM D412 |
LG Chemical SBR 1500H High Acrylonitrile Polymer Description: SBR 1500H is a cold polymerized styrene-butadiene copolymer with non-staining stabilizer and especially well-suited for adhesive applications. It has high internal strength, and excelle.. |
|||
300% Modulus | 0.0157 GPa | 2.28 ksi | 150°C, 40 min., Pressure Vulcanization. 40% Change after 100°C, 70 hrs, Oil Immersion |
KKPC KOSYN KNB 230 Acrylonitrile Butadiene Rubber (NBR) Acrylonitrile Butadiene Rubber (NBR)Characteristics: KOSYN KNB is copolymer of high oil resistance and chemical resistance made from acrylonitrile and butadiene by the cold emulsion polymerization. .. |
|||
300% Modulus | 0.0157 GPa | 2.28 ksi | 150°C, 40 min., Pressure Vulcanization. 43% Change after 100°C, 70 hrs, Oil Immersion |
KKPC KOSYN KNB 35H Acrylonitrile Butadiene Rubber (NBR) Acrylonitrile Butadiene Rubber (NBR)Characteristics: KOSYN KNB is copolymer of high oil resistance and chemical resistance made from acrylonitrile and butadiene by the cold emulsion polymerization. .. |
|||
300% Modulus | 0.0157 GPa @Temperature 145 °C, Time 2990 sec |
2.28 ksi @Temperature 293 °F, Time 0.830 hour |
cured; ASTM D412 |
LG Chemical NBR 6280 High Acrylonitrile Polymer Description: NBR 6280 is a copolymer of butadiene and acrylonitrile manufactured by advanced emulsion polymerization technology of Goodyear and LG Chem. NBR 6280 is a non staining, high mooney, and .. |
|||
300% Modulus | 0.0157 GPa | 2.28 ksi | |
Taiwan PU Corporation TPUI-E95 General Grade, Injection Molding Polyester Base TPU Thermoplastic Polyurethane (TPU), General Grade, Polyester Base, Injection MoldingInformation provided by Taiwan PU Corporation. |
|||
300% Modulus | 0.0157 GPa | 2.28 ksi | ASTM D412 |
Lubrizol Estane® ALR CL87A Thermoplastic Polyurethane Type: Estane® ALR CL87A is an aliphatic, polycaprolactone-based TPU with a Shore A Durometer of 85-90.Features: Contains a UV package that enhances outdoor weatherability. This high performance re.. |
|||
300% Modulus | 0.0157 GPa | 2.28 ksi | aged 70 hours at 250ºF in ASTM Oil #903 |
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 20 PHR HAF Black (Typical) MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
300% Modulus | 0.0157 GPa | 2.28 ksi | |
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 70A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
300% Modulus | 0.0157 GPa | 2.28 ksi | |
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 70A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |