Outokumpu SAF 2507® Duplex Stainless Steel

Category Metal , Ferrous Metal , Duplex , Stainless Steel
Manufacturer Outokumpu
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Outokumpu SAF 2507® Duplex Stainless Steel.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Applications: Pulp and paper industryDesalination plantsFlue-gas cleaningCargo tanks and pipe systems in chemical tankersSeawater systemsFirewalls and blast walls on offshore platformsBridgesComponents for structural designStorage tanksPressure vesselsHeat exchangersWater heatersRotors, impellers and shaftsAvailable in hot rolled plate (Quarto) and cold rolled strip/sheet forms.
Physical Properties Metric English Comments
Density 7.80 g/cc
0.282 lb/in³
RT
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 830 MPa
120000 psi
Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
630 MPa

@Temperature 250 °C
 91400 psi

@Temperature 482 °F
 EN min.; EN 10002-5
640 MPa

@Temperature 200 °C
 92800 psi

@Temperature 392 °F
 EN min.; EN 10002-5
660 MPa

@Temperature 150 °C
 95700 psi

@Temperature 302 °F
 EN min.; EN 10002-5
680 MPa

@Temperature 100 °C
 98600 psi

@Temperature 212 °F
 EN min.; EN 10002-5
Tensile Strength, Yield 530 MPa

@Strain 0.200 %
 76900 psi

@Strain 0.200 %
 EN min.,RT; EN 10002-1
590 MPa

@Strain 0.200 %
 85600 psi

@Strain 0.200 %
 Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
380 MPa

@Strain 0.200 %,
Temperature 250 °C
 55100 psi

@Strain 0.200 %,
Temperature 482 °F
 EN min.; EN 10002-5
400 MPa

@Strain 0.200 %,
Temperature 200 °C
 58000 psi

@Strain 0.200 %,
Temperature 392 °F
 EN min.; EN 10002-5
420 MPa

@Strain 0.200 %,
Temperature 150 °C
 60900 psi

@Strain 0.200 %,
Temperature 302 °F
 EN min.; EN 10002-5
450 MPa

@Strain 0.200 %,
Temperature 100 °C
 65300 psi

@Strain 0.200 %,
Temperature 212 °F
 EN min.; EN 10002-5
Elongation at Break 35 %
35 %
Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
Modulus of Elasticity 200 GPa
29000 ksi
RT
172 GPa

@Temperature 400 °C
 24900 ksi

@Temperature 752 °F
180 GPa

@Temperature 300 °C
 26100 ksi

@Temperature 572 °F
186 GPa

@Temperature 200 °C
 27000 ksi

@Temperature 392 °F
194 GPa

@Temperature 100 °C
 28100 ksi

@Temperature 212 °F
Poissons Ratio 0.30
0.30
RT
Fatigue Strength 802 MPa
116000 psi
R=smin/smax=0.1; 2 million cycles, F50
550 MPa

@# of Cycles 2.00e+6
79800 psi

@# of Cycles 2.00e+6
R=smin/smax=0.1;RT; 50% probability of failure
565 MPa

@Strain 0.200 %
 81900 psi

@Strain 0.200 %
 R=smin/smax=0.1; 2 million cycles, F50
Shear Modulus 77.0 GPa
11200 ksi
calculated
Impact Test >= 60.0 J
>= 44.3 ft-lb
EN 10045-1
>= 40.0 J

@Temperature -40.0 °C
 >= 29.5 ft-lb

@Temperature -40.0 °F
 EN 10045-1
Thermal Properties Metric English Comments
CTE, linear 13.0 µm/m-°C

@Temperature 100 °C
 7.22 µin/in-°F

@Temperature 212 °F
13.5 µm/m-°C

@Temperature 200 °C
 7.50 µin/in-°F

@Temperature 392 °F
14.0 µm/m-°C

@Temperature 300 °C
 7.78 µin/in-°F

@Temperature 572 °F
14.5 µm/m-°C

@Temperature 400 °C
 8.06 µin/in-°F

@Temperature 752 °F
Specific Heat Capacity 0.500 J/g-°C
0.120 BTU/lb-°F
RT
0.530 J/g-°C

@Temperature 100 °C
 0.127 BTU/lb-°F

@Temperature 212 °F
0.560 J/g-°C

@Temperature 200 °C
 0.134 BTU/lb-°F

@Temperature 392 °F
0.590 J/g-°C

@Temperature 300 °C
 0.141 BTU/lb-°F

@Temperature 572 °F
Thermal Conductivity 15.0 W/m-K
104 BTU-in/hr-ft²-°F
RT
16.0 W/m-K

@Temperature 100 °C
 111 BTU-in/hr-ft²-°F

@Temperature 212 °F
17.0 W/m-K

@Temperature 200 °C
 118 BTU-in/hr-ft²-°F

@Temperature 392 °F
18.0 W/m-K

@Temperature 300 °C
 125 BTU-in/hr-ft²-°F

@Temperature 572 °F
20.0 W/m-K

@Temperature 400 °C
 139 BTU-in/hr-ft²-°F

@Temperature 752 °F
Component Elements Properties Metric English Comments
Carbon, C 0.020 %
0.020 %
Chromium, Cr 25 %
25 %
Iron, Fe 63.71 %
63.71 %
Molybdenum, Mo 4.0 %
4.0 %
Nickel, Ni 7.0 %
7.0 %
Nitrogen, N 0.27 %
0.27 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000800 ohm-cm
0.0000800 ohm-cm
RT
0.0000850 ohm-cm

@Temperature 100 °C
 0.0000850 ohm-cm

@Temperature 212 °F
0.0000900 ohm-cm

@Temperature 200 °C
 0.0000900 ohm-cm

@Temperature 392 °F
0.000100 ohm-cm

@Temperature 300 °C
 0.000100 ohm-cm

@Temperature 572 °F
Processing Properties Metric English Comments
Annealing Temperature 1040 - 1120 °C
1900 - 2050 °F
Quench Annealing
1040 - 1120 °C
1900 - 2050 °F
Stress Relief Annealing